Water-soluble copolymers

A water-soluble copolymer and alkene technology, which can be used in ester copolymer adhesives, dissolution, amide/imide polymer adhesives, etc., and can solve problems such as brittleness

Active Publication Date: 2020-10-27
WACKER CHEM GMBH
View PDF24 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage is that this protective colloid-stabilized polymer crosslinks and thus becomes brittle when used in acidic environments or under thermal stress

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0101] A mixture of 269 g of deionized water and 0.74 g of potassium peroxodisulfate was first charged into a 2 liter volume reactor in a nitrogen atmosphere, and the mixture was heated to 80° C. with stirring. At this temperature, 680 g of Geniosil GF 56 (trade name of Wacker Chemie; vinyltriethoxy silane) into the reactor was metered in over 90 minutes and 62 g of an initiator solution of potassium peroxodisulfate (3% in water) were metered in over 150 minutes. At the end of the initiator metering, the mixture was afterpolymerized at 80° C. for 1 hour. The polymer solution was then cooled to room temperature.

[0102] The solution obtained had a solids content of 20% and a viscosity of 685 mPa.s (measured with a Brookfield viscometer, using spindle 2, at 25° C. and 20 rpm).

Embodiment 3

[0108] With 2335g deionized water, 86.4g as the polymer solution of the water-soluble copolymer of the embodiment 1 of protective colloid, 0.05g Dissolvine Na (ethylenediaminetetraacetic acid disodium salt), 2.5g FAS (aminoiminomethanide) Sulphonic acid, 10% in water) and 24.1 g of TBHP (tert-butyl hydroperoxide, 10% in water) were initially charged in a 2 liter volume reactor under a nitrogen atmosphere, and the mixture was heated under stirring to 70°C.

[0109] At this temperature, monomers of 565.2 g of butyl acrylate, 100.3 g of styrene, 2.7 g of Geniosil GF 56 (trade name of Wacker Chemie; vinyltriethoxysilane) were metered into the reactor over 210 minutes mixture and metered in 83.6 g FF6 ( Trade name of Bürgemann Chemical; 12% in water) and TBHP (tert-butyl hydroperoxide, 10% in water).

[0110] At the end of the initiator metering, the mixture was afterpolymerized at 70° C. for 1 hour. The polymer solution was then cooled to room temperature.

[0111] The disper...

Embodiment 4

[0113] Example 4 was carried out analogously to Example 3, except that no Geniosil GF 56 (vinyltriethoxysilane) was used in the polymerization to prepare the polymer dispersion.

[0114] The dispersion obtained had a solids content of 58.5% and a viscosity of 11400 mPa.s (determined with a Brookfield viscometer, using spindle 3, at 25° C. and 20 rpm). Particle size determination by Coulter LS 230 gave a Dw value of 1380 nm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
solid contentaaaaaaaaaa
Login to View More

Abstract

The invention relates to water-soluble copolymers based on a) 50 to 97 wt.% of one or more non-ionic monomers that contain ethylenically unsaturated amide groups, b) 0.1 to 10 wt.% of one or more monomers that contain ethylenically unsaturated silane groups, and c) 1 to 30 wt.% of one or more ionic, ethylenically unsaturated monomers and optionally one or more other ethylenically unsaturated monomers, the amounts in wt.% adding up to 100 wt.%.

Description

technical field [0001] The present invention relates to water-soluble copolymers based on nonionic and ionic monomers containing amide groups, their production and use, for example, as aqueous polymer dispersions or as protective powders redispersible in water colloid. Background technique [0002] Water-soluble polymers are used, for example, as protective colloids, for stabilizing aqueous dispersions of water-insoluble polymers or for producing polymer powders which are redispersible in water. Such polymer dispersions or polymer powders can be used, for example, in construction chemicals. Common protective colloids are polyvinyl alcohol, polyvinylpyrrolidone, cellulose or starch, as described in EP-A133899, WO-A 84 / 00369 or EP-B 62106. In order to obtain a sufficient stabilizing effect, such protective colloids sometimes have to be used in large quantities, which may be related to the disadvantage that by adding protective colloids, the binder content of the dispersion i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F220/56C08F265/06C08F230/08C08F2/20
CPCC08F2/20C08F220/56C08F265/06C08F2/24C08F230/085C09K23/00C09K23/16C04B24/2652C04B24/163C04B24/2688C04B2111/21C04B2111/29C08F220/1804C08F212/08C08F230/08C08F228/02B01J13/0021B01J13/0034C08J3/05C08J2333/08C08J2333/26C08J2341/00C09D5/002C09D133/08C09D133/26C09D141/00C09J133/08C09J133/26C09J141/00C09K3/22D21H17/375D21H21/50
Inventor 阿卜杜尔马杰德·哈什姆扎德
Owner WACKER CHEM GMBH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com