A kind of nodular cast iron material for automobile hub and preparation method thereof

A technology for ductile iron and automobile hubs, which is applied in the field of nodular cast iron materials, can solve problems such as limited application and difficult shape of hubs, improve processing performance, increase strength, hardness and corrosion resistance, and improve heat strength and hydrogen resistance. Effect

Active Publication Date: 2021-07-30
SHANGHAI QINXUAN INFORMATION TECH CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the shortcomings of similar carbon steel hubs, as well as the complexity of the casting process and the limitation of the casting model, the shape of the hub is difficult to control, which limits its application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] An automotive hub balloje iron material, weight percent of each component, as follows: carbon: 3.99%, manganese: 0.28%, copper: 0.74%, silicon: 0.04% magnesium: 0.052%, chromium: 0.097%, nickel: 0.06%, Molybdenum: 0.1%, tungsten: 0.23%, niobium: 0.08%, boron: 0.006%, ruthenium: 0.004%, margin is iron and inevitable impurities.

[0023] The preparation method of the ink cast iron material for the car hub, including the following steps:

[0024] 1) Manufacture includes carbon: 3.99%, manganese: 0.28%, copper: 0.74%, silicon: 0.04% magnesium: 0.052%, chromium: 0.097%, nickel: 0.06%, molybdenum: 0.1%, tungsten: 0.23%, niobium: 0.08%, boron: 0.0026%, yttrium: 0.0063%, ruthenium: 0.004%, the margin is iron melting soup for iron and inevitable impurities;

[0025] 2) After the cast iron molten soup is treated with a spheroidized slag, it is placed in a mold to obtain a ball ink cast iron material.

[0026] The spherochemical gestation treatment is specifically: poured into the sph...

Embodiment 2

[0029] An automotive wheel ballochron cast iron material, weight percent of each component, as follows: carbon: 4.04%, manganese: 0.8%, silicon: 0.02% magnesium: 0.06%, chromium: 0.08%, nickel: 0.08%, Molybdenum: 0.06%, tungsten: 0.24%, niobium: 0.05%, boron: 0.003%, yttrium: 0.005%, ruthenium: 0.005%, margin is iron and inevitable impurities.

[0030] The preparation method of the ink cast iron material for the car hub, including the following steps:

[0031] 1) Manufacture includes carbon: 4.04%, manganese: 0.2%, copper: 0.8%, silicon: 0.02% magnesium: 0.06%, chromium: 0.08%, nickel: 0.08%, molybdenum: 0.06%, tungsten: 0.24%, niobium: 0.05%, boron: 0.003%, yttrium: 0.005%, ruthenium: 0.005%, margin is iron melting soup for iron and inevitable impurities;

[0032] 2) After the cast iron molten soup is treated with a spheroidized slag, it is placed in a mold to obtain a ball ink cast iron material.

[0033] The spheroidized gestation treatment is specifically: poured into the sphe...

Embodiment 3

[0035] An automotive hub ballojo iron material, weight percent of each component, as follows: carbon: 3.95%, manganese: 0.4%, copper: 0.7%, silicon: 0.06% magnesium: 0.049%, chromium: 0.12%, nickel: 0.05%, Molybdenum: 0.13%, tungsten: 0.22%, niobium: 0.1%, boron: 0.02%, yttrium: 0.008%, ruthenium: 0.003%, margin is iron and inevitable impurities.

[0036] The preparation method of the ink cast iron material for the car hub, including the following steps:

[0037] 1) Manufacture includes carbon: 3.95%, manganese: 0.4%, copper: 0.7%, silicon: 0.06% magnesium: 0.049%, chromium: 0.12%, nickel: 0.05%, molybdenum: 0.13%, tungsten: 0.22%, niobium: 0.1%, boron: 0.02%, yttrium: 0.008%, ruthenium: 0.003%, margin is a cast iron melting soup of iron and inevitable impurities;

[0038] 2) After the cast iron molten soup is treated with a spheroidized slag, it is placed in a mold to obtain a ball ink cast iron material.

[0039]The gestational gestation treatment is specifically: poured into th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention provides a nodular cast iron material for automobile hubs and a preparation method thereof, and relates to the technical field of nodular cast iron materials. The weight percentages of each component are as follows: carbon: 3.9-4.1%, manganese: 0.2-0.4%, copper: 0.6-0.9% , silicon: 0.02‑0.06%, magnesium: 0.04‑0.07%, chromium: 0.08‑0.12%, nickel: 0.04‑0.09%, molybdenum: 0.06‑0.13%, tungsten: 0.21‑0.26%, niobium: 0.05‑0.1%, boron : 0.01-0.04%, yttrium: 0.005-0.008%, cerium: 0.002-0.006%, the balance is iron and unavoidable impurities. The nodular cast iron for automobile wheel prepared by the invention through reasonable raw material ratio, appropriate preparation method and process parameters has excellent comprehensive properties such as high strength and elongation.

Description

Technical field [0001] The present invention relates to the technical field of ductile iron material, and in particular, a balloon cast iron material for automotive hub and a preparation method thereof. Background technique [0002] The car wheel is an important part of the car, which is directly related to the operation of the car, so the quality and performance of the car wheel must be guaranteed. A key factor affecting the quality and performance of the car wheel is the hub material. More materials used to produce the production of automotive hubs, as the development of related process technology and the continuous emergence of new materials, the automotive hub material is constantly updating, and more and more superior material materials are applied in the car hub production, different Material, the corresponding production process is also different. [0003] The hub material can be coarsely divided into three major categories such as steel materials, alloy materials, composi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C37/10C22C37/08C22C37/04C21C1/10C22C33/10
CPCC21C1/10C21C1/105C22C33/10C22C37/04C22C37/08C22C37/10
Inventor 黄远霞
Owner SHANGHAI QINXUAN INFORMATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products