Composite photocatalyst for producing hydrogen peroxide and its preparation method and application

A technology of hydrogen peroxide and catalyst, applied in the field of photocatalysis, to achieve excellent visible light and near-infrared light conversion ability, improve separation efficiency, and expand the effect of intrinsic light absorption range

Active Publication Date: 2022-04-08
HUNAN UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, so far, the application of bismuth oxybromide composite photocatalysts with oxygen vacancies modified by nitrogen-doped carbon quantum dots for the production of hydrogen peroxide has not been reported.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite photocatalyst for producing hydrogen peroxide and its preparation method and application
  • Composite photocatalyst for producing hydrogen peroxide and its preparation method and application
  • Composite photocatalyst for producing hydrogen peroxide and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0073] A bismuth oxybromide composite photocatalyst with oxygen vacancies modified by nitrogen-doped carbon quantum dots, the bismuth oxybromide composite photocatalyst with oxygen vacancies modified by nitrogen-doped carbon quantum dots is supported by bismuth oxybromide with oxygen vacancies , Bismuth oxybromide is decorated with nitrogen-doped carbon quantum dots.

[0074] In this embodiment, the volume of the nitrogen-doped carbon quantum dot dispersion in the nitrogen-doped carbon quantum dot-modified bismuth oxybromide composite photocatalyst with oxygen vacancies is 6 mL.

[0075] In this embodiment, the nitrogen-doped carbon quantum dot-modified bismuth oxybromide composite photocatalyst with oxygen vacancies is a sheet material with a diameter of 3 μm-6 μm and a thickness of 100 nm-300 nm.

[0076] In this embodiment, the nitrogen-doped carbon quantum dots are spherical materials with a diameter of 2 nm to 10 nm.

[0077] The preparation method of the bismuth oxybrom...

Embodiment 2

[0119] Application of a nitrogen-doped carbon quantum dot modified bismuth oxybromide composite photocatalyst with oxygen vacancies in the production of hydrogen peroxide, comprising the following steps:

[0120] Weigh respectively BiOBr (comparative example 1), NB-6 (comparative example 2), OV-BiOBr (comparative example 3), NOB-6 (embodiment 1) of 0.05g, and add them to 100mL, volume concentration respectively In a 10% aqueous solution of isopropanol, stir magnetically for one hour in a dark place (that is, under dark conditions), turn on the light source after reaching adsorption equilibrium, and carry out a photocatalytic reaction under visible light (λ≥420nm) for 60 minutes to complete the production of hydrogen peroxide .

[0121] In this embodiment, 100 mL of isopropanol solution with a volume concentration of 10% without adding any material is used as a blank for comparison.

[0122] Determination of hydrogen peroxide production: absorb the photocatalytic reaction solu...

Embodiment 3

[0130] To investigate the reusability of nitrogen-doped carbon quantum dots modified bismuth oxybromide composite photocatalyst with oxygen vacancies in the process of photocatalytic production of hydrogen peroxide, including the following steps:

[0131] (1) Weigh 0.05g of the bismuth oxybromide composite photocatalyst (NOB-6) with oxygen vacancies modified by nitrogen-doped carbon quantum dots prepared in Example 1, add to 100mL, volume concentration of 10% isopropanol In aqueous solution, the reaction system was obtained.

[0132] (2) Place the reaction system (isopropanol solution with NOB-6 added) obtained in step (1) on a magnetic stirrer, and stir for 1 h in the dark to achieve adsorption equilibrium, and take 3 mL of the solution to represent the The initial solution, that is, the solution when the reaction time is 0min, after filtration and color development, measure its concentration with a UV-visible spectrophotometer and convert it into output.

[0133] (3) The re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention "a composite photocatalyst for producing hydrogen peroxide and its preparation method and application" belongs to the technical field of photocatalysis. The composite photocatalyst is a bismuth oxybromide composite photocatalyst with oxygen vacancies modified by nitrogen-doped carbon quantum dots. The composite photocatalyst of the present invention has the advantages of environmental protection, high photogenerated electron-hole separation efficiency, wide light absorption range, good stability of photocatalytic performance, good reusability, etc., and its preparation method has the advantages of simple preparation process, easy control of operating conditions, The raw materials are simple and easy to obtain, and the preparation cost is relatively low. The composite photocatalyst of the invention can be used to produce hydrogen peroxide, has the advantages of simple application method, high output and good reusability, and has good practical application prospect.

Description

technical field [0001] The invention belongs to the technical field of photocatalysis, and relates to a composite photocatalyst for producing hydrogen peroxide, a preparation method and application thereof. Background technique [0002] With the development of modern industry, the problems of energy crisis and environmental pollution are becoming more and more serious. Among them, energy shortage and environmental degradation are major problems that human beings face and need to be solved urgently in the 21st century. Therefore, new energy utilization and environmental pollution control are of great significance to the national sustainable development strategy. Due to its low cost, no pollution and high efficiency, photocatalytic technology has broad application prospects in energy storage, conversion and environmental protection. [0003] Bismuth oxybromide (BiOBr) is a photocatalytic material with visible light response, which has been widely used in photocatalysis due to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J27/24B01J35/02C01B15/026
CPCB01J35/004B01J27/24B01J35/023C01B15/026
Inventor 袁兴中于瀚博蒋龙波张进熊婷陈浩云
Owner HUNAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap