High-temperature-chlorine-corrosion-resistant coating for boiler heating surface, and preparation method thereof

A heating surface and high temperature resistance technology, applied in coatings, anti-corrosion coatings, fire-proof coatings, etc., can solve the problems of high brittleness, easy cracking, poor thermal shock resistance, etc., and achieve improved density and hardness, low cost, and increased The effect of strength and toughness

Active Publication Date: 2020-06-16
CHINA JILIANG UNIV
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The preparation of ceramic coatings by the precursor method has the advantages of simple process, convenient operation, and strong resistance to high-temperature chlorine corrosion, but it also has disadvantages such as easy cracking, high brittleness, and poor thermal shock resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature-chlorine-corrosion-resistant coating for boiler heating surface, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Weigh respectively 60% perhydropolysilazane and 20% graphite powder by volume, add them in turn to 20% butyl acetate, grind for 1 hour with a planetary ball mill, and then mechanically Stir with a mixer for 1 hour, then filter and encapsulate the paint sprayed as a transition layer. Then weigh the organopolysilazane, the barium glass powder of 30%, the zirconia powder of 15% and the aluminum powder of 5% respectively by volume percentage, add successively the butyl acetate of 30% by volume After being ground by a planetary ball mill for 1 hour, stirred by a mechanical stirrer for 1 hour, the coating sprayed as an organic polysilazane precursor composite ceramic coating was filtered and encapsulated.

[0021] The coating preparation process is as follows: first, the surface of the alloy steel substrate on the heating surface is pretreated by sandblasting; then the prepared transition layer coating is sprayed on the surface of the substrate, and placed in a heating furnac...

Embodiment 2

[0023] Weigh respectively 70% perhydropolysilazane and 15% graphite powder by volume, add them in turn to 15% butyl acetate, grind for 1 hour with a planetary ball mill, and then mechanically Stir with a mixer for 1 hour, then filter and encapsulate the paint sprayed as a transition layer. Then weigh the organopolysilazane, the barium glass powder of 25%, the zirconia powder of 20% and the aluminum powder of 10% respectively by volume percentage, add successively the butyl acetate of 20% by volume After being ground by a planetary ball mill for 1 hour, stirred by a mechanical stirrer for 1 hour, the coating sprayed as an organic polysilazane precursor composite ceramic coating was filtered and encapsulated.

[0024] The coating preparation process is consistent with Example 1.

Embodiment 3

[0026] Weigh respectively 60% perhydropolysilazane and 20% graphite powder by volume, add them in turn to 20% butyl acetate, grind for 1 hour with a planetary ball mill, and then mechanically Stir with a mixer for 1 hour, then filter and encapsulate the paint sprayed as a transition layer. Then weigh the organopolysilazane, the barium glass powder of 25%, the zirconia powder of 20% and the aluminum powder of 5% respectively by volume percentage, add successively the butyl acetate of 25% by volume After being ground by a planetary ball mill for 1 hour, stirred by a mechanical stirrer for 1 hour, the coating sprayed as an organic polysilazane precursor composite ceramic coating was filtered and encapsulated.

[0027] The coating preparation process is consistent with Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a high-temperature-chlorine-corrosion-resistant coating for a boiler heating surface, and a preparation method thereof. The coating comprises an inner transition layer and anouter protective layer, wherein the transition layer is a perhydropolysilazane precursor composite ceramic coating, the protective layer is an organic polysilazane precursor composite ceramic coating,the transition layer is formed by spraying surface of a steel matrix with a coating material consisting of 60-70% by volume of perhydropolysilazane, 10-20% by volume of graphite powder and 10-20% byvolume of butyl acetate and then curing at a high temperature of 200 DEG C, and the protective layer is formed by spraying the transition layer with a coating material consisting of 20-25% by volume of organic polysilazane, 25-30% by volume of barium glass powder, 15-20% by volume of zirconium oxide, 5-10% by volume of aluminum powder and 20-30% by volume of butyl acetate and curing at a high temperature of 700 DEG C. The coating is simple in preparation process and low in cost, can be suitable for high-temperature chlorine corrosion protection of heating surfaces of various biomass boilers, waste incineration boilers and high-chlorine coal boilers, and has the advantages of high toughness, compact surface, high thermal shock resistance and the like.

Description

technical field [0001] The invention belongs to the technical field of special coatings, and in particular relates to a high-temperature chlorine corrosion-resistant coating for a heating surface of a boiler and a preparation method thereof. Background technique [0002] Most of the biomass and garbage are high-chlorine fuels. Due to the growth environment and other factors, the chlorine content of the former is as high as 0.1-2% due to the growth environment and other factors, and the chlorine content of the latter is as high as 0.5-2% due to the presence of plastic, rubber and kitchen waste. 2%. When burning high-chlorine fuel, the heating surface of the boiler is prone to high-temperature chlorine corrosion. According to statistics, the corrosion rate of the tube wall on the heating surface of boilers burning biomass and domestic waste can reach 5-12 mm / year, resulting in frequent replacement of tubes on the heating surface, which seriously affects the safe and economica...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/18C09D5/10C09D183/16C09D7/61
CPCC08K2003/0812C08K2003/2244C09D5/103C09D5/18C09D183/16C09D7/61C08K3/04C08K3/00C08K3/40C08K3/22C08K3/08
Inventor 王进卿佟世琪王杰李探宇徐凯莉张晨阳马新宇王智猛张沐安林子祥
Owner CHINA JILIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com