A technology of high temperature resistance and silicone, which is applied in the field of high temperature resistant silicone sleeve and its preparation, and can solve the problems affecting the normal performance of silicone tube, elastic fatigue, and inability to withstand high temperature for a long time

Active Publication Date: 2021-05-18
河北兹尔新材料科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Under certain conditions, there is a high requirement for the high temperature resistance of the silicone tube. However, in the prior art, the ordinary high temperature resistant sili

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature-resistant silica gel sleeve and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] In Example 1, a high-temperature-resistant silicone sleeve adopts the following raw materials in proportion by mass: 100 parts of silicone rubber, 10 parts of thermoplastic resin, 1.5 parts of vulcanizing agent, 8 parts of phenyl silicone oil, 6 parts of titanium oxide, plasticized 3 parts of anti-aging agent, 1 part of anti-aging agent, 10 parts of propylene oxide glycerol polyether, 32 parts of high alumina clinker, 0.5 parts of aluminate coupling agent, 2 parts of silane coupling agent, 15 parts of magnesium stearate and polyformaldehyde 12 parts of triethoxysilane.

[0026] Further, the antiaging agent is a mixture of one or more of antiaging agent RD, antiaging agent 4010 or antiaging agent MB.

[0027] Further, the plasticizer is an alkylsulfonic acid phenyl ester compound.

[0028] Further, the silane coupling agent is one of silane coupling agent KH-550, silane coupling agent KH-558 or silane coupling agent KH-560, and the aluminate coupling agent is aluminate ...

Embodiment 2

[0033] In Example 2, a high-temperature-resistant silicone sleeve adopts the following raw materials in proportion by mass: 120 parts of silicone rubber, 15 parts of thermoplastic resin, 6 parts of vulcanizing agent, 16 parts of phenyl silicone oil, 12 parts of titanium oxide, plasticized 8 parts of anti-aging agent, 5 parts of anti-aging agent, 25 parts of propylene oxide glycerol polyether, 42 parts of high alumina clinker, 2 parts of aluminate coupling agent, 5 parts of silane coupling agent, 22 parts of magnesium stearate and polyformaldehyde 22 parts of triethoxysilane.

[0034] Further, the antiaging agent is a mixture of one or more of antiaging agent RD, antiaging agent 4010 or antiaging agent MB.

[0035] Further, the plasticizer is an alkylsulfonic acid phenyl ester compound.

[0036] Further, the silane coupling agent is one of silane coupling agent KH-550, silane coupling agent KH-558 or silane coupling agent KH-560, and the aluminate coupling agent is aluminate c...

Embodiment 3

[0041] In Example 3, a high-temperature-resistant silicone sleeve adopts the following raw materials in proportion by mass: 110 parts of silicone rubber, 12 parts of thermoplastic resin, 8 parts of reinforcing agent, 4 parts of vulcanizing agent, 12 parts of phenyl silicone oil, oxidized 9 parts of titanium, 6 parts of plasticizer, 4 parts of anti-aging agent, 18 parts of propylene oxide glycerol polyether, 36 parts of high alumina clinker, 1 part of aluminate coupling agent, 3 parts of silane coupling agent, stearic acid 18 parts magnesium and 18 parts polymethyltriethoxysilane.

[0042] Further, the antiaging agent is a mixture of one or more of antiaging agent RD, antiaging agent 4010 or antiaging agent MB.

[0043] Further, the plasticizer is an alkylsulfonic acid phenyl ester compound.

[0044] Further, the silane coupling agent is one of silane coupling agent KH-550, silane coupling agent KH-558 or silane coupling agent KH-560, and the aluminate coupling agent is alumin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of high-temperature-resistant silica gel sleeves, in particular to a high-temperature-resistant silica gel sleeve. The high-strength silicone rubber is prepared from the following raw materials in parts by mass: 100-120 parts of silicone rubber, 10-15 parts of thermoplastic resin, 1.5-6 parts of a vulcanizing agent, 8-16 parts of phenyl silicone oil, 6-12 parts of titanium oxide, 3-8 parts of a plasticizer, 1-5 parts of an anti-aging agent, 10-25 parts of epoxypropane glyceryl polyether, 32-42 parts of high-aluminum clinker, 0.5-2 parts of an aluminate coupling agent, 2-5 parts of a silane coupling agent, 15-22 parts of magnesium stearate and 12-22 parts of polymethyl triethoxy silane. The high-temperature-resistant silica gel sleeve provided by the invention is simple in preparation method, low in raw material price and low in production cost, and the prepared silica gel sleeve is excellent in heat resistance and ageing resistance and can be suitable for high-temperature-resistant places.

Description

technical field [0001] The invention relates to the technical field of high-temperature-resistant silicone sleeves, in particular to a high-temperature-resistant silicone sleeve and a preparation method thereof. Background technique [0002] Silicone tube is the circulation and coating carrier of liquid, gas and other materials. It is widely used in modern industry, national defense industry and daily necessities. Silicone tube is added from raw silicone rubber to a double-roller rubber mixer or a closed kneader. Gradually add white carbon black and other additives, and after repeated refining, the product is made by extrusion. [0003] Common silicone tubes include medical silicone tubes, food grade silicone tubes, industrial silicone tubes, special-shaped silicone tubes, silicone tube accessories, etc. Under certain conditions, there is a high requirement for the high temperature resistance of the silicone tube. However, in the prior art, the ordinary high temperature res...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L83/04C08L71/02C08K13/06C08K9/06C08K5/098C08K3/22
CPCC08L83/04C08L2201/08C08L2203/18C08K2003/2241C08L2205/025C08L2205/035C08K2003/2227C08L71/02C08K13/06C08K9/06C08K5/098C08K3/22
Inventor 杨国安杨亚龙
Owner 河北兹尔新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap