Self-repairing rubber material and preparation method thereof
A rubber material and self-healing technology, applied in the field of rubber materials, can solve the problems of unguaranteed temperature resistance, toughness and tensile resistance, inability to achieve multiple self-healing of rubber, and shortening the service life of rubber materials, etc. Good comprehensive performance and performance stability, good self-healing effect, and improved aging resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0033]Example 1
[0034]A self-repairing rubber material, characterized in that the components of the weight are prepared from each component: 40 parts of the epoxidation of natural rubber, 30 parts of methylvinyl silicone rubber, diphenyl ketone-4,4'- 5 parts of diethylene-endonamin polyurethane, 8 parts of hyperbranched secondary thiol compound, 2 parts of super branched polyamide, 2 pig fibers, 15 inorganic fillers, 2 coupling agents, 1 vulcanizer 1 part of the photoinitiator.
[0035]The photoinitiator is diphenyl ketone; the vulcanizing agent is a disulfurized tetramethyl autumn, dibutyl dithiocarbamate is mixed by mass than 3: 1; the coupling agent is selected Since the silicone coupling agent KH570.
[0036]The inorganic filler is white carbon black; the inorganic filler has a particle diameter of 800 mesh; the pig fibers are waste pig fibers and a length of 3 mm.
[0037]The preparation method of the diphenyl ketone-4,4'-dimethylene / end amino polyurethane polycondensate includes the s...
Example Embodiment
[0041]Example 2
[0042]A self-repairing rubber material, characterized in that it is prepared from each component of weight: 43 parts of epoxidation, 32 parts of methylvinyl silicone rubber, diphenone-4,4'- 6 parts of dimethic acid / end amino polyurethane polycondensate, 9 parts of super branched secondary thiol compound, over-branched polyamide amine, 2.5 parts of pig hair fiber, 17 inorganic fillers, 2.3 parts of coupling agent, 1.5 vulcanizers 1.2 parts of the photoinitiator.
[0043]The photoinitiator is a moistthal ether; the vulcanizing agent is a disulfurized tetramethyl Qalaum, and the disulfurized zinc is mixed in mass than 3: 1.2; the coupling agent is a silane coupling. United agent KH560; the inorganic filler is lignin; the inorganic filler has a particle diameter of 900 mesh; the pig fibers are waste pig fibers and a length of 4 mm.
[0044]The preparation method of the diphenyl ketone-4,4'-dimethylene / end amino polyurethane polycondensate includes the step of: adding dibenz...
Example Embodiment
[0048]Example 3
[0049]A self-repairing rubber material, characterized in that it is prepared from the components of weight: 45 parts of epoxidation of natural rubber, 35 parts of methylvinyl silicone rubber, diphenyl ketone-4,4'- Dikhalic acid / end amino polyurethane polycondensate, 10 parts of super branched secondary thiol compound, 3 parts of super branched polyamide, 3.5 parts of pig hair fiber, 20 inorganic fillers, 2.5 parts of coupling agent, 2 vulcanizers 1.5 parts of the photoinitiator.
[0050]The photoinitiator is a homomeric ether; the vulcanizing agent is a disulfurized tetramethyl Qalaum, and the disulfurized zinc is mixed in mass than 3: 1.5; the coupling agent is a silane Coupling agent KH550; the inorganic filler is carbon black; the inorganic filler has a particle diameter of 1000 mesh; the porcine fiber is a waste pig fiber and a length of 5 mm.
[0051]The preparation method of the diphenyl ketone-4,4'-dimethylene / end amino polyurethane polycondensate includes the st...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Length | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap