A method for reducing the harmfulness of aluminum nitride inclusions in high aluminum steel

A high-aluminum steel and aluminum nitride technology is applied in the field of reducing the hazard of aluminum nitride inclusions in high-aluminum steel, which can solve the problems of increasing vacuum smelting equipment and high cost, and achieves difficult micro-cracks, reduced hazard, and easy shape. Effect

Active Publication Date: 2022-03-15
WUHAN UNIV OF SCI & TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method needs to increase the vacuum smelting equipment, the cost is high, and the addition of nitrogen in the molten steel cannot be avoided during the casting process after the smelting is completed. This method is difficult to fundamentally solve the problems caused by aluminum nitride inclusions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for reducing the harmfulness of aluminum nitride inclusions in high aluminum steel
  • A method for reducing the harmfulness of aluminum nitride inclusions in high aluminum steel
  • A method for reducing the harmfulness of aluminum nitride inclusions in high aluminum steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] This embodiment provides a method for reducing the harmfulness of aluminum nitride inclusions in high aluminum steel, comprising the following steps:

[0040] S1. Prepare 35kg of industrial pure iron, 360g of graphite rod, 10.64kg of electrolytic manganese, 5.3kg of aluminum pellets and 10g of sulfur iron as raw materials for preparing high-alumina steel; wherein, the manganese content is about 20.74%, and the sulfur content is about 0.01%. .

[0041] S2. Put industrial pure iron and graphite rods into a prefabricated magnesia crucible, and put electrolytic manganese, aluminum particles and iron sulfur into a feed bin. Vacuumize the induction furnace to 6Pa, and then raise the temperature to 1600°C to melt the industrial pure iron and graphite rods, then pass argon into the induction furnace, and add electrolytic manganese through the silo. After the electrolytic manganese is completely melted, then Aluminum pellets are added through the silo. After refining for 10 mi...

Embodiment 2～3 and comparative example 1～2

[0044] Embodiments 2-3 and Comparative Examples 1-2 respectively provide a method for reducing the harmfulness of aluminum nitride inclusions in high-aluminum steel. Compared with Example 1, the difference is that the added amount of sulfur iron is changed, The rest of the steps are the same as those in Embodiment 1, and will not be repeated here. The corresponding iron sulfur addition amount and the sulfur content in the high-aluminum steel in each embodiment and comparative example are shown in Table 1 respectively.

[0045] Table 1 Examples 2-3 and comparative examples 1-2 correspond to the amount of iron sulfur added and the sulfur content in high-alumina steel

[0046] Example / Comparative example Amount of iron sulfur added (g) Sulfur content in high aluminum steel (%) Example 2 20 0.02 Example 3 30 0.03 Comparative example 1 3 0.003 Comparative example 2 40 0.04

[0047] In order to test the reduction degree of the harmfulne...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for reducing the harmfulness of aluminum nitride inclusions in high aluminum steel. In this method, industrial pure iron and graphite rods are pre-melted, and then manganese-containing raw materials and aluminum-containing raw materials are sequentially added for smelting; after the manganese-containing raw materials and aluminum-containing raw materials are completely melted, a predetermined amount of sulfur-containing raw materials is added , to obtain molten steel; then cast the molten steel into the mold to obtain high-alumina steel with low harmfulness of aluminum nitride inclusions. Through the above-mentioned method, the present invention can control the sulfur content in the high-aluminum steel composition and utilize the high deformation ability of the formed manganese sulfide inclusions to realize the full wrapping of the brittle aluminum nitride inclusions by the plastic manganese sulfide inclusions, Thereby reducing the harmfulness of aluminum nitride inclusions in high aluminum steel. Moreover, the method provided by the invention is simple in operation and wide in scope of application, can effectively reduce the amount of pure aluminum nitride inclusions in high-aluminum steel, and improve its hardness and tensile strength, and has high practical application value.

Description

technical field [0001] The invention relates to the technical field of iron and steel metallurgy, in particular to a method for reducing the harmfulness of aluminum nitride inclusions in high-aluminum steel. Background technique [0002] High aluminum steel generally has high surface hardness, wear resistance, excellent plasticity, toughness and other mechanical properties, and its aluminum content is usually more than 1%, including high manganese high aluminum low density steel, TRIP steel, TWIP steel, electrical steel , Fe-Cr-Al stainless steel, etc. In recent years, in order to meet the lightweight requirements in the field of automobile manufacturing, high-manganese and high-aluminum steel with high strength and plasticity and low density has become a popular steel type. Huge application potential. [0003] However, the high content of aluminum is easy to combine with nitrogen during the smelting process to form aluminum nitride inclusions. Moreover, aluminum nitride ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C33/04C21C7/00
CPCC22C33/04C21C7/0006
Inventor 朱航宇王蓝卿李建立彭其春宋明明薛正良
Owner WUHAN UNIV OF SCI & TECH