Bulletproof composite armor and manufacturing method thereof

An armor and bulletproof technology, which is applied in the direction of protective equipment, armor, protective equipment, etc., can solve the problems that cannot meet the surface density limit of lightweight protective decks, and the bulletproof plates are too heavy, so as to improve the ability to resist multiple bullets and reduce Effect of small weight and crack spread

Active Publication Date: 2020-06-12
SUZHOU FIRST ELEMENT NANO TECH
View PDF8 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The composite bulletproof armor uses a CrMo alloy frame, and the bulletproof plate is too heavy to meet the surface density limit of a lightweight protective deck

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bulletproof composite armor and manufacturing method thereof
  • Bulletproof composite armor and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] This embodiment relates to a preparation method of bulletproof composite armor, comprising:

[0026] Step 1, you need 44g of B according to a single ceramic piece 4 C powder (Saifu Nano Technology) and 4.4g nano-carbon fiber (Suzhou First Element CNTcr), after mixing the two raw materials evenly, put them into a regular hexagonal mold with a height of 50mm and a thickness of 10.6mm, and undergo continuous automatic plasma Discharge sintering, the equipment used is Dr. FRITSCH DSP500 from Germany, the heating rate is 200°C / min, 50Mpa, 1800°C for 10 minutes, and a sufficient number of regular hexagonal boron carbide ceramic sheets are produced. The obtained regular hexagonal boron carbide ceramic sheets are high 50mm, thickness 8mm;

[0027] Step 2, the above-mentioned boron carbide ceramic sheet and copper foil with a thickness of 15 μm and a purity of >99% are combined according to figure 1 spliced ​​into the base metal, and then placed in a hot-pressing mold with the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
heightaaaaaaaaaa
Vickers hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a bulletproof composite armor and a manufacturing method thereof, and belongs to the technical field of ceramic and metal based composite material preparation. The manufacturing method for the bulletproof composite armor comprises the following steps: step 1 of uniformly mixing B4C powder with nano carbon fibers to obtain a mixture, putting the mixture into a regularly hexagonal mould, and quickly sintering the mixture into regularly hexagonal ceramic sheets through plasma discharge sintering; step 2 of splicing the regularly hexagonal ceramic sheets into a ceramic basematerial, filling splicing seams with micro-level copper foils, and performing vacuum hot-pressing sintering to obtain a ceramic deck; and step 3 of performing hot-isostatic pressing compounding on the ceramic deck and a bulletproof back board to obtain the bulletproof composite armor. The high-toughness composite ceramic bonded by the copper based metal material is compounded with the bulletproof back board to manufacture the bulletproof composite armor, so that multi-time impact resistance ability of armor-piercing bullets and armor-piercing incendiary ammunitions of the composite armor isgreatly improved.

Description

technical field [0001] The invention relates to a technique in the field of organic chemistry, in particular to a bulletproof composite armor and a preparation method thereof. Background technique [0002] The excellent properties of boron carbide make it more and more used in various industries. For example, a Chinese invention patent application with application number CN200910180582.5 discloses a composite ceramic, which increases the hardness of boron carbide ceramics by compounding boron carbide with carbon fibers; although the hardness of boron carbide ceramics is improved by compounding with other materials , but it is still difficult to achieve the bulletproof effect. [0003] The Chinese invention patent application with application number 200510086629.3 discloses a preparation method of steel honeycomb ceramic sandwich composite bulletproof armor. The method uses bulletproof steel plates to prepare honeycomb, fills ceramic chips, and glues and brazes to form compo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): F41H5/04B28B1/52B32B9/00B32B9/04B32B27/32B32B7/12B32B7/08B32B7/022B32B33/00B32B37/12B32B37/10B32B37/06C04B35/563C04B35/80C04B35/622
CPCF41H5/0414F41H5/0421B28B1/52B32B9/005B32B9/045B32B27/32B32B7/12B32B7/08B32B7/022B32B33/00B32B37/1284B32B37/10B32B37/06C04B35/563C04B35/622B32B2307/50B32B2307/536B32B2571/02C04B2235/5248C04B2235/666C04B2235/6562C04B2235/6567
Inventor 陈玉华董明
Owner SUZHOU FIRST ELEMENT NANO TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com