Colored polymer cement waterproof coating and preparation method thereof

A technology of waterproof coating and polymer, which is applied in the field of building materials, can solve the problems of poor dispersibility and reduce the water resistance of waterproof coating, and achieve the effect of good dispersibility, excellent waterproof effect and simple process

Active Publication Date: 2021-08-24
临海市忠信新型建材有限公司
View PDF10 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the dispersion of the pigment in the coating is poor, and it will also reduce the water resistance of the waterproof coating.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Colored polymer cement waterproof coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Prepare 100ml of silane coupling agent aqueous solution with a mass concentration of 1%, then add 50ml of 95% absolute ethanol solution, fully react for 20min in a water bath at 30°C, then add 10g of pigment powder, keep stirring, and gradually heat up to 50°C, Afterwards, heat preservation treatment for 2 hours, and finally suction filtration and drying at 105°C, and the dried solids were ground to obtain modified pigment powders;

[0032] Mix 5g of the modified pigment powder prepared above with 100g of water, stir until the solid dissolves, then add 100g of quartz sand for high-speed stirring, then let it stand for 24 hours, add 20g of EVA emulsion, continue stirring, and finally dry it at 70°C. Obtain pretreated quartz colored sand;

[0033] Place the pretreated quartz colored sand prepared above in a muffle furnace and first heat-preserve at 200°C for 2 hours, then gradually raise the temperature to 500°C for 2 hours at a heating rate of 5°C / min, and take it out af...

Embodiment 2

[0036] Prepare 100ml of silane coupling agent aqueous solution with a mass concentration of 1%, then add 50ml of 95% absolute ethanol solution, fully react for 10min in a water bath at 40°C, then add 10g of pigment powder, keep stirring, and gradually heat up to 70°C, Afterwards, heat preservation treatment for 2 hours, and finally suction filtration and drying at 105°C, and the dried solids were ground to obtain modified pigment powders;

[0037] Mix 10g of the modified pigment powder prepared above with 100g of water, stir until the solid dissolves, then add 100g of quartz sand for high-speed stirring, then let it stand for 24 hours, add 20g of EVA emulsion, continue stirring, and finally dry it at 70°C. Obtain pretreated quartz colored sand;

[0038] Place the pretreated quartz colored sand prepared above in a muffle furnace and first heat-preserve at 200°C for 2 hours, then gradually raise the temperature to 500°C for 2 hours at a heating rate of 5°C / min, and take it out a...

Embodiment 3

[0041] Prepare 100ml of silane coupling agent aqueous solution with a mass concentration of 1%, then add 50ml of 95% absolute ethanol solution, fully react for 10min in a water bath at 30°C, then add 10g of pigment powder, keep stirring, and gradually heat up to 60°C, Afterwards, heat preservation treatment for 2 hours, and finally suction filtration and drying at 105°C, and the dried solids were ground to obtain modified pigment powders;

[0042] Mix 7g of the modified pigment powder prepared above with 100g of water, stir until the solid is dissolved, then add 100g of quartz sand for high-speed stirring, then let it stand for 24 hours, add 20g of EVA emulsion, continue stirring, and finally dry it at 70°C. Obtain pretreated quartz colored sand;

[0043] Place the pretreated quartz colored sand prepared above in a muffle furnace and first heat-preserve at 200°C for 2 hours, then gradually raise the temperature to 500°C for 2 hours at a heating rate of 5°C / min, and take it out...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a colored polymer cement waterproof coating which comprises a powder material and a liquid material, and the mass ratio of the liquid material to the powder material is (10-15):25; the powder material comprises the following components in parts by weight: 25-55 parts of white cement, 10-20 parts of heavy calcium carbonate and 35-60 parts of modified colored quartz sand, wherein the modified colored quartz sand is prepared by adopting modified pigment powder and EVA emulsion to pretreat quartz sand and then conducting roasting, and the mass ratio of the quartz sand to the modified pigment powder to the EVA emulsion is 1:(0.05-0.1):(0.2-0.4); and the liquid material comprises the following components in parts by weight: 80-100 parts of emulsion, 1-3 parts of a defoaming agent, and 10-15 parts of water, wherein the emulsion is formed by co-doping an EVA emulsion and a styrene-acrylic emulsion in a mass ratio of 1:(1-2.5). The invention also discloses a preparation method of the colored polymer cement waterproof coating. The prepared colored polymer cement waterproof coating is uniform in color, free of color attachment and floating phenomena, high in tensile strength, small in porosity, few in communicating holes and excellent in waterproof effect.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a colored polymer cement waterproof coating and a preparation method thereof. Background technique [0002] Polymer cement waterproof coating, also known as JS waterproof coating, is a two-component water-based waterproof coating that is formulated with polymer emulsion and cement as the main raw materials, adding fillers and other additives, and is cured by water volatilization and cement hydration reaction to form a film. coating. Polymer cement waterproof coating has the flexibility of emulsion and the high strength of cement. It is one of the most widely used water-based waterproof coatings in the waterproof market. It is widely used in the waterproofing of toilets, kitchens, balconies, basements and other areas. [0003] Traditional waterproof coatings usually add pigments, which are often mixed into waterproof coatings in the form of powder or color paste to inc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B111/27C04B111/50C04B111/82
CPCC04B28/04C04B2111/82C04B2111/27C04B2111/00508C04B2111/00293C04B2201/10C04B2201/50C04B2111/503C04B24/42C04B24/026C04B24/26C04B14/06C04B14/28C04B2103/54C04B2103/50
Inventor 范树景安艳菲何广朋
Owner 临海市忠信新型建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap