Alloy powder and repair method for laser cladding repair of hydraulic cylinder in mine hydraulic column

A hydraulic column and laser cladding technology, which is applied in the coating process and coating of metal materials, can solve the problems of surface pitting, short corrosion life, pitting corrosion of alloy coatings, etc., to achieve grain refinement and increase production The effect of temperature and toughness increase

Active Publication Date: 2022-04-15
XIAN BESAME LASER TECH CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to solve the technical problem that surface pitting often occurs in the overlapping area of ​​the cladding layer when the existing hydraulic cylinder for mining is repaired by laser cladding, and to provide a hydraulic cylinder for mining. Laser cladding repair method for column and middle cylinder and alloy powder for cladding
[0009] The invention is aimed at the problem that the alloy coating that occurs when the laser cladding repairs the mining hydraulic cylinder is prone to pitting and causes short corrosion life, and proposes a mining hydraulic column with high pitting resistance and long service life Alloy powder and repair method for laser cladding repair of middle cylinder

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Alloy powder and repair method for laser cladding repair of hydraulic cylinder in mine hydraulic column

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0076]An alloy powder for laser cladding and repairing the middle cylinder of a mining hydraulic column, including the powder of the following components:

[0077] Cr: 16.6wt%;

[0078] Ni: 1.75wt%;

[0079] Co: 1.75wt%;

[0080] Mo: 1.0wt%;

[0081] Mn: 0.2wt%;

[0082] Nb: 0.15wt%;

[0083] C: 0.10wt%;

[0084] N: 0.10wt%;

[0085] Ce: 0.045wt%;

[0086] B: 0.76wt%;

[0087] Si: 1.0wt%;

[0088] Fe is the balance.

[0089] The above-mentioned alloy powder for laser cladding and repairing the middle cylinder of mining hydraulic column is prepared by pre-mixing and then using nitrogen atomization powder making method. The particle size distribution of the prepared powder is between 120 and 260 mesh. figure 1 It is the scanning electron microscope picture of the alloy powder. It can be seen that the sphericity is good in the picture, which can be used for laser cladding repair.

[0090] A laser cladding repair method for the middle cylinder of a mine hydraulic column...

Embodiment 2

[0096] An alloy powder for laser cladding and repairing the middle cylinder of a mining hydraulic column, including the powder of the following components:

[0097] Cr: 15.6wt%;

[0098] Ni: 1.65wt%;

[0099] Co: 1.65wt%;

[0100] Mo: 0.9wt%;

[0101] Mn: 0.3wt%;

[0102] Nb: 0.12wt%;

[0103] C: 0.09wt%;

[0104] N: 0.11wt%;

[0105] Ce: 0.035wt%;

[0106] B: 0.68wt%;

[0107] Si: 0.9wt%;

[0108] Fe is the balance.

[0109] The above-mentioned alloy powder for laser cladding and repairing the middle cylinder of mining hydraulic column is prepared by pre-mixing and then using nitrogen atomization powder making method, and the particle size distribution of the prepared powder is between 120 and 260 mesh.

[0110] A laser cladding repair method for the middle cylinder of a mine hydraulic column, based on the alloy powder for laser cladding repair of the mine hydraulic column middle cylinder, comprising the following steps:

[0111] 1) Remove the oil and impurities on...

Embodiment 3

[0116] An alloy powder for laser cladding and repairing the middle cylinder of a mining hydraulic column, including the powder of the following components:

[0117] Cr: 15.0wt%;

[0118] Ni: 1.5wt%;

[0119] Co: 1.5wt%;

[0120] Mo: 0.8wt%;

[0121] Mn: 0.0wt%;

[0122] Nb: 0.1wt%;

[0123] C: 0.07wt%;

[0124] N: 0.06wt%;

[0125] Ce: 0.03wt%;

[0126] B: 0.6wt%;

[0127] Si: 0.8wt%;

[0128] Fe is the balance.

[0129] The above-mentioned alloy powder for laser cladding and repairing the middle cylinder of mining hydraulic column is prepared by pre-mixing and then using nitrogen atomization powder making method, and the particle size distribution of the prepared powder is between 120 and 260 mesh.

[0130] A laser cladding repair method for the middle cylinder of a mine hydraulic column, based on the alloy powder for laser cladding repair of the mine hydraulic column middle cylinder, comprising the following steps:

[0131] 1) Remove the oil and impurities on the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to laser processing and repairing, in particular to an alloy powder and a repairing method for laser cladding and repairing a middle cylinder of a mine hydraulic column. The invention is aimed at the problem that the alloy coating that occurs when the laser cladding repairs the mining hydraulic cylinder is prone to pitting and causes short corrosion life, and proposes a mining hydraulic column with high pitting resistance and long service life Alloy powder and repair method for laser cladding repair of middle cylinder. Alloy powder includes: Cr: 15.0~17.0wt%; Ni: 1.5~2.0wt%; Co: 1.5~2.0wt%; Mo: 0.8~1.2wt%; Mn: 0.0~0.4wt%; Nb: 0.1~0.2wt% %; C: 0.07-0.14wt%; N: 0.06-0.12wt%; Ce: 0.03-0.06wt%; B: 0.6-1.0wt%; Si: 0.8-1.2wt%; Fe is the balance. Among them, the addition of Co element can not only expand the austenite area, but also increase the toughness and wear resistance, further improve the pitting corrosion resistance of the cladding layer, and increase the service life.

Description

technical field [0001] The invention relates to an alloy powder for laser processing and repair and a repair method, in particular to an alloy powder and a repair method for laser cladding and repair of a middle cylinder of a mine hydraulic column. Background technique [0002] The traditional middle cylinder of mining hydraulic column is often repaired by electroplating hard chrome. This repair process mainly has the following three deficiencies: [0003] First, it pollutes the environment seriously and runs counter to the direction of social development; [0004] Second, the bonding force between the chrome plating layer and the base material is weak, and it is easy to "peel and pack"; [0005] Third, the porosity of the chromium plating layer cannot be effectively controlled, resulting in a decrease in corrosion resistance. [0006] With the development of high-power semiconductor lasers and the maturity of their technology, the laser cladding technology with its outsta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/44C22C38/48C22C38/52C22C38/54C23C24/10
CPCC22C38/52C22C38/44C22C38/04C22C38/02C22C38/48C22C38/54C22C38/001C22C38/005C23C24/106
Inventor 王晓飚曹伟业
Owner XIAN BESAME LASER TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com