Lithium-ion battery pole piece slurry, pole piece and preparation method and application thereof

A technology of lithium-ion batteries and electrode active materials, applied in battery electrodes, non-aqueous electrolyte battery electrodes, secondary batteries, etc., can solve the problems of pole piece breakage, graphite shedding, etc., to increase service life, improve shedding, and tightly bonded Effect

Active Publication Date: 2022-05-27
JIANGSU ZENIO NEW ENERGY BATTERY TECH CO LTD
View PDF24 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

By adding a flexibilizer to the pole piece slurry, the present invention well solves the problem that the positive pole piece breaks due to the use of high nickel material and high compaction density process, and improves the processing yield of the positive pole piece And the safety of use; at the same time, it solves the problem of graphite falling off due to the use of high-gram capacity graphite and the use of high-pressure compaction technology, and improves the service life of the negative electrode.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lithium-ion battery pole piece slurry, pole piece and preparation method and application thereof
  • Lithium-ion battery pole piece slurry, pole piece and preparation method and application thereof
  • Lithium-ion battery pole piece slurry, pole piece and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0066] A preparation method of lithium ion battery positive electrode sheet slurry, which comprises:

[0067] The ternary material (NCM) is used as the positive electrode active material, carbon black (SP) is used as the conductive agent, polyvinylidene fluoride (PVDF) is used as the binder, and N-methylpyrrolidone (NMP) is used as the solvent. Agent 1,2-propanediol, NCM:SP:PVDF=98:1:1 according to the solid weight ratio, the slurry solid content is 78%, wherein NMP:1,2-propanediol=98:2 (volume ratio); Stir and mix the above materials uniformly at a temperature of 30° C. to obtain positive electrode slurry.

preparation example 2

[0069] A preparation method of lithium ion battery negative electrode sheet slurry, which comprises:

[0070] Graphite (AG) is used as the negative electrode active material, styrene-butadiene rubber (SBR) is used as the binder, carboxymethyl cellulose (CMC) is used as the dispersant, carbon black (SP) is used as the conductive agent, and distilled water is used as the solvent, 1, 2-propylene glycol is a flexible agent, and the above-mentioned raw materials are stirred and mixed according to the ratio AG:SBR:CMC:SP=96:1.5:1:1.5 to form a negative electrode slurry, and the solid content of the slurry is 50%, wherein distilled water: 1,2 - Propylene glycol weight ratio = 99:1 (volume ratio); then the above materials were stirred and mixed evenly at a temperature of 30° C. to obtain negative electrode slurry.

preparation example 3

[0072] Compared with Preparation Example 1, only the softening agent was replaced with 1,2-butanediol by 1,2-propanediol.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The present invention relates to a lithium-ion battery pole piece slurry, a pole piece and a preparation method and application thereof. The pole piece slurry includes: an electrode active material, a conductive agent, a binder, a solvent and a flexible agent. The softening agent is an alcohol with 2 to 5 carbon atoms, calculated as 100% of the content of the solvent and the softening agent, and the volume percentage of the softening agent is 0.1 to 15%; , the pole piece is made by mixing a flexible agent into the pole piece slurry, or coated with a flexible agent on the surface of the prepared pole piece, so as to obtain a pole piece with low hardness and brittleness; at the same time, the present invention also provides a low hardness and brittle pole piece; A method for breaking the pole piece, which is realized by adding a flexible agent to the pole piece. The positive electrode sheet provided by the present invention greatly reduces the probability of fracture during processing and use, improves the processing yield and safety of use of lithium-ion batteries, overcomes the problem of powder falling off the negative electrode during charging and discharging, and prolongs the life of the lithium-ion battery. ion battery life.

Description

technical field [0001] The invention relates to the technical field of power batteries, in particular to a lithium-ion battery pole piece slurry, a pole piece and a preparation method and application thereof. Background technique [0002] Lithium-ion batteries have the advantages of no pollution, high energy density and power density, high voltage, long cycle life, small self-discharge, and no memory effect. They have been widely used in portable electronic devices such as smartphones, notebooks, and tablet computers. With the development of electric vehicles, lithium batteries have also been widely used as power batteries for vehicles. With the popularity of electric vehicles, consumers urgently need a high-energy-density power lithium-ion battery to meet the demand for increased mileage and extended service life of electric vehicles. [0003] At present, in order to improve the energy density and cycle life of lithium-ion batteries, the technical means commonly used by re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/62H01M4/13H01M4/139H01M10/0525
CPCH01M4/62H01M4/13H01M4/139H01M10/0525Y02E60/10
Inventor 王汭姚毅於洪将邹武元姜斌杨月球
Owner JIANGSU ZENIO NEW ENERGY BATTERY TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com