UV curing adhesive and preparation method thereof

A production method and technology for curing glue, applied in the direction of adhesives, adhesive types, polyurea/polyurethane adhesives, etc., can solve problems such as retention

Active Publication Date: 2022-01-11
深圳市浩力新材料技术有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the widespread use of UV-curable adhesives, the problems caused by UV-curable adhesives have become increasingly prominent. Due to their special chemical structures and characteristics, traditional UV-curable adhesives cannot be degraded or hydrolyzed by microorganisms in the environment. Long-term stay in the environment has become a major hidden danger and threat in modern society

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • UV curing adhesive and preparation method thereof
  • UV curing adhesive and preparation method thereof
  • UV curing adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

experiment example 1

[0058] A kind of UV solid adhesive is prepared by mixing the raw materials in Table 1 parts by weight:

[0059] Raw material mixing ratio of UV-curable adhesive in Table 1 Experimental Example 1

[0060] Polybutylene succinate modified acrylate resin 45 copies VORANOL TM 220-110N Polyol

25 copies Isooctyl acrylate 10 copies Polyethylene glycol (200) diacrylate 14 copies 1-Hydroxycyclohexyl phenyl ketone 3 copies 2,4,6-Trimethylbenzoylphenylphosphonic acid ethyl ester 1 copy EFKA-3777 1 copy Silok-5100 1 copy

[0061] Wherein, the preparation method of polybutylene succinate modified acrylate resin is:

[0062] Put 100 parts of 1,4-butanediol and 65 parts of succinic acid into the reaction kettle; add 0.05 parts of tetrabutyl titanate under the protection of nitrogen; control the stirring speed at 150-200r / min, heat the oil bath and keep it at 130-160°C, use a vacuum dehydration device to reduce the internal...

experiment example 2

[0067] A kind of UV solid adhesive, is mixed and formulated by the raw material of table 2 parts by weight:

[0068] Raw material mixing ratio of UV-curable adhesive in Table 2 Experimental Example 2

[0069] Polybutylene succinate modified acrylate resin 38 copies WANOL C2010 32 copies Polyethylene glycol (200) diacrylate 16 copies 2-Methyl-2-propenoic acid-3,3,5-trimethylcyclohexyl ester 9.5 servings 1-Hydroxycyclohexyl phenyl ketone 2 copies 2,4,6-Trimethylbenzoylphenylphosphonic acid ethyl ester 1 copy EFKA-3777 1 copy Silok-5100 0.5 parts

[0070] Wherein, the preparation method of polybutylene succinate modified acrylate resin is:

[0071] Put 100 parts of 1,4-butanediol and 65 parts of succinic acid into the reaction kettle; add 0.05 parts of tetrabutyl titanate under the protection of nitrogen; control the stirring speed at 150-200r / min, heat the oil bath and keep it at 130-160°C, use a vacuum dehydratio...

experiment example 3

[0076] A kind of UV solid adhesive is prepared by mixing the raw materials in Table 1 parts by weight:

[0077] Raw material mixing ratio of UV-curable adhesive in Table 3 Experimental Example 3

[0078] Polybutylene succinate modified acrylate resin 49 copies Acetyl tributyl citrate 20 copies Isooctyl acrylate 15 copies 2-(2-Ethoxyethoxy)ethyl acrylate 11 copies 1-Hydroxycyclohexyl phenyl ketone 2 copies 2,4,6-Trimethylbenzoylphenylphosphonic acid ethyl ester 1.5 servings EFKA-3777 0.5 parts Silok-5100 1 copy

[0079] Wherein, the preparation method of polybutylene succinate modified acrylate resin is:

[0080] Put 100 parts of 1,4-butanediol and 65 parts of succinic acid into the reaction kettle; add 0.05 parts of tetrabutyl titanate under the protection of nitrogen; control the stirring speed at 150-200r / min, heat the oil bath and keep it at 130-160°C, use a vacuum dehydration device to reduce the internal pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a UV curing adhesive and a preparation method thereof. The preparation method of the UV curing adhesive comprises the following steps: adding 30-60 parts of poly(butylene succinate) modified acrylate resin, 15-50 parts of a filler, 15-40 parts of an active monomer and 1-10 parts of a photoinitiator into a stirring pot and carrying out rapid stirred for 20-50 min; and then adding 0.5-5 parts of a flatting agent, and continuing stirring for 5-20 minutes. The UV adhesive provided by the invention can be naturally degraded under certain conditions after being cured, and is green and environment-friendly.

Description

technical field [0001] The invention relates to the technical field of chemical adhesives, in particular to a UV curing adhesive and a preparation method thereof. Background technique [0002] UV curing adhesive is a kind of adhesive that makes the bonded substrate quickly produce bonding performance under the action of ultraviolet light energy. UV curing adhesives have developed rapidly at home and abroad due to their advantages of fast curing speed, low curing temperature, no pollution, and energy saving. They have been widely used in printed circuit board manufacturing, optical fiber bonding, liquid crystal display installation, electronic component assembly, etc. It plays a huge role in many fields, especially in some places where traditional adhesives cannot be used, such as high-precision electronic equipment or the bonding of heat-sensitive substrates. With the widespread use of UV-curable adhesives, the problems caused by UV-curable adhesives have become increasingl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J175/14C08G18/42C08G18/67
CPCC09J175/14C08G18/4238C08G18/672C08G18/42Y02W90/10
Inventor 林武欧阳亮王攀
Owner 深圳市浩力新材料技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap