Ultralow-temperature-resistant rubber and plastic product and preparation method thereof

A rubber and plastic product, ultra-low temperature technology, applied in the field of rubber and plastic products, can solve the problems of poor low temperature resistance of rubber, and achieve the effects of improving resilience, uniform cells, and improving dispersion

Active Publication Date: 2020-09-15
HEBEI SHENZHOU THERMAL INSULATION BUILDING MATERIAL GRP CO LTD
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention proposes an ultra-low temperature resistant rubber and plastic product and its preparation method, which solves the problem of poor low temperature resistance of rubber in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultralow-temperature-resistant rubber and plastic product and preparation method thereof
  • Ultralow-temperature-resistant rubber and plastic product and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A kind of ultra-low temperature resistant rubber and plastic product, including 20 parts of EPDM rubber, 5 parts of butyl rubber, 1 part of butadiene rubber, 7 parts of foaming agent, 20 parts of flame retardant, and 8 parts of process oil in parts by mass 4 parts of low-temperature plasticizer, 0.5 part of active agent, 0.1 part of stearic acid, 5 parts of protective wax, 3 parts of accelerator, 0.8 part of vulcanizing agent, and 0.1 part of pigment fast yellow.

[0025] Among them, the foaming agent includes foaming agent DC-W, triammonium citrate, and polyisobutylene succinimide dispersant T155 with a mass ratio of 1:0.8:0.54; the low-temperature plasticizer includes a mass ratio of 0.5:1:1.2 Dibutylmethylene dithioethylene glycol ester, epoxy tall oil fatty acid 2-ethylhexyl ester, polyethylene glycol monomethyl ether acrylate; accelerators include accelerators with a mass ratio of 1:1.1 NA-22 and accelerator TMTD; the vulcanizing agent includes sulfur and bis(1,5-p...

Embodiment 2

[0032] A kind of ultra-low temperature resistant rubber and plastic product, including 25 parts of EPDM rubber, 3 parts of butyl rubber, 1.5 parts of butadiene rubber, 5 parts of foaming agent, 30 parts of flame retardant, and 6 parts of process oil in parts by mass 7 parts, 7 parts of low temperature plasticizer, 0.3 part of active agent, 0.3 part of stearic acid, 3 parts of protective wax, 5 parts of accelerator, 0.5 part of vulcanizing agent, 0.2 part of pigment phthalocyanine.

[0033] Among them, the foaming agent includes foaming agent DC-W, triammonium citrate, and polyisobutylene succinimide dispersant T155 with a mass ratio of 1:1:0.25; the low-temperature plasticizer includes a mass ratio of 0.85:1:1 Dibutylmethylene dithioethylene glycol ester, epoxy tall oil fatty acid 2-ethylhexyl ester, polyethylene glycol monomethyl ether acrylate; accelerators include accelerators with a mass ratio of 1:1.14 NA-22 and accelerator TMTD; the vulcanizing agent includes sulfur and ...

Embodiment 3

[0040]A kind of ultra-low temperature resistant rubber and plastic product, including 22 parts of EPDM rubber, 4 parts of butyl rubber, 1.2 parts of butadiene rubber, 6 parts of foaming agent, 25 parts of flame retardant, and 7 parts of process oil in parts by mass 5 parts, 5 parts of low temperature plasticizer, 0.4 part of active agent, 0.2 part of stearic acid, 4 parts of protective wax, 4 parts of accelerator, 0.7 part of vulcanizing agent, 0.15 part of pigment phthalogreen.

[0041] Among them, the foaming agent includes foaming agent DC-W, triammonium citrate, and polyisobutylene succinimide dispersant T155 with a mass ratio of 1:0.9:0.3; the low-temperature plasticizer includes a mass ratio of 0.6:1:1.1 Dibutylmethylene dithioethylene glycol ester, epoxy tall oil fatty acid 2-ethylhexyl ester, polyethylene glycol monomethyl ether acrylate; accelerators include accelerators with a mass ratio of 1:1.12 NA-22 and accelerator TMTD; the vulcanizing agent includes sulfur and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
brittleness temperatureaaaaaaaaaa
tensile strengthaaaaaaaaaa
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of rubber and plastic products, and provides an ultralow-temperature-resistant rubber and plastic product. The product comprises, by mass, 20-25 parts of ethylene propylene diene monomer rubber. 3-5 parts of butyl rubber, 1-1.5 parts of butadiene rubber, 5-7 parts of a foaming agent, 20-30 parts of a flame retardant, 6-8 parts of operating oil, 4-7 parts of a low-temperature plasticizer, 0.3-0.5 part of an activator, 0.1-0.3 part of stearic acid, 3-5 parts of protective wax, 3-5 parts of an accelerant, 0.5-0.8 part of a vulcanizing agent and 0.1-0.2part of pigment. The ethylene propylene diene monomer, the butyl rubber, the butadiene rubber, the foaming agent, the flame retardant, the pigment, the operating oil, the low-temperature plasticizer,the protective wax, the activator and the stearic acid are subjected to banburying, discharging, open milling, compound milling and storage for 22-26 h, the vulcanizing agent and the accelerant are added, and mixing, extrusion molding and vulcanization foaming are conducted to obtain the ultralow-temperature-resistant rubber and plastic product. Through the technical scheme, the problem of poor low-temperature resistance of rubber in the prior art is solved.

Description

technical field [0001] The invention belongs to the technical field of rubber and plastic products, and relates to an ultra-low temperature resistant rubber and plastic product and a preparation method thereof. Background technique [0002] The rubber industry is an important part of my country's chemical industry and is a highly elastic polymer material with reversible deformation. It is elastic at room temperature, can produce large deformation under a small external force, and can return to its original shape after the external force is removed. Its glass transition temperature (Tg) is low, and its molecular weight is often large, greater than hundreds of thousands. It not only provides people with daily-use, medical and other light industrial rubber products that are indispensable in daily life, but also plays an indispensable role in heavy and emerging industries such as transportation, construction, machinery and electronics. Due to the poor low temperature resistanc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08L23/22C08L9/00C08L91/06C08L23/06C08L71/02C08K13/02C08K5/09C08K5/372C08K3/38C08K3/22C08J9/08C08J9/10
CPCC08J9/0061C08J9/103C08J9/08C08J9/0023C08J9/0033C08J9/0066C08J9/0095C08J2323/16C08J2423/22C08J2409/00C08J2491/06C08J2423/06C08J2471/02C08K13/02C08K5/09C08K5/372C08K2003/387C08K3/2279C08K2003/2227C08J2203/04C08J2203/18
Inventor 高铁强高铁彦高景岐
Owner HEBEI SHENZHOU THERMAL INSULATION BUILDING MATERIAL GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap