Adhesive composition and a viscous-reducing adhesive tape for cutting optical filters

A composition and adhesive technology, applied in the directions of adhesives, adhesive types, ester copolymer adhesives, etc., can solve the problems of not easy to peel off, not easy to peel, low peeling force, etc., and achieve good pick-up. , Easy peeling, low peeling force

Active Publication Date: 2021-10-26
NINGBO EXCITON TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In order to solve the problem that the existing adhesive tape is not easy to peel off after the optical filter is cut and degummed, the present invention provides an adhesive composition and an adhesive tape used for cutting optical filters
The adhesive composition is cured to form an adhesive layer, and the prepared adhesive-reducing adhesive tape is subjected to UV debonding after the optical filter is cut, and the peeling force is low after UV degumming, and it is easy to separate from the optical filter, which solves the problem There is a problem that the adhesive tape is not easy to peel off after the filter is cut and degummed
[0008] On the other hand, in order to solve the problem that the film needs to be poured after the existing optical filter is cut and degummed, the present invention provides an adhesive composition and an adhesive tape for cutting the optical filter

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Adhesive composition and a viscous-reducing adhesive tape for cutting optical filters
  • Adhesive composition and a viscous-reducing adhesive tape for cutting optical filters
  • Adhesive composition and a viscous-reducing adhesive tape for cutting optical filters

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0071] The invention provides an adhesive composition and a viscous-reducing adhesive tape applied to cutting filters.

[0072] In the adhesive composition, select butyl (meth)acrylate unit (45-55%), methyl (meth)acrylate unit (40-50%) and 2-hydroxyethyl (meth)acrylate A (meth)acrylate copolymer (commercially available product A) composed of units (1-5%), with a weight-average molecular weight of 500,000-600,000, weighing 100 parts by mass; select a polyurethane containing 10 unsaturated double bond functional groups Acrylate oligomer (commercially available product A), molecular weight 40000, weighing 30 parts by mass; choose hexafunctional dipentaerythritol hexaacrylate as polyfunctional acrylic acid monomer (manufactured by Changxing Chemical: EM265), weigh 5.0 parts by mass; choose Toluene diisocyanate was used as a curing agent (manufactured by Tosoh Chemical: CORONATE L), weighing 1.5 parts by mass; 1-hydroxycyclohexyl phenyl ketone was selected as a photoinitiator (manu...

Embodiment 2

[0075] The invention provides an adhesive composition and a viscous-reducing adhesive tape applied to cutting filters.

[0076] In the adhesive composition, select butyl (meth)acrylate unit (45-55%), methyl (meth)acrylate unit (40-50%) and 2-hydroxyethyl (meth)acrylate A (meth)acrylate copolymer (commercially available product A) composed of units (1-5%), with a weight-average molecular weight of 500,000-600,000, weighing 100 parts by mass; select a polyurethane containing 10 unsaturated double bond functional groups Acrylate oligomer (commercially available), molecular weight 40000, weighing 30 parts by mass; choose hexafunctional dipentaerythritol hexaacrylate as polyfunctional acrylic acid monomer (manufactured by Changxing Chemical: EM265), weigh 10 parts by mass; choose toluene Diisocyanate was used as a curing agent (manufactured by Tosoh Chemical: CORONATE L), and 1.5 parts by mass was weighed; 1-hydroxycyclohexyl phenyl ketone was used as a photoinitiator (manufactured...

Embodiment 3

[0079] The invention provides an adhesive composition and a viscous-reducing adhesive tape applied to cutting filters.

[0080] In the adhesive composition, select butyl (meth)acrylate unit (45-55%), methyl (meth)acrylate unit (40-50%) and 2-hydroxyethyl (meth)acrylate A (meth)acrylate copolymer (commercially available product A) composed of units (1-5%), with a weight-average molecular weight of 500,000-600,000, weighing 100 parts by mass; Urethane acrylate oligomer (commercially available product A), molecular weight 40,000, weighed 30 parts by mass; selected hexafunctional dipentaerythritol hexaacrylate as the polyfunctional acrylic monomer (manufactured by Changxing Chemical: EM265), weighed 5.0 parts by mass; Select toluene diisocyanate as a curing agent (manufactured by Tosoh Chemical: CORONATE L), and weigh 1.5 parts by mass; select 1-hydroxycyclohexyl phenyl ketone as a photoinitiator (manufactured by BASF: 184), and weigh 1.5 parts by mass.

[0081] The adhesive comp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
elastic modulusaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to an adhesive tape, in particular to an adhesive composition, an adhesive tape applied to cutting filters and a preparation method thereof. In order to solve the problem that the existing adhesive tape is not easy to peel off after the optical filter is cut, the present invention provides an adhesive composition and an adhesive tape used for cutting the optical filter. The adhesive composition comprises 100 parts by mass of (meth)acrylate copolymer, 30 parts by mass of polyurethane acrylate oligomer containing 10 unsaturated double bond functional groups, polyfunctional acrylic acid containing 6 unsaturated double bond functional groups 5.0-10.0 parts by mass of ester monomer, 1.5 parts by mass of curing agent, and 1.5 parts by mass of photoinitiator. The adhesive composition is cured to form an adhesive layer, and the prepared adhesive-reducing adhesive tape is subjected to UV debonding after the optical filter is cut, and the peeling force is low after UV degumming, and it is easy to separate from the optical filter, which solves the problem There is a problem that the adhesive tape is not easy to peel off after the filter is cut.

Description

technical field [0001] The invention relates to an adhesive tape, in particular to an adhesive composition and an adhesive tape applied to cut filters. Background technique [0002] Camera modules are an important part of mobile devices such as smartphones or tablets, and are developing in the direction of miniaturization, integration and functionality. In order to eliminate the impact of infrared light on solid-state electronic devices CCD (Charge Coupled Device, which is a charge-coupled device image sensor) or CMOS (Complementary Metal Oxide Semiconductor, originally meant to refer to complementary metal oxide semiconductors, a large-scale application in the manufacture of integrated circuit chips The raw material is a readable and writable RAM chip on the motherboard of the microcomputer, which is used to save the hardware configuration of the current system and the user's setting of certain parameters) and other imaging effects, usually by adding an infrared cut filter ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More