Preparation method and application of modified brominated butyl rubber porous material

A technology of bromobutyl rubber and porous materials, applied in chemical instruments and methods, other chemical processes, water/sludge/sewage treatment, etc., can solve the problem of difficult to control the shape and size of pore structure, lack of crack resistance and Self-healing ability and other issues, to achieve the effect of simple, controllable and environmentally friendly operation process, excellent anti-crack performance, and enhanced adsorption capacity

Active Publication Date: 2020-02-11
CHANGZHOU UNIV
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing polar resins do not have crack resistance and self-healing ability
[0005] In the prior art, the rubber porous material is usually prepared by adding a rubber foaming agent, which is difficult to control the shape and size of the pore structure.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of modified brominated butyl rubber porous material
  • Preparation method and application of modified brominated butyl rubber porous material
  • Preparation method and application of modified brominated butyl rubber porous material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Weigh 25 g of bromobutyl rubber and 1 g of butyl imidazole respectively. At a high temperature of 150°C, the mixture of components was cured in an internal mixer to obtain butyl imidazole-modified brominated butyl rubber INR. Weigh 1.6g of modified bromobutyl rubber INR and 30g of petroleum ether, and mix them for later use. After the mixture has stood at room temperature for more than 4 days, heat it in a water bath for 1 hour, and dissolve the INR with petroleum ether at 65°C to form a uniform mixture. solution to obtain a solution-like modified bromobutyl rubber INR. Weigh 0.16g of CB and 24g of deionized water, and stir with a high-speed mixer to form a uniform suspension. At a temperature of 65°C, slowly pour the CB suspension into the INR solution while stirring, and keep stirring for 20 min to obtain a CB@INR mixture. After removing the excess moisture layered out of the mixture material obtained in the previous step, pour it into a petri dish, place it in an o...

Embodiment 2

[0034] Weigh 26 g of bromobutyl rubber and 1 g of butyl imidazole respectively. At a high temperature of 150°C, the mixture of components was cured in an internal mixer to obtain butyl imidazole-modified brominated butyl rubber INR. Weigh 1.5g of modified bromobutyl rubber INR and 30g of petroleum ether, and mix them for later use. After the mixture is allowed to stand at room temperature for more than 4 days, heat it in a water bath for 1.5 hours, and dissolve the INR with petroleum ether at 65°C to form a uniform mixture. solution to obtain a solution-like modified bromobutyl rubber INR. Weigh 0.175g of CB and 28g of deionized water, and stir with a high-speed mixer to form a uniform suspension. At a temperature of 65°C, slowly pour the CB suspension into the INR solution while stirring, and keep stirring for 23 minutes to obtain a CB@INR mixture. After removing the excess moisture layered out of the mixture material obtained in the previous step, pour it into a petri dish...

Embodiment 3

[0036]Weigh 28 g of bromobutyl rubber and 1 g of butyl imidazole respectively. At a high temperature of 150°C, the mixture of components was cured in an internal mixer to obtain butyl imidazole-modified brominated butyl rubber INR. Weigh 1.4g of modified bromobutyl rubber INR and 30g of petroleum ether, and mix them for later use. After the mixture has stood at room temperature for more than 4 days, heat it in a water bath for 1 hour, and dissolve the INR with petroleum ether at 65°C to form a uniform mixture. solution to obtain a solution-like modified bromobutyl rubber INR. Weigh 0.135g of CB and 23g of deionized water, and stir with a high-speed mixer to form a uniform suspension. At a temperature of 65°C, slowly pour the CB suspension into the INR solution while stirring, and keep stirring for 25 minutes to obtain a CB@INR mixture. After removing the excess moisture layered out of the mixture material obtained in the previous step, pour it into a petri dish, place it in ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical fields of adsorption material preparation and adsorption separation, and particularly relates to a preparation method and application of a modified brominated butyl rubber porous material. According to the preparation method, carbon black CB is used as a stable particle, deionized water is used as a water phase, and modified brominated butyl rubber and petroleum ether are mixed, heated and dissolved to obtain an oil phase; after the water phase and the oil phase are mixed, a relatively stable Pickering emulsion is formed; and rubber is used as a substratematerial, and the modified brominated butyl rubber porous material is prepared by means of the unique self-crosslinking polymerization capacity of the rubber, and the modified brominated butyl rubberporous material is applied to adsorption separation of tetrodotoxin TTX in an aqueous solution. The product has a porous internal structure and good stability and is beneficial for adsorption separation of target molecules; a large number of adsorption sites are provided for doped and dispersed CB in rubber; and a porous material prepared from the modified brominated butyl rubber has good self-adhesion healing capacity.

Description

technical field [0001] The invention belongs to the technical field of material preparation and adsorption separation, and relates to a preparation method and application of a modified brominated butyl rubber porous material, in particular to a Pickering emulsion template method for preparing a modified material doped with nano-scale carbon black particles A method of bromobutyl rubber porous material applied to the adsorption and isolation of tetrodotoxin from environmental water samples. Background technique [0002] Tetrodotoxin (TTX) belongs to amino perhydroquinazoline compounds, is a clathrate orthoester alkaloid, molecular formula is C 11 h 17 N 3 o 8 . As a typical non-protein neurotoxin, TTX is more than 1250 times more toxic than cyanide. It binds to receptors on sodium ion channels, causing nerve and muscle paralysis, limb weakness, paralysis, etc. Patients with severe poisoning will suffer from Central nervous paralysis, respiratory arrest and death, no spec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08J9/00C08L23/36C08K3/04C08F8/30C08F210/12B01J20/26B01J20/30C02F1/28C02F101/38
CPCC08J9/00C08J9/0066C08F8/30B01J20/265C02F1/285C08J2323/36C02F2101/38C08F210/12
Inventor 欧红香贡晨霞郑旭东黄如君李凯佳周东升
Owner CHANGZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap