A steam-free high-strength anti-corrosion pipe pile and its preparation method

A high-strength, anti-corrosion pipe technology, applied in the field of pipe piles, can solve problems affecting the structural strength and service life of pipe piles, threats to people's lives and property, collapse of buildings and bridges, etc., to improve compactness, improve flexural performance, and improve The effect of impermeability and durability

Active Publication Date: 2021-11-05
TIANJIN JIAN CHENG JI YE TUBULAR PILE CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, in the actual use of concrete pipe piles, since the pipe piles are often buried deep in the ground, the chloride ions and sulfate ions in the soil will cause corrosion on the surface and inside of the pipe piles. It affects the structural strength and service life of pipe piles, and even causes the collapse of buildings, bridges, etc., causing serious accidents and posing a great threat to people's lives and property

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A steam-free high-strength anti-corrosion pipe pile and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

preparation example

[0046] In the following preparation examples, examples and comparative examples:

[0047] Chitosan was purchased from Anhui Qianshun Biotechnology Co., Ltd.;

[0048] Basalt fiber was purchased from Zhoukou Qifeng Mineral Fiber Co., Ltd.;

[0049] The rubber particles adopt the rubber particles sold by Qufu Xinhua Trading Co., Ltd. with the item number of 118;

[0050] The water reducing agent was purchased from Beijing Shuangrenda Building Materials Co., Ltd.;

[0051] Nano-calcium carbonate was purchased from Yuantong Mineral Products Processing Plant;

[0052] Phosphorus slag powder was purchased from Guizhou Jinhaoyuan Trading Co., Ltd.

[0053] Preparation example

preparation example 1

[0055] The modification method of basalt fiber comprises the following steps:

[0056] The preparation of chitosan solution, chitosan is dissolved in concentration and is in the acetic acid solution of 0.5%, obtains the chitosan solution that concentration is 1.5wt%;

[0057] Soak the basalt fiber in the step In the chitosan solution, take out after soaking 2h and dry, obtain the basalt fiber of chitosan modification.

preparation example 2

[0059] The modification method of basalt fiber comprises the following steps:

[0060] The preparation of chitosan solution, chitosan is dissolved in the acetic acid solution that concentration is 0.8%, obtains the chitosan solution that concentration is 1.2wt%;

[0061] Soak the basalt fiber in the step In the chitosan solution, take out and dry after soaking 2.5h, obtain the basalt fiber of chitosan modification.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The application relates to a steam-cured high-strength anti-corrosion pipe pile and a preparation method thereof, belonging to the field of pile foundation technology, which includes 250-320 parts of cement, 1000-1200 parts of fine aggregate, and 1300-1500 parts of coarse Aggregate, 120-210 parts of water, 40-60 parts of fly ash, 50-70 parts of mineral powder, 6.5-8.5 parts of water reducer, 20-25 parts of nano-calcium carbonate, 0.12-0.2 parts of sodium hexametaphosphate, 2 ‑5 parts chitosan modified basalt fiber, 10‑18 parts dimethicone. Preparation method: Mix all components evenly to obtain concrete slurry; send the obtained concrete slurry into a pipe pile mold equipped with a steel cage, and centrifugally form it; hoist the centrifugal pile mold into an atmospheric curing tank for curing ; After the curing is finished, the pipe pile is obtained by demoulding. The present application has the effect of improving the corrosion resistance of pipe piles, thereby improving the durability of pipe piles.

Description

technical field [0001] The present application relates to the field of pipe piles, in particular to a non-steam curing high-strength anti-corrosion pipe pile and a preparation method thereof. Background technique [0002] The foundation refers to the load-bearing structure below the ground of the building. It is the enlarged part of the wall or column of the building underground. Its function is to bear the load transmitted from the upper structure of the building and transmit them to the foundation together with its own weight. [0003] At present, the utilization rate of pile foundation in foundation engineering exceeds 90%, and it is one of the commonly used foundation forms. The pile foundation is composed of two parts: a plurality of piles buried in the foundation (called pile group) and a pile platform (called cap) that combines the pile group to work together; the function of the pile foundation is to transmit the load to the ground The deep soil layer with good bear...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B111/20
CPCC04B28/04C04B2111/20C04B2111/2015C04B2201/50C04B14/02C04B14/06C04B14/28C04B18/08C04B18/141C04B14/4643C04B24/42C04B24/38C04B22/16C04B2103/302C04B18/22
Inventor 崔凤歧苏永刚
Owner TIANJIN JIAN CHENG JI YE TUBULAR PILE CO LTD