High-imitation anodic treatment powder paint, preparation method and application thereof

A powder coating and anodizing technology, used in powder coatings, polyester coatings, epoxy resin coatings, etc., can solve the problems of incompatibility with outdoor requirements and low gloss, and achieve excellent surface leveling and leveling. , Enhance the effect of metal effect

Active Publication Date: 2020-01-10
HUNAN LIANXIN SCI & TECH CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The gloss of the product obtained by this method is relatively low, which can only reach about 200 degrees, and it is not suitable for outdoor requirements.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-imitation anodic treatment powder paint, preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A high imitation anodized powder coating of the present invention, its raw material is made up of each component of following mass fraction: the bisphenol A type epoxy resin of 1000g, the polypentyl isophthalate of 1000g, the mica powder of 20g , 2g antioxidant, 2g leveling agent, 2g alignment agent (powder coating imitation electroplating silver powder alignment agent), 2g dispersant, 1g transparent pigment; wherein, the softening point of bisphenol A type epoxy resin is 82~88 ℃, The number average molecular weight is 420, the viscosity at 25°C is 11000-14000mPa.s, the viscosity of polypentyl isophthalate is 25Pa·s, and the average particle size of mica powder is 100μm.

[0031] The preparation method of the high imitation anodized powder coating comprises the following steps:

[0032] (1) Mix and stir 1000g bisphenol A type epoxy resin, 1000g polypentyl isophthalate, 2g antioxidant, 2g leveling agent, 2g alignment agent, and 2g dispersant in proportion, and pass throu...

Embodiment 2

[0035] A high imitation anodized powder coating of the present invention, its raw material is made up of each component of following mass fraction: the bisphenol A type epoxy resin of 1000g, the polypentylene isophthalate of 1000g, the mica powder of 25g , 2g antioxidant, 2g leveling agent, 2g alignment agent (powder coating imitation electroplating silver powder alignment agent), 2g dispersant, 2g transparent pigment; wherein, the softening point of bisphenol A type epoxy resin is 82~88 ℃, The number average molecular weight is 420, the viscosity at 25°C is 11000-14000mPa.s, the viscosity of polypentyl isophthalate is 25Pa·s, and the average particle size of mica powder is 100μm.

[0036] The preparation method of the high imitation anodized powder coating comprises the following steps:

[0037] (1) Mix and stir 1000g bisphenol A type epoxy resin, 1000g polypentyl isophthalate, 2g antioxidant, 2g leveling agent, 2g alignment agent, and 2g dispersant in proportion, and pass th...

Embodiment 3

[0040] A high imitation anodized powder coating of the present invention, its raw material is made up of each component of following mass fraction: the bisphenol A type epoxy resin of 1000g, the polypentyl isophthalate of 1000g, the mica powder of 20g , 2g antioxidant, 2g leveling agent, 2g alignment agent (powder coating imitation electroplating silver powder alignment agent), 2g dispersant, 1g transparent pigment; wherein, the softening point of bisphenol A type epoxy resin is 82~88 ℃, The number average molecular weight is 420, the viscosity at 25°C is 11000-14000mPa.s, the viscosity of polypentyl isophthalate is 25Pa·s, and the average particle size of mica powder is 100μm.

[0041] The preparation method of the high imitation anodized powder coating comprises the following steps:

[0042] (1) Mix and stir 1000g bisphenol A type epoxy resin, 1000g polypentyl isophthalate, 2g antioxidant, 2g leveling agent, 2g alignment agent, and 2g dispersant in proportion, and pass throu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-imitation anodic treatment powder paint, which comprises the following raw materials by weight: 900-1000 parts of epoxy resin, 900-1000 parts of polyester resin, 20-25 parts of mica powder and 1-3 parts of an arrangement agent. The high-imitation anodic treatment powder paint disclosed by the invention can greatly improve the surface leveling properties and glossiness of a film formed by the powder paint, the leveling properties of the obtained paint film can reach level 10, and the glossiness can reach 600 degrees or above, the surface of the paint film has metal luster, and after the paint is coated on a device surface, a good anode-imitation effect can be achieved, so that the high-imitation anodic treatment powder paint provided by the invention can replace traditional high-pollution anode electroplating and be used for preparation of device surface coatings. The invention also discloses a preparation method and application of the high-imitation anodic treatment powder paint, the method adopts special multi-stage control speed stirring processing, has the characteristics of precise temperature control, convenient operation, low cost, and environment-friendly and pollution-free preparation process.

Description

technical field [0001] The invention belongs to the field of coatings, in particular to a high imitation anodized powder coating and its preparation method and application. Background technique [0002] Most of the high imitation anodized powder coatings currently use epoxy resin and polyester formulations, which are directly formed after stirring. The gloss of the product obtained by this method is relatively low, which can only reach about 200 degrees, and it is not suitable for outdoor requirements. Therefore, there is an urgent need for a powder coating with high surface gloss and adaptability to outdoor conditions, and to develop an outdoor high imitation anodized powder coating preparation process with easy control of the preparation process and high gloss without pollution. Contents of the invention [0003] The technical problem to be solved by the present invention is to overcome the deficiencies and defects mentioned in the above background technology, provide a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D167/02C09D7/61C09D5/03
CPCC08K2003/0806C09D5/033C09D163/00C09D167/02C08L67/02C08K3/34C08K3/08C08L63/00
Inventor 夏连心方志旺
Owner HUNAN LIANXIN SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com