A kind of long-acting anti-icing paint and its preparation method and application

An anti-icing and coating technology, used in polyurea/polyurethane coatings, coatings, devices for coating liquids on surfaces, etc. problem, to achieve the effect of delaying volatilization

Active Publication Date: 2022-04-29
SOUTHEAST UNIV +1
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Technical problem to be solved: In view of the above technical problems, in order to avoid the poor wear resistance of the superhydrophobic anti-icing coating and the insufficient service life of the lubricating coating, the present invention provides a long-acting anti-icing coating and its preparation method and application. Easy to operate, low cost, simple and effective, the prepared coating has both anti-icing and durable wear resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of long-acting anti-icing paint and its preparation method and application
  • A kind of long-acting anti-icing paint and its preparation method and application
  • A kind of long-acting anti-icing paint and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] In this embodiment, a modified nano-silica nano-solution is used. Include the following steps:

[0029] (1) Preparation of modified porous silica powder: mix ethanol, deionized water, and ammonia water in a ratio of 20:4:1, stir evenly, add 1vol.% nano-chain silica sol solution dropwise, and then add 0.6vol.% TEOS is used as a cross-linking agent, and then 0.6vol.% n-octyltriethoxysilane is added for surface modification. Finally, the beaker is sealed and stirred for 24 hours to obtain modified nano-SiO 2 solution. Move the solution into an oven at 120°C, dry it completely, and sieve it with a 200-mesh sieve to obtain the modified porous powder;

[0030] (2) Preparation of oil storage powder: Mix 1 g of the modified porous powder prepared in step (1) with 4 g of simethicone oil with a viscosity of 500 CS, stir thoroughly for 10 min, then place it in an autoclave and pressurize to 0.5MPa, keep for 10 minutes, and then ultrasonic for 10 minutes, you can get the oil sto...

Embodiment 2

[0037] In this embodiment, a modified silicon dioxide nanometer solution is used. Include the following steps:

[0038] (1) Preparation of modified porous silica powder: mix ethanol, deionized water, and ammonia water in a ratio of 20:4:1, stir evenly, add 1vol.% nano-chain silica sol solution dropwise, and then add 0.6vol.% TEOS is used as a cross-linking agent, and then 0.6vol.% n-octyltriethoxysilane is added for surface modification. Finally, the beaker is sealed and stirred for 24 hours to obtain modified nano-SiO 2 solution. Move the solution into an oven at 120°C, dry it completely, and sieve it with a 200-mesh sieve to obtain the modified porous powder;

[0039] (2) Preparation of anti-icing coating: mix 10g of butyl acetate and 10g of fluorocarbon resin to obtain a resin solution, then add the modified porous powder prepared in step (1) to the resin solution, ultrasonically mix for 1min, and mix Add 3.33g polyisocyanate in the solution as curing agent, then stir to...

Embodiment 3

[0045] In this embodiment, a modified nano-silica nano-solution is used. Include the following steps:

[0046] (1) Preparation of modified porous silica powder: mix ethanol, deionized water, and ammonia water in a ratio of 20:4:1, add 1vol.% nano-chain silica sol solution dropwise after stirring evenly, and then Add 0.6vol.% TEOS as a cross-linking agent, then add 0.6vol.% n-octyltriethoxysilane for surface modification, and finally, seal the beaker and stir for 24 hours to obtain modified nano-SiO 2 solution. Move the solution into an oven at 120°C, dry it completely, and sieve it with a 200-mesh sieve to obtain the modified porous powder;

[0047] (2) Preparation of oil storage powder: Mix 1 g of modified porous powder prepared in step (1) with 8 g of simethicone oil with a viscosity of 500 CS, stir thoroughly for 10 min, then place it in an autoclave and pressurize to 0.5MPa, keep for 10 minutes, and then ultrasonic for 10 minutes, you can get the oil storage powder.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

A long-acting anti-icing coating and its preparation method and application belong to the technical field of coating preparation. The preparation process is as follows: first, modify the porous powder to be hydrophobic and lipophilic, and then carry out oil storage treatment, so that the silicone oil can fully enter the pores of the porous powder, and then diluent, resin, curing agent and modified porous powder according to a certain The anti-icing coating is obtained by mixing in proportion, which is drip-coated, scraped-coated or spin-coated. After the coating is cured, a long-lasting anti-icing coating can be obtained. The anti-icing coating prepared by the present invention has both anti-icing properties and durability and wear resistance, and has strong adhesion of the paint film. The method is easy to operate, low in cost, simple and effective, suitable for various types of base materials, and can be applied to the surface of aircraft , the inner wall of refrigeration equipment, and outdoor facilities in cold areas.

Description

technical field [0001] The invention belongs to the technical field of coating preparation, and in particular relates to a long-acting anti-icing coating and its preparation method and application. Background technique [0002] Based on the concept of bionics, people first observed the special micro-nano composite structure on the surface of the lotus leaf, thus proposing the concept of super-hydrophobic, and further prepared a super-hydrophobic coating. This extremely water-repelling surface can be used in anti-icing, self-cleaning, corrosion protection, enhanced heat transfer, and underwater drag reduction. However, the common disadvantage of this kind of interface is that due to the roughness of the surface, the surface will still freeze under the environment of humidity condensation; and the microstructure of the coating surface is easily damaged, the wear resistance is poor, and the ice layer will contact the surface. The rough structure forms a mechanical interlock, w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D127/12C09D175/04C09D7/62C09D7/65B05D7/24B05D7/00B05D7/14
CPCC09D127/12C09D175/04C09D7/62C09D7/65C09D7/70B05D7/24B05D7/00B05D7/14C08K2201/011B05D2203/35B05D2203/30C08L83/04C08K9/06C08K7/26
Inventor 张友法肖振余新泉
Owner SOUTHEAST UNIV