Cement-based capillary crystalline waterproof coating and preparation method thereof

A technology of infiltration crystallization and waterproof coating, applied in the field of building waterproof materials, can solve the problems of impermeability and waterproof performance, bonding performance and poor flexural and compressive strength, so as to improve the impermeability and waterproof effect, improve the impermeability and improve the The effect of water resistance

Inactive Publication Date: 2020-03-27
MAANSHAN MCC17 ENG TECH CO LTD
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to overcome the deficiencies of the existing osmotic crystalline waterproofing materials, which are relatively poor in impermeabili

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cement-based capillary crystalline waterproof coating and preparation method thereof
  • Cement-based capillary crystalline waterproof coating and preparation method thereof
  • Cement-based capillary crystalline waterproof coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0030] The preparation method of the above-mentioned osmotic crystalline waterproof coating mainly includes: using a planetary mortar mixer, wiping the mixing blade and the mixing bucket with a clean damp cloth before mixing, first mixing the modified siloxane, calcium ion balancer, Add water reducer and water into the mixing tank, then add ordinary portland cement, silica fume, water glass, redispersible latex powder, granulated blast furnace slag, make the mixer rotate at a speed of 57~67r / min, and stir for 20 ~40s; add quartz sand evenly into the mixing tank and continue stirring for 20-40s; stop stirring for 90s, adjust the speed of the mixer to 115-135r / min, scrape the slurry to the middle of the mixing tank, and continue stirring for 50 ~70s, the waterproof coating is obtained.

[0031] The existing cement-based osmotic crystalline waterproof material mainly uses the osmotic crystallization effect of active chemical substances in its composition to achieve the purpose of...

Embodiment 1

[0038] The percentage by weight of each component of the infiltration crystalline waterproof material obtained in the present embodiment is as follows: 56% of ordinary Portland cement, 2% of modified siloxane, 6.2% of quartz sand, 2.2% of silica fume, 3% of water glass, The modulus is 0.5, the redispersible latex powder is 10%, the calcium ion balancer is 0.2%, the water reducer is 0.4%, and the granulated blast furnace slag is 20%. Among them, calcium hydroxide is used as calcium ion balancer, and powdered sulfamate water reducer is used as water reducer; when the fineness modulus of quartz sand is controlled to be 2-2.3 and 2.3-3.0, the mass percentages are respectively 20%, 80%; the mass percentage of blast furnace slag is 10% and 90% when the mesh number of blast furnace slag is controlled to be 200-300 mesh, and 300 mesh and above.

[0039] Use a planetary plastic sand mixer, wipe the mixing blade and the mixing bucket with a clean damp cloth before mixing, first add the ...

Embodiment 2

[0042] The percentage by weight of each component of the permeable crystalline waterproof material obtained in the present embodiment is as follows: 45% of ordinary Portland cement, 3% of modified siloxane, 10% of quartz sand, 1.8% of silica fume, 1% of water glass, The modulus is 0.5, the redispersible latex powder is 8.1%, the calcium ion balancer is 0.4%, the water reducer is 0.7%, and the granulated blast furnace slag is 30%. Among them, calcium hydroxide is used as calcium ion balancer, and powdered sulfamate water reducer is used as water reducer; when the fineness modulus of quartz sand is controlled to be 2-2.3 and 2.3-3.0, the mass percentages are 40%, 60%; the mass percentages of blast furnace slag are 30% and 70% when the mesh number of blast furnace slag is controlled to be 200-300 mesh, and 300 mesh and above.

[0043] Use a planetary plastic sand mixer, wipe the mixing blade and the mixing bucket with a clean damp cloth before mixing, first add the modified silox...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Bond strengthaaaaaaaaaa
Bond strengthaaaaaaaaaa
Bond strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a cement-based capillary crystalline waterproof coating and a preparation method thereof, and belongs to the technical field of building waterproof materials. The cement-basedcapillary crystalline waterproof coating is composed of, by weight, 35%-60% of ordinary Portland cement; 1%-3% of a modified siloxane, 5%-20% of quartz sand, 1.4%-2.4% of silica fume, 1%-5% of water glass, 6.3%-10.8% of redispersible latex powder, 0.2%-1.2% of a calcium ion balancing agent, 0.4%-1.6% of a water reducing agent and 20%-30% of granulated blast furnace slag. By adopting the technicalscheme, the anti-permeability and waterproof performance, the bonding performance and the flexural and compressive strength of the obtained cement-based capillary crystalline waterproof coating can beeffectively improved, the anti-permeability and waterproof effects can be further improved when the cement-based capillary crystalline waterproof coating is applied to the surface of concrete, and therefore the service life of the concrete can be prolonged.

Description

technical field [0001] The invention belongs to the technical field of building waterproof materials, and more specifically relates to a cement-based permeable crystalline waterproof coating and a preparation method thereof. Background technique [0002] In recent years, with the rapid development of the construction industry and the increasing number of underground projects, people have put forward higher requirements for the waterproofing of buildings and the moisture-proof and anti-corrosion materials of underground projects. Building waterproof material is an important part of construction engineering, and its performance directly affects the use function and service life of the building. [0003] Waterproof coatings on the existing market can generally be divided into two categories: rigid waterproof materials and flexible waterproof materials. Among them, the working principle of the flexible waterproof material is: by brushing a certain thickness of waterproof materi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/04C04B111/27C04B24/42C04B24/26C04B18/14C04B14/06
CPCC04B28/04C04B2111/00508C04B2111/27C04B24/42C04B14/068C04B18/146C04B12/04C04B24/2623C04B18/141C04B22/064C04B24/226Y02W30/91
Inventor 黄维军杨德富雷团结王孝平钱元弟郭生全孙敏李亚辉杨德健
Owner MAANSHAN MCC17 ENG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap