Polyester yarn with flame retardant property and preparation process thereof

A technology of flame retardant performance and preparation process is applied in the field of polyester yarn with flame retardant performance and its preparation technology, which can solve the problems of poor flame retardant performance of polyester yarn, and achieve the effect of not affecting fiber performance.

Pending Publication Date: 2021-07-16
太仓市泽记新材料有限公司
View PDF10 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides a polyester yarn with flame-retardant propert

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A polyester yarn with flame-retardant properties, which is composed of the following raw materials in the weight ratio: 10 parts of 2-carboxyethylphenyl hypophosphorous acid, 45 parts of ethylene glycol, 8 parts of dimethyl methyl phosphate, and 6 parts of stabilizer parts, 3 parts of toner, 15 parts of polyester catalyst, appropriate amount of PTA and appropriate amount of pure PET chips.

[0029] The stabilizer is trimethylolpropane.

[0030] The toner is cobalt acetate.

[0031] The polyester catalyst is antimony trioxide.

[0032] A preparation process of polyester yarn with flame retardant properties, comprising the following steps:

[0033] S1. Mix and stir the above-mentioned 2-carboxyethylphenyl hypophosphorous acid and ethylene glycol, add dimethyl methyl phosphate after stirring for 12 minutes and continue stirring for 10 minutes, and record the obtained mixture as a flame retardant mixture;

[0034] S2. Put the flame retardant mixture prepared in S1 and 20...

Embodiment 2

[0044] A polyester yarn with flame-retardant properties, which is composed of the following raw materials in the weight ratio: 13 parts of 2-carboxyethylphenylphosphinic acid, 35 parts of ethylene glycol, 7 parts of dimethyl methyl phosphate, and 5 parts of stabilizer parts, 6 parts of toner, 18 parts of polyester catalyst, appropriate amount of PTA and appropriate amount of pure PET chips.

[0045] The stabilizer is trimethylolpropane.

[0046] The toner is cobalt acetate.

[0047] The polyester catalyst is antimony trioxide.

[0048] A preparation process of polyester yarn with flame retardant properties, comprising the following steps:

[0049] S1. Mix and stir the above-mentioned 2-carboxyethylphenyl hypophosphorous acid and ethylene glycol, add dimethyl methyl phosphate after stirring for 10 minutes and continue stirring for 8 minutes, and record the obtained mixture as a flame retardant mixture;

[0050] S2. Put the flame retardant mixture prepared in S1 and 25 parts ...

Embodiment 3

[0060] A polyester yarn with flame-retardant properties, which is composed of the following raw materials in the weight ratio: 15 parts of 2-carboxyethylphenyl hypophosphorous acid, 40 parts of ethylene glycol, 5 parts of dimethyl methyl phosphate, and 8 parts of stabilizer parts, 4 parts of toner, 20 parts of polyester catalyst, appropriate amount of PTA and appropriate amount of pure PET chips.

[0061] The stabilizer is trimethylolpropane.

[0062] The toner is cobalt acetate.

[0063] The polyester catalyst is antimony trioxide.

[0064] A preparation process of polyester yarn with flame retardant properties, comprising the following steps:

[0065] S1. Mix and stir the above-mentioned 2-carboxyethylphenyl hypophosphorous acid and ethylene glycol, add dimethyl methyl phosphate after stirring for 15 minutes and continue stirring for 5 minutes, and record the obtained mixture as a flame retardant mixture;

[0066] S2. Put the flame retardant mixture prepared in S1 and 22 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of polyester yarn preparation processes, and provides a polyester yarn with flame retardance and a preparation process thereof. Flame retardants 2-carboxyethyl phenyl hypophosphorous acid and dimethyl methylphosphate are added in the process of esterifying PTA into PET; the flame retardant 2-carboxyethyl phenyl hypophosphorous acid and a dimethyl methylphosphate monomer can be embedded into the PTA macromolecular chain through the esterification reaction to form the PET, so that the 2-carboxyethyl phenyl hypophosphorous acid and the dimethyl methylphosphate can be closely arranged in the gaps of the PTA macromolecules so as to form the flame-retardant PET through copolymerization; at a high temperature, 2-carboxyethyl phenyl hypophosphorous acid and the dimethyl methylphosphate can exert the flame retardant property for flame retardance; and then flame-retardant PET is prepared into the flame-retardant polyester fiber, the flame-retardant polyester fiber is spun into the polyester yarn with the flame-retardant performance; and the polyester yarn prepared through the preparation process has no side reaction, does not affect the fiber performance and has permanent flame retardance.

Description

technical field [0001] The invention relates to the technical field of polyester yarn preparation technology, in particular to a flame-retardant polyester yarn and a preparation process thereof. Background technique [0002] Polyester yarn refers to the yarn spun from polyester. Polyester is a kind of fiber made of polymer by spinning. At present, it mostly refers to the fiber produced from ethylene phthalate as raw material. According to its raw material English name "polyethyleneterephthalate" abbreviation, referred to as "PET" fiber. Commonly known as polyester in our country. The so-called "yarn" actually refers to the general term of "yarn" and "thread". Rotating and twisting to form a slender object with a certain strength and linear density; and the "thread" is a strand formed by twisting two or more single yarns. Yarn is a thin strand made of cotton, wool, hemp, chemical fiber, etc., which is elongated and twisted, and then multi-strand thin strands twisted with t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01F6/92D01F1/07D02G3/02D02G3/44C08G63/692C08G63/86
CPCD01F6/92D01F1/07D02G3/02D02G3/443C08G63/6926C08G63/866D10B2331/04
Inventor 曹泽
Owner 太仓市泽记新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka