A processing technology for degradable plastics

A processing technology and a technology for degrading plastics, applied in the field of plastic processing, can solve the problems of poor load-bearing capacity, easy aging, poor toughness, etc., and achieve the effects of long service life, non-perishable, and strong plasticity

Active Publication Date: 2022-05-24
JINHUA ENJOY & WONDERFUL INC
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Plastic is the most common and commonly used material in daily life. In order to ensure the sustainable development of the environment, it is necessary to reduce the amount of plastic used, especially in food, pharmaceutical packaging, and shopping malls. Plastic products are unavoidable. In order to reduce environmental impact Pollution, degradable plastics enter people's lives, but most degradable plastics are prepared from waste plant fibers, starch and other raw materials, and the above raw materials are not only in the process of use, but also have poor toughness, poor load-bearing capacity, and heat resistance Poor, easy to age, wet, moldy and damaged by other insects, inconvenient to use and store, therefore, the existing technology needs further improvement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A processing technology for degradable plastic, prepared by the following methods:

[0015] (1) Nano FeSO 4 Solution and Na 2 CO 3 Solution and Nano Si 3 N 4 Mixed, ultrasonically dispersed at 400 Hz for 20 min, dried at 40 °C, ground into powder, and then placed in a muffle furnace at 400 °C under N 2 sintered, and then added chitosan, CaCO 3 , EPDM copolymer, poly-β-hydroxybutyrate and bifenthrin are mixed and ground into powder, then sodium tripolyphosphate solution and guanidine hydrochloride solution are added, stirred evenly, and dried to obtain mixed powder;

[0016] (2) Mix the epoxy resin, glycerol, polylactic acid and the mixed powder in step (1), extrude it with a twin-screw extruder, and then put it into an injection molding machine for molding.

[0017] FeSO in the step (1) 4 Solution: Na 2 CO 3 Solution: Nano Si 3 N 4 : Chitosan: CaCO 3 : EPDM copolymer: poly-β-hydroxybutyrate: bifenthrin: sodium tripolyphosphate solution: guanidine hydrochlori...

Embodiment 2

[0023] A processing technology for degradable plastic, prepared by the following methods:

[0024] (1) Nano FeSO 4 Solution and Na 2 CO 3 Solution and Nano Si 3 N 4 Mixed, ultrasonically dispersed at 450Hz for 25min, dried at 45°C, ground into powder, and then placed in a muffle furnace at 450°C under N 2 sintered, and then added chitosan, CaCO 3 , EPDM copolymer, poly-β-hydroxybutyrate and bifenthrin are mixed and ground into powder, then sodium tripolyphosphate solution and guanidine hydrochloride solution are added, stirred evenly, and dried to obtain mixed powder;

[0025] (2) Mix the epoxy resin, glycerol, polylactic acid and the mixed powder in step (1), extrude it with a twin-screw extruder, and then put it into an injection molding machine for molding.

[0026] FeSO in the step (1) 4 Solution: Na 2 CO 3 Solution: Nano Si 3 N 4 : Chitosan: CaCO 3 : EPDM copolymer: poly-β-hydroxybutyrate: bifenthrin: sodium tripolyphosphate solution: guanidine hydrochloride s...

Embodiment 3

[0032] A processing technology for degradable plastic, prepared by the following methods:

[0033] (1) Nano FeSO 4 Solution and Na 2 CO 3 Solution and Nano Si 3 N 4 Mixed, ultrasonically dispersed at 500Hz for 30min, dried at 50°C, ground into powder, and then placed in a muffle furnace at 500°C under N 2 sintered, and then added chitosan, CaCO 3 , EPDM copolymer, poly-β-hydroxybutyrate and bifenthrin are mixed and ground into powder, then sodium tripolyphosphate solution and guanidine hydrochloride solution are added, stirred evenly, and dried to obtain mixed powder;

[0034] (2) Mix the epoxy resin, glycerol, polylactic acid and the mixed powder in step (1), extrude it with a twin-screw extruder, and then put it into an injection molding machine for molding.

[0035] FeSO in the step (1) 4 Solution: Na 2 CO 3 Solution: Nano Si 3 N 4 : Chitosan: CaCO 3 : EPDM copolymer: poly-β-hydroxybutyrate: bifenthrin: sodium tripolyphosphate solution: guanidine hydrochloride s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
concentrationaaaaaaaaaa
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of plastic processing, in particular to a processing technology for degradable plastics, which is prepared by the following method: (1) adding nano-FeSO 4 solution and Na 2 CO 3 solution and nano-Si 3 N 4 Mix, ultrasonically disperse at 400-500Hz for 20-30min, dry at 40-50°C, grind into powder, then place in a muffle furnace at 400-500°C, under N 2 sintering, followed by adding chitosan, CaCO 3 , EPDM copolymer, poly-β-hydroxybutyrate and bifenthrin are mixed and ground into powder, then sodium tripolyphosphate solution and guanidine hydrochloride solution are added, stirred evenly, and dried to obtain a mixed powder; ( 2) Mix epoxy resin, glycerin, polylactic acid and the mixed powder in step (1), extrude with a twin-screw extruder, and then enter into an injection molding machine for molding. The invention prepares degradable plastics which are not easy to mildew, age and be bitten by insects.

Description

technical field [0001] The invention relates to the technical field of plastic processing, in particular to a processing technology for degradable plastics. Background technique [0002] Plastic is the most common and commonly used material in daily life. In order to ensure the sustainable development of the environment, it is necessary to reduce the amount of plastic, especially food, medicine packaging, and the use of plastic products in shopping malls. Pollution, degradable plastics enter people's lives, but most of the degradable plastics are prepared from waste plant fibers, starch and other raw materials, and the above raw materials are not only in the process of use, they have poor toughness, poor load-bearing capacity, and heat resistance. Poor, easy to be aged, damp, mildewed and destroyed by other insects, inconvenient to use and store, therefore, the existing technology needs further improvement. SUMMARY OF THE INVENTION [0003] The purpose of the present inve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L5/08C08L23/16C08L67/04C08K13/02C08K3/30C08K3/26C08K3/34C08K5/101C08K3/32
CPCC08L5/08C08L2201/06C08K2003/324C08K2201/011C08K2003/3045C08K2003/265C08L2201/04C08L2205/03C08L23/16C08L67/04C08K13/02C08K3/30C08K3/26C08K3/34C08K5/101C08K3/32
Inventor 蔡胜张滕飞
Owner JINHUA ENJOY & WONDERFUL INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products