Resin grinding wheel for cutting and disassembling reinforced concrete as well as preparation method and application of resin grinding wheel

A reinforced concrete and resin grinding wheel technology, applied in the field of mold processing, can solve problems such as dangerous accidents, saw blade deformation, tooth loss, etc., and achieve the effect of increasing cutting speed and avoiding temperature rise

Pending Publication Date: 2022-02-25
LANGFANG SHENGSEN ABRASIVES CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The cutting test of reinforced concrete found that diamond saw blades or alloy toothless saw blades can cut cement stones faster when cutting reinforced concrete, but when cutting steel bars inside concrete, the speed is slower and the frictional heat is large. Accumulation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Resin grinding wheel for cutting and disassembling reinforced concrete as well as preparation method and application of resin grinding wheel
  • Resin grinding wheel for cutting and disassembling reinforced concrete as well as preparation method and application of resin grinding wheel
  • Resin grinding wheel for cutting and disassembling reinforced concrete as well as preparation method and application of resin grinding wheel

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0038] Example 1 Pretreatment of abrasives

[0039] Fully mix 100 parts of white corundum abrasive with 1.0-1.5 parts of sodium silicate aqueous solution (concentration is 50-51°Bé Baume degree), add 0.8-1.2 parts of zirconia powder to fully mix, bake at 900-950 ℃ temperature Bake for 30 minutes.

[0040] The present invention finds that the pretreatment effect is not only related to the proportion of the formula material, but also the baking temperature and time are particularly important for the hardening of the sodium silicate aqueous solution, which can improve the surface strength of white corundum and enhance the abrasive toughness.

Example Embodiment

[0041] Example 2 Preparation of resin grinding wheel of the present invention

[0042] Resin grinding wheel of the present invention is made of the following raw materials by weight:

[0043] 60 parts of white corundum abrasive, 30 parts of silicon carbide abrasive, 15 parts of phenolic resin, 5 parts of potassium hexafluoroaluminate, 2 parts of calcium sulfate whisker, 0.4 part of KH550 silane coupling agent, wherein the resin solution and the resin The weight ratio of the powder is 1:1, wherein the phenolic resin powder is composed of thermosetting phenolic resin powder and thermoplastic phenolic resin powder, and the weight ratio of thermosetting phenolic resin powder to thermoplastic phenolic resin powder is 7:3.

[0044] The preparation method of the grinding wheel of the present invention is:

[0045] (1) Mixing:

[0046] (1-1) Quantitatively put the required abrasives into the mixer and mix them evenly.

[0047] (1-2) Add KH550 silane coupling agent to wet and wrap t...

Example Embodiment

[0067] Example 3 Preparation of resin grinding wheel of the present invention

[0068] Resin grinding wheel of the present invention is made of the following raw materials by weight:

[0069] 70 parts of white corundum abrasive, 40 parts of silicon carbide abrasive, 20 parts of phenolic resin, 15 parts of potassium hexafluoroaluminate, 5 parts of calcium sulfate whisker, 0.6 part of KH550 silane coupling agent, wherein, the resin solution and the resin The weight ratio of the powder is 1:3, wherein the phenolic resin powder is composed of thermosetting phenolic resin powder and thermoplastic phenolic resin powder, and the weight ratio of thermosetting phenolic resin powder to thermoplastic phenolic resin powder is 7:3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of mold processing, and particularly relates to a resin grinding wheel for cutting and disassembling reinforced concrete as well as a preparation method and application of the resin grinding wheel. The resin grinding wheel for cutting and disassembling the reinforced concrete is prepared from the following raw materials in parts by weight: 60-70 parts of a white corundum grinding material, 30-40 parts of a silicon carbide grinding material, 15-20 parts of phenolic resin, 5-15 parts of potassium aluminate, 2-5 parts of calcium sulfate whiskers and 0.4-0.6 part of a coupling agent.

Description

technical field [0001] The invention belongs to the technical field of mold processing, and in particular relates to a resin grinding wheel for cutting and dismantling reinforced concrete, a preparation method and application thereof. Background technique [0002] Grinding wheel, also known as bonded abrasive, is a bonded abrasive with a certain strength that consolidates ordinary abrasives into a certain shape (mostly circular with a through hole in the center) by a binder. It is generally composed of abrasives, binders and pores. These three parts are often called the three elements of bonded abrasives. According to different classifications of bonds, the common ones are ceramic (bond) grinding wheels, resin (bond) grinding wheels, and rubber (bond) grinding wheels. Grinding wheel is the most widely used type of grinding tool. It rotates at high speed when used, and can be used for rough grinding, semi-finishing and Fine grinding as well as grooving and parting off etc. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B24D3/28B24D3/34B24D18/00B24D5/04B24D5/12
CPCB24D3/285B24D3/344B24D18/0009B24D5/12B24D5/04
Inventor 许胜英许亚宁许静贤
Owner LANGFANG SHENGSEN ABRASIVES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap