A kind of preparation technology of high stability waterborne paint

A water-based coating, high stability technology, applied in coatings, separation methods, grain processing, etc., can solve the problems that affect the processing and production efficiency of water-based coatings, reduce the efficiency of coating raw material grinding, affect the use of water-based coatings, etc., and achieve freeze-thaw Good stability, good storage stability, and the effect of reducing impurities and solid precipitation

Active Publication Date: 2021-08-31
江苏秦港新材料科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, when the existing water-based paints on the market are used, the water-based paints are prone to precipitation and stratification during the long-term storage process, and the water-based paints are placed in a warm room when the external temperature is low, which is easy to cause Flocs appear inside the water-based paint, which affects the use of water-based paint;
[0004] Moreover, when the existing water-based paint grinder is in use, when the paint raw material is ground, it is prone to incomplete grinding, and the incompletely ground paint raw material will be directly discharged along with the raw material, requiring staff to filter the ground paint, And repeated grinding, resulting in a reduction in the efficiency of coating raw material grinding, affecting the processing and production efficiency of water-based coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation technology of high stability waterborne paint
  • A kind of preparation technology of high stability waterborne paint
  • A kind of preparation technology of high stability waterborne paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Such as figure 1 Shown, the present invention provides technical scheme, a kind of preparation technology of high-stability water-based coating, high-stability water-based coating is made up of following components by weight:

[0046] 100 parts by weight of water-based resin, 9 parts by weight of nano-calcium carbonate, 6 parts by weight of film-forming aid, 1 part by weight of preservative, 10 parts by weight of talcum powder, 17 parts by weight of pigment, 0.8 parts by weight of thickener, and 0.4 parts by weight of dispersant , 0.4 parts by weight of an antifoaming agent and 50 parts by weight of deionized water.

[0047] According to the above technical features, the film-forming aid is specifically dodecyl alcohol ester, the preservative is specifically isothiazolinone, the thickener is specifically polyacrylic acid thickener, and the dispersant is specifically polyacrylic acid ammonium salt.

[0048] According to above-mentioned technical feature, a kind of prepa...

Embodiment 2

[0057] Such as figure 1 Shown, the present invention provides technical scheme, a kind of preparation technology of high-stability water-based coating, high-stability water-based coating is made up of following components by weight:

[0058] 80 parts by weight of water-based resin, 7 parts by weight of nano-calcium carbonate, 3 parts by weight of film-forming aid, 0.5 parts by weight of preservative, 8 parts by weight of talcum powder, 10 parts by weight of pigment, 0.4 parts by weight of thickener, and 0.2 parts by weight of dispersant , 0.1 parts by weight of an antifoaming agent and 40 parts by weight of deionized water.

[0059] According to the above technical features, the film-forming aid is specifically ethylene glycol, the preservative is specifically a nitrogen-sulfur cyclic compound, the thickener is specifically a polyacrylic acid thickener, and the dispersant is specifically a polyacrylic acid ammonium salt.

[0060] According to above-mentioned technical feature...

Embodiment 3

[0069] Such as figure 1 Shown, the present invention provides technical scheme, a kind of preparation technology of high-stability water-based coating, high-stability water-based coating is made up of following components by weight:

[0070] 120 parts by weight of water-based resin, 12 parts by weight of nano-calcium carbonate, 9 parts by weight of film-forming aid, 1.5 parts by weight of preservative, 12 parts by weight of talc, 24 parts by weight of pigment, 1.2 parts by weight of thickener, and 0.6 parts by weight of dispersant , 0.6 parts by weight of an antifoaming agent and 60 parts by weight of deionized water.

[0071] According to the above technical features, the film-forming aid is specifically dodecyl alcohol ester, the preservative is specifically isothiazolinone, the thickener is specifically high molecular weight hydroxyethyl cellulose, and the dispersant is specifically polycarboxylate sodium salt.

[0072] According to above-mentioned technical feature, a kin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation process of a high-stability water-based coating. The high-stability water-based coating is composed of the following components in parts by weight: 80-120 parts by weight of water-based resin, 7-12 parts by weight of nano-calcium carbonate, and 3-9 parts by weight of film aid, 0.5-1.5 parts by weight of preservative, 8-12 parts by weight of talcum powder, 0-24 parts by weight of pigment, 0.4-1.2 parts by weight of thickener, 0.2-0.6 parts by weight of dispersant, 0.1-0.6 parts by weight of foaming agent and 40-60 parts by weight of deionized water. The structure of the present invention is scientific and reasonable, and it is safe and convenient to use. The prepared water-based paint has the best storage stability, and is not prone to precipitation and stratification during long-term storage. The thawing stability is the best, and no flocs will appear after freezing and thawing. The pH value of the prepared water-based coating is more neutral and less corrosive.

Description

technical field [0001] The invention relates to the technical field of water-based paints, in particular to a preparation process of high-stability water-based paints. Background technique [0002] Water-based coatings include water-soluble coatings, water-diluted coatings and water-dispersible coatings. Water-soluble coatings use water-soluble resins as film-formers, represented by polyvinyl alcohol and its various modified products. In addition, there are Water-soluble alkyd resin, water-soluble epoxy resin and inorganic polymer water-based resin, etc., water-based coatings need to go through material selection, stirring, crushing and grinding, secondary feeding and stirring, and filtration and screening in the process of production and packaging; [0003] At present, when the existing water-based paints on the market are used, the water-based paints are prone to precipitation and stratification during the long-term storage process, and the water-based paints are placed in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D201/00C09D7/61B01D46/10B01D53/04B01D53/18B01D53/26B02C17/16B02C17/22B02C17/24
CPCB01D46/10B01D53/04B01D53/18B01D53/26B02C17/16B02C17/163B02C17/22B02C17/24C08K2003/265C08K2201/011C09D201/00C09D7/61C08K13/02C08K3/26C08K3/34
Inventor 刘易承李向和卫凤仪
Owner 江苏秦港新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products