A silicon nitride-based, ceramic preparation technology, applied in the field of structural ceramic materials, can solve the problems of graphene damage, reinforcement and toughness, graphene agglomeration, etc., and achieve the effect of improving fracture toughness and good mechanical properties

Inactive Publication Date: 2020-06-05
SHAANXI UNIV OF SCI & TECH
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, graphene is very prone to agglomeration, which affects the overall performance of ceramics. During high-temperature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of graphene-reinforced silicon nitride-based ceramic
  • Preparation method of graphene-reinforced silicon nitride-based ceramic
  • Preparation method of graphene-reinforced silicon nitride-based ceramic

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0032] Example 1

[0033] A method for preparing graphene-reinforced silicon nitride-based ceramics includes the following steps:

[0034] Step S1, weighing silicon nitride, graphene, magnesium oxide and yttrium oxide, the mass percentages of which are: graphene: 10wt%, yttrium oxide and alumina 10wt%, silicon nitride: 80wt%, as the main raw materials; Weigh 100% of the graphene mass of PVP (polyvinylpyrrolidone), measure and add graphene, the graphene concentration can reach 1mg / ml NMP (N-methylpyrrolidone), as a dispersant and dispersion medium; yttrium oxide and Alumina is a sintering aid.

[0035] Step S2, pour the graphene and PVP weighed in step S1 into NMP to form a graphene dispersion, which is placed in a 60°C water bath environment for supergenerating dispersion and mechanically stirred for 120 minutes;

[0036] Step S3, pour the aluminum oxide, yttrium oxide and silicon nitride weighed in step S1 into the dispersion in step S2 to obtain a composite raw material dispersion,...

Example Embodiment

[0044] Example 2

[0045] A method for preparing graphene-reinforced silicon nitride-based ceramics includes the following steps:

[0046] Step S1, weighing silicon nitride, graphene, magnesium oxide and yttrium oxide, the mass percentages of which are: graphene: 0.5wt%, yttrium oxide and alumina 10wt%, silicon nitride: 89.5wt%, as the main raw materials ; Separately weigh PVP (polyvinylpyrrolidone) with 100% graphene mass, measure and add graphene to NMP (N-methylpyrrolidone) whose graphene concentration can reach 1.5mg / ml, as dispersant and dispersion medium;

[0047] Step S2: Pour the graphene and PVP weighed in step S1 into NMP to form a graphene dispersion, which is placed in a 70°C water bath environment for supergenerating dispersion and mechanically stirred for 120 minutes;

[0048] Step S3, pour the aluminum oxide, yttrium oxide and silicon nitride weighed in step S1 into the dispersion in step S2 to obtain a composite raw material dispersion, which is placed in a 60°C water ...

Example Embodiment

[0055] Example 3

[0056] A method for preparing graphene-reinforced silicon nitride-based ceramics includes the following steps:

[0057] Step S1, weighing silicon nitride, graphene, magnesium oxide and yttrium oxide, the mass percentages of which are: graphene: 1wt%, yttrium oxide and alumina 10wt%, silicon nitride: 89wt%, as the main raw materials; Weigh 75% of the graphene mass of PVP (polyvinylpyrrolidone), measure and add graphene to NMP (N-methylpyrrolidone) whose graphene concentration can reach 2mg / ml, as a dispersant and dispersion medium;

[0058] Step S2, pour the graphene and PVP weighed in step S1 into NMP to form a graphene dispersion, which is placed in a water bath environment at 80°C for supergenerating dispersion and mechanically stirred for 60 minutes;

[0059] Step S3, pour the aluminum oxide, yttrium oxide and silicon nitride weighed in step S1 into the dispersion in step S2 to obtain a composite raw material dispersion, which is placed in a 60°C water bath envir...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a graphene-reinforced silicon nitride-based ceramic. The preparation method adopts silicon nitride and graphene as raw materials and a mixture of aluminum oxide and yttrium oxide as a composite sintering aid. The preparation method sequentially comprises the steps of independent dispersion of raw materials, composite dispersion, ball milling, dryingand sieving, three-dimensional mixing and hot press sintering. The mechanical property of the silicon nitride ceramic material is enhanced, and the added graphene improves the friction property of theceramic, so that the silicon nitride can be used as a good wear-resistant and friction-resistant material by improving the mechanical properties.

Description

Technical field [0001] The invention belongs to the technical field of structural ceramic materials, and specifically relates to a method for preparing graphene-reinforced silicon nitride-based ceramics. Background technique [0002] With the development of science and technology, the traction of functional requirements makes people have higher and higher requirements for material properties, such as bearing balls and tools on machine tools. People hope to make them have both good mechanical and tribological properties at the same time. With these two properties, it is more difficult to achieve. Silicon nitride ceramics have high hardness, high melting point, corrosion resistance and self-lubricating ability, but its brittleness makes simple silicon nitride materials easy to fracture, which affects the application of silicon nitride ceramics. In order to enhance its fracture toughness, graphene can be added to the silicon nitride ceramic, so that when the silicon nitride ceramic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/584C04B35/622C04B35/64C04B35/645C04B35/626C01B32/194
CPCC04B35/584C04B35/622C04B35/64C04B35/645C04B35/6261C01B32/194C04B2235/3217C04B2235/3225C04B2235/422
Inventor 陈威赵自强
Owner SHAANXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap