Ivory white ceramic glaze with self-cleaning function and preparation method of ivory white ceramic glaze

A ceramic glaze and functional technology, applied in the field of ivory white ceramic glaze and its preparation, can solve the problems of insignificant self-cleaning function effect, single gloss, stained with stains, etc. strong effect

Inactive Publication Date: 2020-05-29
林丽品
View PDF8 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The gloss is relatively single, so it is impossible to obtain a glossy glaze with a beautiful and smooth surface.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ivory white ceramic glaze with self-cleaning function and preparation method of ivory white ceramic glaze

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] An ivory white ceramic glaze with self-cleaning function, comprising the following raw materials in parts by mass: 25 parts of silicon dioxide, 20 parts of feldspar, 20 parts of kaolin, 10 parts of boric acid powder, 10 parts of calcite, 15 parts of wood knot clay, 15 parts of glaze fruit, 10 parts of talcum powder, 15 parts of aluminum oxide, 2 parts of zinc oxide, 2 parts of tin crystal material, 2 parts of magnesium carbonate, 1 part of calcium carbonate, 0.8 parts of diboron trioxide, 2 parts of lime glaze and compound antibacterial Powder, the composite antibacterial powder is a mixture of 20 parts of titanium dioxide, 20 parts of silver molybdate and 60 parts of ammonium dihydrogen phosphate.

Embodiment 2

[0032] An ivory white ceramic glaze with self-cleaning function, comprising the following raw materials in parts by mass: 30 parts of silicon dioxide, 25 parts of feldspar, 22 parts of kaolin, 12 parts of boric acid powder, 12 parts of calcite, 17 parts of wood knot clay, 17 parts of glaze fruit, 15 parts of talcum powder, 17 parts of aluminum oxide, 4 parts of zinc oxide, 3 parts of tin crystal material, 3 parts of magnesium carbonate, 2 parts of calcium carbonate, 1.2 parts of diboron trioxide, 3 parts of lime glaze and compound antibacterial Powder, the composite antibacterial powder is a mixture of 25 parts of titanium dioxide, 25 parts of silver molybdate and 50 parts of ammonium dihydrogen phosphate.

Embodiment 3

[0034] An ivory white ceramic glaze with self-cleaning function, comprising the following raw materials in parts by mass: 32 parts of silicon dioxide, 28 parts of feldspar, 23 parts of kaolin, 14 parts of boric acid powder, 14 parts of calcite, 19 parts of wood knot clay, 19 parts of glaze fruit, 18 parts of talcum powder, 19 parts of aluminum oxide, 6 parts of zinc oxide, 4 parts of tin crystal material, 4 parts of magnesium carbonate, 3 parts of calcium carbonate, 1.6 parts of diboron trioxide, 4 parts of lime glaze and compound antibacterial Powder, the composite antibacterial powder is a mixture of 28 parts of titanium dioxide, 28 parts of silver molybdate and 44 parts of ammonium dihydrogen phosphate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Login to view more

Abstract

The invention discloses an ivory white ceramic glaze with a self-cleaning function and a preparation method of the ivory white ceramic glaze. The ivory white ceramic glaze comprises 25-35 parts of silicon dioxide, 20 to 30 parts of melilite; 20-25 parts of kaolin, 10-16 parts of boric acid powder, 10-15 parts of calcite, 15-20 parts of kapok clay, 15-20 parts of glaze stone, 10-20 parts of talcumpowder, 15-20 parts of aluminum oxide, 2-8 parts of zinc oxide, 2-5 parts of tin crystal materials, 2-6 parts of magnesium carbonate, 1-4 parts of calcium carbonate, 0.8-1.8 parts of diboron trioxide,2-5 parts of lime glaze and a composite antibacterial powder. The ivory white ceramic glaze has the beneficial effects that repeated washing by using a cleaning agent and water is greatly reduced, the ivory white ceramic glaze has a strong self-cleaning function, and the ivory white ceramic glaze with quick and lasting antibacterial performance and a good self-cleaning function can be obtained.

Description

technical field [0001] The invention relates to the technical field of ceramic glaze production technology, in particular to an ivory white ceramic glaze with self-cleaning function and a preparation method thereof. Background technique [0002] Glaze is a kind of silicate. The glaze applied on ceramics is generally made of quartz, feldspar, and clay, which are ground and added with water. After preparation, it is applied on the surface of the green body and melted by roasting at a certain temperature. When the temperature drops, the glass quality of the ceramic surface is formed. TLC. Currently ceramic. The same glaze color of the product can be roughly divided into glossy glaze and matte glaze in terms of luster, so the presented. The gloss is relatively single, so it is impossible to obtain a glossy glaze with a beautiful and smooth surface. At the same time, it is easy to cause stains on the ceramic surface, and the self-cleaning effect is not obvious. [0003] Aimin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/02C03C8/20
CPCC03C8/02C03C8/20C03C2204/02
Inventor 林丽品
Owner 林丽品
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap