Mulberry silk wool fiber blend wetting emulsion

Abstract

The invention discloses a mulberry silk wool fiber blend wetting emulsion which comprises a wool fiber wetting pretreatment emulsion and a mulberry silk fiber wetting pretreatment emulsion. The wool fiber wetting pretreatment emulsion is prepared from the following raw materials in parts by weight: 0.3 to 0.5 part of wool lubricant, 1.0 to 1.6 parts of softening agent I, 0.8 to 1.2 parts of antistatic agent I, 0.5 to 0.8 part of penetrating agent I, 0.3 to 0.6 part of emulsifier, and 15 to 20 parts of water. According to the mulberry silk wool fiber blend wetting emulsion provided by the invention, after two blended fibers are emulsified through the two emulsions, the mulberry silk wool fiber blend wetting emulsion can fully permeate into the fibers so as to achieve the effects on resisting static, softening and increasing a cohesive force. The spinnability is improved, and meanwhile, not only can the process requirement on spinning be met, but also the phenomena of lapping and the like of a card cylinder and a drawing frame can be relieved.

Description

technical field [0001] The invention relates to the technical field of textiles, in particular to a wet emulsion for mulberry silk and wool fiber blending. Background technique [0002] Wool fiber has the characteristics of good elasticity and phosphorus flakes. In order to reduce the friction of wool during spinning, increase the softness and cohesion of wool fiber, and improve the spinnability of wool fiber, in the wool spinning system, It is necessary to pretreat the wool fiber first, and add a certain amount of spinning aids such as wool and wool oil. The fineness of mulberry silk fiber is fine and the specific resistance is large. It is easy to have serious static electricity in the spinning process. Therefore, some antistatic agents are added in the general silk spinning production process. However, the fineness of mulberry silk fiber is very fine. , and the fibers are soft, the carding process in the spinning process can easily cause the carding machine to wind aroun...

AI Technical Summary

Problems solved by technology

The fineness of mulberry silk fiber is fine and the specific resistance is large. It is easy to have serious static electricity in the spinning process. Therefore, some antistatic agents are added in the general silk spinning production process. However, the fineness of mulberry silk fiber is very fine. , the fiber is relatively soft, and the carding process in the spinning process is very easy to cause the carding machine to wrap around the cylinder, which affects the normal production

[0003] When traditional mulberry silk and wool fiber are blended, conventional and wool oil, softener and electrostatic agent are used to pre-treat the two fibers, which is very easy to cause the carding machine to wind around the cylinder during production, and the drawing process will also Wrapped wool, life is not easy to do, affecting yarn quality; and the softener is generally only slightly soluble in water, has poor permeability, does not have bactericidal properties, and is not stable for long-term storage; and in the process of processing blended fibers, It cannot be used for dust removal and impurity removal, and the excess emulsion can not be recycled, and it cannot be applied to fabrics of different widths

Images