Interface agent and preparation method thereof and application of interface agent in fabricated building structure

A technology of interface agent and coagulation agent, applied in the direction of sustainable waste treatment, solid waste management, climate sustainability, etc., can solve the problems of long hardening time and high bonding strength of interface agent, achieve long hardening time and improve the interface Excellent bonding performance and low temperature resistance

Active Publication Date: 2020-06-16
JIANGSU SOBUTE NEW MATERIALS
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] In order to solve the performance requirements of interface agents such as high bond strength, long hardening time, and low temperature resistance in the construction of new and old

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Interface agent and preparation method thereof and application of interface agent in fabricated building structure
  • Interface agent and preparation method thereof and application of interface agent in fabricated building structure
  • Interface agent and preparation method thereof and application of interface agent in fabricated building structure

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0044] Example 1

[0045] An interface agent for fabricated building structure, which is composed of component A and component B in the following parts by weight:

[0046] The composition of the component A calculated in parts by weight is:

[0047]

[0048] The composition of the component B calculated in parts by weight is:

[0049]

[0050] Among them, ordinary portland cement is PO 42.5 type cement; white silicate is 42.5 type cement; fine aggregate is 40 mesh quartz sand; mineral powder is ultra-fine mineral powder with a specific surface area of ​​1400 m2 / kg; dense silica fume The bulk density is 500kg / m3; the low temperature enhancer is a mixture of sodium silicate and calcium nitrate with a mass ratio of 1:1; the dispersant is a polycarboxylic acid early-strength powder water-reducing agent; the emulsion is a vinyl acetate-ethylene copolymer emulsion; Cellulose ether is 50,000 molecular weight hydroxypropyl cellulose ether; coagulant is hydroxyethylidene diphosphonic acid coa...

Example Embodiment

[0051] Example 2

[0052] An interface agent for fabricated building structures, which is composed of component A and component B in the following parts by weight:

[0053] The composition of the component A calculated in parts by weight is:

[0054]

[0055] The composition of the component B calculated in parts by weight is:

[0056]

[0057] Among them, ordinary portland cement is PO 42.5 type cement; white silicate is 42.5 type cement; fine aggregate is 40 mesh quartz sand; mineral powder is ultra-fine mineral powder with a specific surface area of ​​1400 m2 / kg; dense silica fume The bulk density is 500kg / m3; the low temperature enhancer is a mixture of sodium silicate and calcium nitrate with a mass ratio of 1:2; the dispersant is a polycarboxylate early-strength powder water-reducing agent; the emulsion is a vinyl acetate-ethylene copolymer emulsion; Cellulose ether is 80,000 molecular weight hydroxypropyl cellulose ether; coagulant is Shandong Zouping Dongfang Chemical Co., Lt...

Example Embodiment

[0058] Example 3

[0059] An interface agent for fabricated building structure, which is composed of component A and component B in the following parts by weight:

[0060] The composition of the component A calculated in parts by weight is:

[0061]

[0062] The composition of the component B calculated in parts by weight is:

[0063]

[0064] Among them, ordinary portland cement is PO 42.5 type cement; white silicate is 42.5 type cement; fine aggregate is 40 mesh quartz sand; mineral powder is ultra-fine mineral powder with a specific surface area of ​​1400 m2 / kg; dense silica fume The bulk density is 500kg / m3; the low temperature enhancer is a mixture of sodium silicate and calcium nitrate with a mass ratio of 1:1; the dispersant is a polycarboxylic acid early-strength powder water-reducing agent; the emulsion is a vinyl acetate-ethylene copolymer emulsion; Cellulose ether is 80,000 molecular weight hydroxypropyl cellulose ether; coagulant is Shandong Zouping Dongfang Chemical Co.,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Bulk densityaaaaaaaaaa
Bulk densityaaaaaaaaaa
Login to view more

Abstract

The invention provides an interface agent, a preparation method thereof and an application of the interface agent in a fabricated building structure. The interface agent uses an ultrafine composition,and the low-temperature construction performance and the bonding strength of the interface agent are improved. The interface agent is prepared from a component A and a component B, wherein the component A is prepared from ordinary Portland cement, white Portland cement, a low-temperature reinforcing agent, a dispersing agent, fine aggregate, mineral powder and dense silica fume, and the componentB is prepared from emulsion, cellulose ether, a thickening time control agent, a defoaming agent and water. The interface agent has the excellent characteristics of high bonding strength, long hardening time, low temperature resistance and the like. The interface agent is applied to a fabricated building structure, and has remarkable economic and social benefits for improving the construction efficiency and engineering quality of the fabricated building structure.

Description

technical field [0001] The invention relates to an interface agent, its preparation method and its application in assembled building structures. Background technique [0002] The construction of prefabricated building components involves the bonding of new and old concrete components such as laminated panels, balconies, air-conditioning panels, stairs, prefabricated beams, and prefabricated columns. However, due to the precast production process, the mold is coated with oil-based release agent, so that the product is still relatively smooth after demoulding, and the existing interface agent has poor permeability, and subsequent on-site pouring of new concrete is prone to hollowing, voiding, etc. problems, reducing the quality of construction. [0003] At the same time, during the assembly and construction of prefabricated components, the waiting time for the next process (new concrete pouring or grouting) after the application of the interface agent is relatively long, gene...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B18/14C04B28/04
CPCC04B40/0039C04B28/04C04B2111/00637C04B2201/50C04B14/06C04B18/12C04B18/146C04B12/04C04B22/085C04B2103/408C04B24/383C04B24/003C04B2103/50C04B24/2623C04B24/2676Y02W30/91
Inventor 沙建芳徐海源刘建忠郭飞刘加平夏中升李炜
Owner JIANGSU SOBUTE NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap