Phosphaphenanthrene and polyphosphazene double-base synergistic flame-retardant acrylonitrile-butadiene-styrene copolymer composite material and preparation method thereof

A technology of styrene copolymer and composite material, which can be used in fireproof coatings, transportation and packaging, containers, etc. It can solve the problems of decreased mechanical properties and poor compatibility, and achieve excellent flame retardant properties, excellent mechanical properties, excellent Interface Compatibility Effects

Inactive Publication Date: 2020-07-03
GUIZHOU MINZU UNIV
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the technical problem of poor compatibility between DOPO flame retardants and polymer matrix or reinforcing materials in the above background technology, the present invention provides a phosphorus Phenanthrene and polyphosphazene double-base synergistic flame-retardant acrylonitrile-butadiene-styrene copolymer composite material and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Phosphaphenanthrene and polyphosphazene double-base synergistic flame-retardant acrylonitrile-butadiene-styrene copolymer composite material and preparation method thereof
  • Phosphaphenanthrene and polyphosphazene double-base synergistic flame-retardant acrylonitrile-butadiene-styrene copolymer composite material and preparation method thereof
  • Phosphaphenanthrene and polyphosphazene double-base synergistic flame-retardant acrylonitrile-butadiene-styrene copolymer composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A kind of preparation method of phosphaphenanthrene and polyphosphazene double base synergistic flame retardant acrylonitrile-butadiene-styrene copolymer composite material, comprises the following steps:

[0033] S1, the acrylonitrile-butadiene-styrene copolymer of 90kg, the vapor phase flame retardant of 2.5kg, the condensed phase flame retardant of 2.5kg, the compatibilizer of 5kg and the antioxidant of 0.5kg are in 80 After drying at °C, mix well to obtain a mixture. The drying time is 1-4 hours, until there is no obvious moisture.

[0034] S2. Blending and extruding the mixture in step S1 through a twin-screw extruder at 210-235° C., followed by cooling to room temperature, followed by hauling and pelletizing to obtain polylactic acid, phosphaphenanthrene and polyphosphorus Nitrile double base synergistic flame retardant composite material.

[0035] Described vapor phase flame retardant is reactive type phosphaphenanthrene, (DOPO) 2 -P-PPD-PH), the structure of ...

Embodiment 2

[0042] The difference with embodiment 1 is: in step S1, gas phase flame retardant gets 1.5kg, and condensed phase flame retardant gets 1.5kg.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of acrylonitrile-butadiene-styrene copolymer composite materials, and particularly relates to a phosphaphenanthrene and polyphosphazene double-base synergistic flame-retardant acrylonitrile-butadiene-styrene copolymer composite material and a preparation method thereof. The phosphaphenanthrene and polyphosphazene double-base synergistic flame-retardant acrylonitrile-butadiene-styrene copolymer composite material is prepared from, by mass, 80 to 95 parts of an acrylonitrile-butadiene-styrene copolymer, 2 to 5 parts of a gas-phase flame retardant, 2 to 5 partsof a a condensed-phase flame retardant, 5 to 10 parts of bulking agent and 0.5 part of an antioxidant. Due to the synergistic effect of the gas-phase flame retardant and the condensed-phase flame retardant, the gas-phase flame retardant is mainly used for gas-phase flame retardance, and the condensed-phase flame retardance is weak. The condensed-phase flame retardant is mainly used as a condensedphase, so that the gas-phase flame retardant is made up; and by mixing the gas-phase flame retardant, the liquid-phase flame retardant and the acrylonitrile-butadiene-styrene copolymer, the flame-retardant material has more excellent flame retardancy and excellent interfacial compatibility, so that the mechanical properties of the polymer flame-retardant material are not reduced and are enhanced.

Description

technical field [0001] The invention belongs to the field of acrylonitrile-butadiene-styrene copolymer composite materials, in particular to a kind of phosphaphenanthrene and polyphosphazene double base synergistic flame-retardant acrylonitrile-butadiene-styrene copolymer composite material and its preparation method. Background technique [0002] Acrylonitrile-butadiene-styrene copolymer (Acrylonitrile Butadiene Styrene) is abbreviated as AB, which is a thermoplastic polymer material with high strength, good toughness and easy processing. It is used to prepare various parts such as instruments, electrical appliances, machinery, etc. But acrylonitrile-butadiene-styrene copolymer is easy to burn. Halogenated flame retardants are used in acrylonitrile-butadiene-styrene copolymer resins, mainly polybrominated biphenyl compounds. Flame retardant effect, but halogen-containing flame retardants will emit toxic and corrosive gases and smoke when they are burned or processed at h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L55/02C08L85/02C08L51/00C08K5/527C08K5/5397C09D155/02C09D5/18B65D90/04B65D90/06
CPCB65D90/04B65D90/06B65D2590/023B65D2590/026C08L55/02C08L2201/02C08L2205/03C08L2205/08C09D5/18C09D155/02C08L85/02C08L51/003C08K5/527C08K5/5397
Inventor 张道海罗迎春谭芳宝冬梅田琴何敏秦舒浩左晓玲于杰
Owner GUIZHOU MINZU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com