A kind of finishing light imitation brick material and the processing method of imitation brick

A processing method and imitation brick technology, applied in the field of imitation bricks, can solve the problems of short service life, high brittleness, low strength, etc., and achieve the effect of reducing quality

Active Publication Date: 2022-03-08
CHENGDU FIRST NEW MATERIAL CO LTD +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, paint is commonly used to make imitation bricks to decorate the wall surface. More light imitation brick materials are made of gypsum as the base material and then mixed with additives, or perlite as the base material mixed with adhesives. Or mix cement with fly ash as the base material; although the lightweight bricks made of the above materials play a certain decorative role in different occasions, the quality of the imitation bricks is heavy, brittle, and low in strength. Short lifespan and poor water resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of finishing light imitation brick material and the processing method of imitation brick
  • A kind of finishing light imitation brick material and the processing method of imitation brick
  • A kind of finishing light imitation brick material and the processing method of imitation brick

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A kind of processing method of imitation brick, comprises the steps:

[0030] Step 1: Prepare as figure 1 A kind of imitation brick processing equipment shown, comprises support plate 1, support frame 2, mold frame 3 and pressing unit; figure 2 As shown, the support frame 2 includes a column 4 and a top plate 5, the upper end of the column 4 and the top plate 5 are fixedly connected by screws; It is fixedly connected with the support block 7 by screws.

[0031] Such as image 3 As shown, the mold frame 3 is provided with a "T"-shaped cavity-forming unit, the cavity-forming unit includes a cavity-forming block 8 and two connecting blocks 9, and the cavity-forming block 8 is connected to the mold frame 3 through the connecting block 9, namely One end of the connection block 9 is fixedly connected with the side wall of the mold frame 3 by screws, and the other end of the connection block 9 is fixedly connected with the cavity forming block 8 by screws, and the width of...

Embodiment 2

[0039] On the basis of Example 1, as figure 1 As shown, the support block 7 is fixedly connected with a support bar 17 by screws, the support bar 17 is arranged obliquely, and the upper end of the support bar 17 is fixedly connected with the column 4 by screws. A rubber pad is bonded to the push-pull rod 15 , and the rubber pad is conducive to increasing the frictional force between the push-pull rod 15 and the hole 14 . The support plate 1 is fixed with a material retaining plate by screws, and the material retaining plate is positioned between the support bar 17 and the mold frame 3 to prevent the imitation brick material from entering the chute 6 .

Embodiment 3

[0041] The difference from Example 1 is that a light-weight imitation brick material for painting includes the following raw materials: 50g of water, 1g of cellulose, 0.5g of MZ bentonite, 0.5g of pH regulator, 3g of wetting and dispersing agent, ethylene glycol 8g, defoamer 0.5g, alcohol ester twelve 3g, preservative 1g, silica sol 5g, styrene-acrylic emulsion 110g, heavy calcium powder 110g, polyvinyl alcohol 0.5g, expanded perlite 20g, titanium dioxide 10g, quartz sand 530g , Thickener 1g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of imitation bricks, in particular to a light-weight imitation brick material for coating, which comprises the following raw materials: water, cellulose, MZ bentonite, pH regulator, wetting and dispersing agent, ethylene glycol, defoaming agent, alcohol ester ten 2. Preservatives, silica sol, styrene-acrylic emulsion, heavy calcium powder, polyvinyl alcohol, expanded perlite, titanium dioxide, quartz sand, thickener; a processing method for imitating bricks, including the following steps: Step 1: Preparation An imitation brick processing equipment; Step 2: forming lightweight imitation bricks; Step 3: pushing the formed lightweight imitation bricks to move; Step 4: separating the mold frame from the light imitation bricks; Step 5: pulling the push-pull rod to drive the pressing block, The supporting frame and the mold frame move in opposite directions. When the push-pull rod is separated from the connection block, the mold frame moves downward to contact the support plate, and the mixed imitation brick material is loaded into the mold frame. When the technical proposal is adopted, it is convenient to process light-weight imitation bricks and to demould.

Description

technical field [0001] The invention relates to the field of imitation bricks, in particular to a coated lightweight imitation brick material and a processing method for the imitation bricks. Background technique [0002] At present, paint is commonly used to make imitation bricks to decorate the wall surface. More light imitation brick materials are made of gypsum as the base material and then mixed with additives, or perlite as the base material mixed with adhesives. Or mix cement with fly ash as the base material; although the lightweight bricks made of the above materials play a certain decorative role in different occasions, the quality of the imitation bricks is heavy, brittle, and low in strength. Short life and poor water resistance. Contents of the invention [0003] The object of the present invention is to provide a lightweight imitation brick material with high strength, excellent water resistance and light weight. [0004] In order to achieve the above-menti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/26B28B3/04B28B1/29B28B7/00B28B7/18B28B13/06B28B17/00
Inventor 刘东华何剑南青林高如玉李秋金吴学通郅亚楠何滔蒋滔刘健卢远中
Owner CHENGDU FIRST NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com