A tungsten-based feeding technology, which is applied in the special feeding field of Y-shaped fragile tungsten-based MIM, can solve the problems of self-injury protection of soldiers, and meet the requirements of environmental protection treatment process. control simple effects

Pending Publication Date: 2021-02-26
SHANDONG JINZHU MATERIALS TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

4. The projectile must be spherical, and the size must be within ±0.05mm
[0005] 2. The existing projectiles based on tungsten-nickel-iron have no problem in satisfying the penetration. However, after the projectile hits the reinforced concrete wall within 5 meters, the projectile will not be broken and will bounce back, so it cannot be used against one's own side. Warrior's Self-Injury Protection
But there is no such feed material suitable for metal powder injection molding production process on the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0036] The Y-type friable tungsten-based MIM special feeding material of the present invention includes Y-type friable tungsten-based materials and wax-based binders; in the Y-type friable tungsten-based materials, the tungsten powder is 85-90 parts, and the tungsten particles are 1-5 parts, nickel powder 0.5-3 parts, iron powder 0.5-3 parts, cobalt powder 0.1-2 parts, molybdenum powder 0.3-1 parts, alumina powder 1-6 parts, the wax base The binder contains 40-45 parts of Brazilian wax, 12-20 parts of paraffin wax, 20-35 parts of HDPE, 3-6 parts of PP, and 1-3 parts of SA.

specific Embodiment 2

[0038] The ratio of the Y-shaped fragile tungsten-based material and the wax-based binder in the present invention is 92 parts of tungsten powder, 2 parts of tungsten grain, 0.5 part of nickel powder, and 3 parts of iron powder. 1 part of cobalt powder, 0.5 parts of molybdenum powder, 1 part of alumina powder, the proportion of wax-based binder is 43 parts of Brazilian wax, 15 parts of paraffin wax, 35 parts of HDPE, 5 parts of PP, SA Makes 3 servings.

specific Embodiment 3

[0040] The ratio of the Y-shaped fragile tungsten-based material and the wax-based binder in the present invention is 86 parts of tungsten powder, 4 parts of tungsten particles, 1 part of nickel powder, and 2 parts of iron powder. , 1 part of cobalt powder, 1 part of molybdenum powder, 3 parts of alumina powder, the proportion of wax-based binder is 40 parts of Brazilian wax, 19 parts of paraffin wax, 35 parts of HDPE, 5 parts of PP, SA is 1 part.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Sizeaaaaaaaaaa
Sizeaaaaaaaaaa
Liquidity indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a Y-shaped fragile tungsten-based MIM special feed which comprises a Y-shaped fragile tungsten-based material and a wax-based binder. The Y-shaped fragile tungsten-based material comprises 85-90 parts of tungsten powder, 1-5 parts of tungsten particles, 0.5-3 parts of nickel powder, 0.5-3 parts of iron powder, 0.1-2 parts of cobalt powder, 0.3-1 part of molybdenum powder and 1-6 parts of alumina powder, and the wax-based binder comprises 40-45 parts of Brazilian wax, 12-20 parts of sliced paraffin, 20-35 parts of HDPE, 3-6 parts of PP and 1-3 parts of SA. The adopted H-shaped fragile tungsten-based MIM special feed overcomes the characteristic of soft texture of a lead material, ensures the penetrability, and avoids the constraint of international regulations; compared with a traditional tungsten-nickel-iron alloy, the adopted H-shaped fragile tungsten-based MIM special feed has fragility on the premise of keeping the hardness of the tungsten-based alloy; according to the wax-based binder system MIM special feed, few preparation processes are needed, process control is simple, and mass production can be easily realized; the fluidity is good, and injection molding is facilitated; and polluting tail gas is not generated, and the technological requirement for environment-friendly treatment can be easily met.

Description

technical field [0001] The invention relates to the technical field of new materials, in particular to Y-shaped fragile tungsten-based MIM special feeding material. Background technique [0002] The military put forward the following indicators for a new type of shotgun under research: 1. Self-injury protection for one’s own fighters, that is, when the bullet is fired at a muzzle velocity of 370-400 m / s for a distance of 5 meters, the projectile hits the reinforced concrete wall. Broken can not rebound. Two, the enemy must have lethality, that is, when the bullet is fired at a distance of 50 meters with a muzzle velocity of 370-400 m / s, the projectile will also penetrate a 25mm pine board. 3. The number of projectiles loaded in each bullet shall not be less than 20. 4. The projectile must be spherical, and the size must be within ±0.05mm. [0003] Defects and deficiencies of the prior art: [0004] 1. Now there are bullets that do not bounce back, and the material is lea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F1/00B22F3/22
CPCB22F3/225B22F1/108B22F1/107
Inventor 严远海李晶惠继恒
Owner SHANDONG JINZHU MATERIALS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products