Thermosetting resin composition, coating material for pre-coated metal, cured product, and laminate

A resin composition, thermosetting technology, applied in synthetic resin layered products, coatings, devices for applying liquid to surfaces, etc., can solve problems such as insufficient performance

A resin composition, thermosetting technology, applied in synthetic resin layered products, coatings, devices for applying liquid to surfaces, etc., can solve problems such as insufficient performance

CN112004890AActive Publication Date: 2020-11-27MITSUI CHEM INC
18 Cites 1 Cited by

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermosetting resin composition, coating material for pre-coated metal, cured product, and laminate
  • Thermosetting resin composition, coating material for pre-coated metal, cured product, and laminate
  • Thermosetting resin composition, coating material for pre-coated metal, cured product, and laminate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0135] Hereinafter, the present invention will be more specifically described based on examples, but the present invention is not limited by these examples.

[0136] [Material]

[0137] In the following examples and comparative examples, the compositions (coating materials) and raw materials used for the preparation of the coating materials, and the covered bodies (substrates) used for coating the compositions are as follows.

[0138]

[0139] "Polyester Resin with Hydroxyl Group"

[0140] ・(A-1) "Almatex P646" manufactured by Mitsui Chemicals Co., Ltd.

[0141] Solvent: mixed solvent of SOLVESSO #100 (manufactured by ExxonMobil Chemical Co., SP value=18.0) / methyl isobutyl ketone (SP value=17.2)=9 / 1

[0142] Solid content: 60%

[0143] Weight average molecular weight: 51,000

[0144] Hydroxyl value: 52mgKOH / g

[0145] ・(A-2) "Almatex P646SB" manufactured by Mitsui Chemicals Co., Ltd.

[0146] Solvent: sec-butanol (SP value = 22.1)

[0147] Solid content: 60%

[0148]...

Embodiment A1～29

[0253] [Examples A1-29, Comparative Examples A1-20]

[0254] By mixing resin (A) or (a) having a hydroxyl group, melamine resin (B), Lewis acid catalyst (C) or other catalyst (c') and solvent (D) in the ratio shown in Tables 2-4, Thus, a composition (coating material) was prepared and evaluated.

[0255] After the obtained composition was coated on a steel plate (150 mm x 70 mm x thickness 0.8 mm) using a bar coater so that the cured film thickness became 15 μm, the composition was cured by heating at 80° C. for 30 minutes, Thus, a test panel with a coated film was prepared and evaluated.

[0256] The evaluation results are shown in Tables 2-4.

[0257] [Table 2]

[0258]

[0259] [table 3]

[0260]

[0261] [Table 4-1]

[0262] Table 4-1

[0263]

[0264] 1) SOLVESSO 100 / methyl isobutyl ketone = 9 / 1 (weight) 5) Mixed solvent of n-butyl acetate and methyl isobutyl ketone

[0265] 2) sec-butanol 6) isobutanol

[0266] 3) mixed solvent of toluene and n-butyl ace...

Embodiment A30～45 and comparative example A21～39

[0276] The composition is prepared by mixing titanium oxide dispersed polyol solution A1, melamine resin (B), Lewis acid catalyst (C) or other catalyst (c'), and solvent (D) at the ratios shown in Tables 5 to 7 (white coating material) and evaluated.

[0277] After the obtained composition was coated on a steel plate (150 mm x 70 mm x thickness 0.8 mm) using a bar coater so that the cured film thickness became 15 μm, the composition was cured by heating at 80° C. for 30 minutes, Thus, a test panel with a coated film was prepared and evaluated.

[0278] The evaluation results are shown in Tables 5-7.

[0279] [table 5]

[0280]

[0281] [Table 6-1]

[0282]

[0283] [Table 6-2]

[0284] Table 6-2

[0285]

[0286] 1) SOLVESSO 100 / methyl isobutyl ketone=9 / 1 (weight)

[0287] 2) Isobutanol

[0288] [Table 7]

[0289] Table 7

[0290]

[0291] 1) SOLVESSO 100 / methyl isobutyl ketone=9 / 1 (weight)

[0292] 2) Isobutanol

[0293] 3) mixed xylene / n-butanol=4 / 6 (w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Hydroxyl valueaaaaaaaaaa
Hydroxyl valueaaaaaaaaaa
Hydroxyl valueaaaaaaaaaa
Login to View More

Abstract

The purpose of the present invention is to provide a thermosetting resin composition that has excellent storage stability and is able to obtain, at a low temperature, a cured film having excellent durability and appearance. The thermosetting resin composition according to the present invention contains: a resin that has a specific hydroxyl group; (B) an alkyl etherified melamine resin; (C) a Lewisacid catalyst that comprises a cation comprising a metal having a Pauling electronegativity of 1.31 to 2.02, and that comprises, as a counter anion, a deprotonated protonic acid having an acid dissociation constant pKa of no more than 1.0; and (D) a solvent, wherein the solvent (D) contains a solvent (D-1) that has a Hildebrand solubility parameter value (SP value) of 18.6 to 47.9, the content ofthe solvent (D-1) is at least 21% by mass with respect to the total amount of the solvent (D), and within the solvent (D-1), the content of a solvent (D-S) that has a solubility of the Lewis acid catalyst (C) of at least 0.01% by mass is at least 4% by mass with respect to the total amount of the solvent (D).

Description

technical field [0001] The present invention relates to a thermosetting resin composition, a cured product containing the composition, and a laminate containing a cured film containing the composition. [0002] Furthermore, the present invention relates to a coating material for precoated metal, a cured product including the coating material, and a laminate including a cured film including the coating material. Background technique [0003] Conventionally, thermosetting resin compositions containing polyols and alkyl-etherified melamines have been used in various fields such as automotive coatings and home appliance coatings, and the compositions are required to have good storage stability and the durability and durability of the resulting cured film. Excellent appearance. In addition, the curing of the above-mentioned thermosetting resin composition requires a heating time at a temperature of approximately 110 to 160° C. for 10 to 60 minutes. However, from the viewpoint of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
27 Nov 2020
Publication
CN112004890A
IPC
C08L101/06; B05D7/24; B32B27/26; C08L33/14; C08L61/30; C08L67/00; C08L75/04
CPC
B05D7/24; B32B27/26; C08L33/14; C08L61/30; C08L67/00; C08L75/04; C08L101/06
Inventors
市原有人; 浅野阳介