Preparation method of high-performance heat-conducting plastic composite material
A technology of thermally conductive plastics and composite materials, used in heat exchange materials, chemical instruments and methods, etc., can solve the problems of narrow application area and poor thermal conductivity, achieve large heat source and power consumption, improve thermal conductivity and good fluidity. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0024] Add 48 parts of modified phenolic resin, 5 parts of urotropine, and 30 parts of wood flour fiber into a high-speed mixer, and mix them with high-speed stirring to obtain E mixture; add the coupling agent to anhydrous ethanol solvent to prepare the coupling agent solution, add 3 parts of silicon carbide and 1.5 parts of graphite to the coupling agent solution, stir evenly, filter with suction, and dry to obtain F mixture; mix E mixture, F mixture, 8 parts of magnesium oxide, 1.5 parts of stearic acid, talc 1 part of powder, 0.5 parts of plasticizer, 1.5 parts of coloring matter, mixed uniformly according to a certain mass ratio, masticated under certain conditions through a twin-screw machine, extruded and granulated, and can be molded at 180 ° C. Name it PF-NS321.
Embodiment 2
[0026] Add 40 parts of modified phenolic resin, 5 parts of urotropine, and 30 parts of wood flour fiber into a high-speed mixer, and mix them with high-speed stirring to obtain E mixture; add the coupling agent to anhydrous ethanol solvent to prepare the coupling agent solution, add 3 parts of silicon carbide and 1 part of graphite to the coupling agent solution, stir evenly, filter with suction, and dry to obtain F mixture; mix E mixture, F mixture, 8 parts of magnesium oxide, 8 parts of calcium oxide, stearin 2 parts of acid, 1 part of talcum powder, 0.5 parts of plasticizer, 1.5 parts of coloring material, mixed uniformly according to a certain mass ratio, plasticized under certain conditions through a twin-screw machine, extruded and granulated, and can be granulated at 185 ° C The lower molded, named it PF-NS322.
[0027] Table 1 is a performance comparison table of radiators made of different materials. Table 2 is a comparison table of the technical parameters of the hi...
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap