A kind of stripping method of diaspore type bauxite

A technology of bauxite and bauxite, applied in chemical instruments and methods, preparation of alkali metal aluminate/aluminum oxide/aluminum hydroxide, aluminum compounds, etc., can solve the problem of large lime consumption and alkali content in effluent red mud High-level problems, to reduce economic costs, realize solid waste reuse, and improve the effect of red mud composition

Active Publication Date: 2021-06-29
CENT SOUTH UNIV
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The application requires a large amount of lime consumption, and the alkali content of the discharged red mud is relatively high, which brings great risks to the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of stripping method of diaspore type bauxite

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Dissolution of diaspore ore, the specific operation process is as follows figure 1 As shown, 30g of Shanxi mine A (the specific composition is shown in Table 1) and 60mL of sodium aluminate solution (Na 2 o K : 220g / L, α K : 2.9, alpha K is the molar ratio of sodium oxide to alumina), added to the low-pressure steel bomb, added steel balls to strengthen stirring, and pre-desiliconized at a temperature of 90 ° C for 4 hours (pre-desiliconized bauxite is mixed with the circulating mother liquor, stirred, and kept warm The process of removing silicon from ores). Dissolution red mud mixed with lime, CaO / Na 2 The molecular ratio of O is 4, and the liquid-solid ratio is 4. Take 0.2g of dried dealkalized red mud and pre-desiliconized slurry, mix it into high-pressure steel bombs, replenish the circulating mother liquor to 100ml, dissolve at a temperature of 260°C for 60 minutes, separate the solid-liquid of the dissolved slurry, and the aluminum-silicon ratio of the red m...

Embodiment 2

[0034] The basic content of this embodiment is the same as that of embodiment 1, the difference is that after the red mud is dissolved and mixed with lime, the CaO / Na 2 The molecular ratio of O is 2, and the liquid-solid ratio is 5. Take 0.4g of dried dealkalized red mud and pre-desiliconized slurry and mix it with the high-pressure steel bomb. The dissolution rate is 98.95%.

Embodiment 3

[0036] The content of this example is basically the same as Example 1, except that 30g of Shanxi Mine B (the specific components are shown in Table 1) and 60mL of sodium aluminate solution (Na 2 o K : 230g / L, α K : 3.0), pre-desilicate at a temperature of 95°C for 6 hours, and dissolve at a temperature of 260°C for 70 minutes, the relative dissolution rate of alumina is 96.1%, and the amount of red mud is reduced by 32.5% compared with the traditional lime method.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for dissolving diaspore type bauxite, which belongs to the technical field of hydrometallurgy. In the present invention, the diaspore-type bauxite is uniformly mixed with the circulating mother liquor for pre-desilication treatment, and the obtained pre-desilication slurry is then mixed with the dealkalized red mud to enter high-temperature dissolution, and the dissolved slurry is diluted and desiliconized, and the red mud settles The red mud is obtained after separation and washing treatment, and the red mud is dealkalized with lime to obtain dealkalized red mud, and part of the dealkalized red mud is returned to the high-temperature dissolution step, so that calcium can be recycled. Compared with the prior art, the relative dissolution rate of alumina in the ore of the present invention is significantly improved, and the use of dealkalized red mud instead of lime can greatly reduce the amount of lime added, reduce waste discharge, is beneficial to environmental protection, and has low cost. Value.

Description

technical field [0001] The invention relates to the technical field of hydrometallurgy, in particular to a method for leaching diaspore type bauxite. Background technique [0002] my country's bauxite reserves are abundant, but from the perspective of bauxite types, my country's bauxite is mainly diaspore-type bauxite, which accounts for about 98% of the total reserves, and generally has high aluminum and high silicon , low-iron and silicon-containing minerals, complex composition, etc., and most of them are ores with medium and low aluminum-silicon ratios, and their aluminum-silicon ratio is about 4-7. About 10% of resources, or even lower. At present, in order to eliminate the blocking effect of titanium minerals, domestic alumina enterprises generally add 8% to 12% lime. In addition to ensuring the full dissolution of diaspore, it also removes fluorine, phosphorus, vanadium and other elements in the solution. The transformation of iron ore plays an important role in delay...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01F7/06
CPCC01F7/0606C01F7/0646C01F7/0666C01F7/0693
Inventor 周秋生程路伟王一霖李小斌彭志宏刘桂华齐天贵
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More