Nano negative ion fiber, preparation method thereof and application of nano negative ion fiber material in cosmetic brush
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A nano-anion and nano-zinc oxide technology, which is applied in the field of textile materials, can solve the problems of poor powder-holding power of artificial fibers, insufficient make-up application, unfavorable animal protection, etc., and achieve improved powder-holding ability and powder-releasing ability, flexibility Sexual enhancement, the effect of improving overall performance
Inactive Publication Date: 2021-04-13
东莞市杰瑟普化妆用具有限公司
View PDF7 Cites 4 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] At present, the bristles of cosmetic brushes are mainly made of man-made fibers and animal hairs. Because the animal hair has a complete scale structure on the surface, it has the advantages of soft hair, saturated powder, and does not irritate the skin. Poor, uneven powder sticking, insufficient makeup application, therefore, animal hair brushes are more popular with consumers, while using animal hair is not conducive to the protection of animals
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0047] A nano anion fiber makeup brush bristle, comprising the following raw materials: 60g of epoxy resin, 25g of graphene oxide, 13g of nano silver, 13g of nano zinc oxide, 6g of opal, 12g of quartz powder, 5g of acrylic acid, 1g of phenylpropanyl peroxide, Additive 10g, antibacterial agent 8g, dispersant 3g.
[0048] The additives are 2 g of Angelica dahurica powder, 3 g of Tribulus terrestris powder, and 5 g of pearl powder; the antibacterial agent is 3 g of chitin, 1 g of hinoki alcohol, and 4 g of zinc oxide; the dispersant is sodium pyrophosphate.
[0049]A kind of nano anion fiber makeup brush bristle, its preparation method comprises the following steps: add 74.4g water in nano silver, nano zinc oxide, opal, additive, antibacterial agent, stir with 120 ℃ evenly, use acetic acid to adjust the pH value Adjust to 7 to obtain a mixed solution; put epoxy resin, graphene oxide, acrylic acid, phenylpropanyl peroxide, and dispersant into a stirrer and stir evenly at a tempera...
Embodiment 2
[0051] Differences from Example 1: 50g of epoxy resin, 30g of graphene oxide, 10g of nano-silver, 15g of nano-zinc oxide, 1g of opal, 15g of quartz powder, 2g of acrylic acid, 2g of phenylpropanyl peroxide, 5g of additives, 10g of antibacterial agent , Dispersant 2g.
Embodiment 3
[0053] Differences from Example 1: 70g of epoxy resin, 20g of graphene oxide, 15g of nano-silver, 10g of nano-zinc oxide, 10g of opal, 10g of quartz powder, 15g of acrylic acid, 0.5g of benzoyl peroxide, 15g of additives, antibacterial agent 5g, dispersant 5g.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to the field of textile materials, and particularly discloses a nano negative ion fiber material, a preparation method thereof and application of the nano negative ion fiber material in a cosmetic brush. The nano negative ion fiber material is prepared from 50-70 parts of epoxy resin, 20-30 parts of graphene oxide, 10-15 parts of nano silver, 10-15 parts of nano zinc oxide, 1-10 parts of opal, 10-15 parts of quartz powder, 2-15 parts of acrylic acid, 0.5-2 parts of benzoyl peroxide, 5-15 parts of an additive, 5-10 parts of an antibacterial agent and 2-5 parts of a dispersing agent. The preparation method comprises the following steps that the epoxy resin, the graphene oxide, the acrylic acid, the benzoyl peroxide and the dispersing agent are uniformly mixed to obtain a mixture, water is added into the nano-silver, the nano-zinc oxide, the opal, the quartz powder, the additive and the antibacterial agent to obtain a mixed solution, the mixture is mixed with the mixed solution, drying and melting are carried out to obtain the nano negative ion fiber material. The nanometer negative ion fiber material can be used for preparing bristles of the cosmetic brush and has the advantages of being soft, high in powder grabbing force, capable of whitening skin and the like.
Description
technical field [0001] The application relates to the field of textile materials, more specifically, it relates to a nano anion fiber. Background technique [0002] Nano-anion fiber is a fiber material that releases negative ions. Negative ions not only have the functions of purifying the air, sterilizing, and deodorizing, but also have a health care effect on the human body. They can eliminate free radicals. Excessive free radicals are the cause of human diseases. Aging, the killer of death. Therefore, the nano-anion fiber material is very popular in the beauty field, especially the cosmetic brush used in the beauty field, which directly contacts with people's skin, and its quality and skin care effect are just crucial for users. [0003] At present, the bristles of cosmetic brushes are mainly made of man-made fibers and animal hairs. Because the animal hair has a complete scale structure on the surface, it has the advantages of soft hair, saturated powder, and does not ir...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more