Preparation method of light energy self-disinfection formaldehyde-free and non-ironing fabric

A formaldehyde and fabric technology, applied in plant fibers, fiber processing, textiles and papermaking, etc., can solve the problems of inability to give fabrics no-iron antibacterial, reduce formaldehyde emission in non-iron finishing processing, etc., to avoid the risk of formaldehyde release, improve Antibacterial properties and easy ironing, high processing efficiency

Pending Publication Date: 2021-06-18
LUTAI TEXTILE
View PDF9 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The imidazoline derivative used in this patent is a conventional formaldehyde scavenger, and its function is to reduce the amount of formaldehyde released in the non-ironing finishing process, which cannot give the fabric non-ironing and antibacterial effects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of light energy self-disinfection formaldehyde-free and non-ironing fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The fabric is made of pure cotton woven fabric in the warp and weft direction, the yarn is pure cotton 80s ply yarn, the weave is 1 / 1 plain weave, the warp density is 160 threads / inch, and the weft density is 72 threads / inch. The weight of the fabric is 130g / m 2 .

[0033] (1) Formaldehyde-free non-iron finishing agent finishing: the fabric adopts uniform padding on the stenter setting machine to pad imidazoline derivatives formaldehyde-free non-ironing resin WFF (Archroma Chemicals) and corresponding catalysts, formaldehyde-free non-ironing resin The dosage is 100g / L, the catalyst is a mixed aqueous solution of citric acid and magnesium chloride (the mass ratio of citric acid and magnesium chloride is 1:1, and the total mass of citric acid and magnesium chloride is 60% of the catalyst quality), and the dosage of the catalyst is 20g / L , the surplus rate of the fabric is 50%, the drying temperature of the oven is 110°C, and the speed of the stenter setting machine is 70...

Embodiment 2

[0038] The fabric is made of cotton / linen woven fabric, the warp yarn is pure cotton 30s single yarn, the weft yarn is 21s linen yarn, the weave is 2 / 2 punched, the warp density is 130 threads / inch, and the weft density is 100 threads / inch, the weight of the fabric is 220g / m 2 .

[0039] (1) Formaldehyde-free non-iron finishing agent finishing: the fabric adopts uniform padding on the stenter setting machine to pad imidazoline derivatives formaldehyde-free non-ironing resin WFF (Archroma Chemicals) and corresponding catalysts, formaldehyde-free non-ironing resin The consumption is 260g / L, and the catalyst is a mixed aqueous solution of maleic acid and magnesium chloride (the mass ratio of maleic acid and magnesium chloride is 1:3, and the total mass of maleic acid and magnesium chloride is 50% of the catalyst quality), and the consumption of the catalyst is 52g / L, the excess rate of the fabric after padding is 85%, the oven temperature is 130°C, and the speed of the stenter s...

Embodiment 3

[0044] The fabric is made of pure cotton weft-knitted fabric, the yarn is pure cotton 60s strands, the fabric structure is jersey, and the weight of the fabric is 175g / m 2 .

[0045] (1) Formaldehyde-free non-iron finishing agent finishing: the fabric adopts uniform padding on the stenter setting machine to pad imidazoline derivatives formaldehyde-free non-ironing resin WFF (Archroma Chemicals) and corresponding catalysts, formaldehyde-free non-ironing resin Consumption is 160g / L, and catalyzer is the mixed aqueous solution of citric acid, maleic acid and magnesium chloride (the mass ratio of citric acid, maleic acid and magnesium chloride is 1:1:2, and the total mass of citric acid, maleic acid and magnesium chloride is 70% of catalyst mass), the consumption of catalyst is 32g / L, the excess rate of fabric after padding is 60%, oven temperature is 120 ℃, and the speed of tenter setting machine is 30m / min;

[0046] (2) Light energy self-disinfection auxiliary agent treatment: ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of textiles, and particularly relates to a preparation method of a light energy self-disinfection formaldehyde-free and non-ironing fabric. The fabric is firstly padded with a formaldehyde-free and non-ironing finishing agent, then padded with a light energy self-disinfection auxiliary agent and baked to obtain the light energy self-disinfection formaldehyde-free and non-ironing fabric, wherein the formaldehyde-free and non-ironing finishing agent comprises formaldehyde-free and non-ironing resin and a catalyst, and the light energy self-disinfection auxiliary agent is an amino acid zinc phthalocyanine compound. Aiming at the problems that a traditional antibacterial and non-ironing fabric is poor in antibacterial property, not washable, high in formaldehyde content and the like in the use process, the functional fabric with the formaldehyde-free and non-ironing property and the antibacterial property is prepared, the antibacterial property and non-ironing property of the fabric are improved, and meanwhile, the risk of formaldehyde release of the conventional non-ironing fabric is avoided.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a method for preparing light-energy self-sterilizing formaldehyde-free non-ironing fabrics. Background technique [0002] Cotton fabrics are hygroscopic, breathable, and comfortable to wear, and are deeply loved by people. However, cotton fabrics have a large specific surface area and strong moisture absorption capacity, and are easily attached by microorganisms. The growth and reproduction of microorganisms on textiles not only affects the cleanliness of textiles, but also the wearability. Comfort, but also because of the reproduction of microorganisms, the cotton fiber will be discolored or damaged, produce a special smell, and even cause the spread of diseases, affecting the health of users. In order to reduce the invasion of bacteria on the human body, it is very necessary to carry out waterproof and antibacterial finishing on cotton fabrics. [0003] Common ant...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/37D06M13/503D06M101/06
CPCD06M15/37D06M13/503D06M16/00D06M2101/06
Inventor 张凯刘德延王昌钊杜立新解倩倩孙丽洁张高倩刘德铭邵淑华
Owner LUTAI TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com