Glass raw material tabletting method suitable for X-ray fluorescence spectrometer analysis

A fluorescence spectrometer and glass raw material technology, which is applied in the field of instrument analysis, can solve the problems of inability to perform X-ray fluorescence spectrometer analysis, affecting the service life of equipment, and easy cracking of samples, so as to improve sample detection efficiency, ensure use safety, and powder molding. stable effect

Pending Publication Date: 2022-07-01
中建材(蚌埠)光电材料有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the problem that after the glass raw material is pressed into tablets, the sample is easily cracked and damaged, which cannot be analyzed by the X-ray fluorescence spectrometer or even affects the service life of the equipment, and to provide a glass raw material tablet suitable for the analysis of the X-ray fluorescence spectrometer method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass raw material tabletting method suitable for X-ray fluorescence spectrometer analysis
  • Glass raw material tabletting method suitable for X-ray fluorescence spectrometer analysis
  • Glass raw material tabletting method suitable for X-ray fluorescence spectrometer analysis

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Select the raw material alumina to be tested, add the alumina into an agate mortar and grind it into powder and sieve it, collect a sample with a particle size of 150 mesh, and then pass the mass ratio with the binder to a ratio of 1:3. After weighing, pour it into the tablet press mold, adjust the tablet pressure of the tablet press to 225KN, and start pressing the sample after the pressure holding time is 25s, and use the pressed sample for X-ray fluorescence spectrometer detection.

Embodiment 2

[0032] Select the raw material feldspar to be tested, add the feldspar into an agate mortar and grind it into powder and sieve it, collect a sample with a particle size of 75 meshes, and then pass the mass ratio of 3:1 with the binder. After weighing, pour it into the mold of the tablet press, adjust the tablet pressure of the tablet press to 200KN, and start to press the sample after the pressure holding time is 50s, and use the pressed sample for X-ray fluorescence spectrometer detection.

Embodiment 3

[0034] Select the raw material silica sand to be tested, add the silica sand into an agate mortar and grind it into powder and sieve it, collect a sample with a particle size of 100 mesh, and then weigh it with the binder in a ratio of 2:1 by mass. After the weight is poured into the tablet press mold, the tablet pressure of the tablet press machine is adjusted to 250KN, and the pressure holding time is 30s, and then the sample is pressed, and the pressed sample is used for X-ray fluorescence spectrometer detection.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a glass raw material tabletting method suitable for analysis of an X-ray fluorescence spectrometer. The method is characterized by comprising the following steps: (1) preparing a glass raw material to be detected; (2) grinding the glass raw material, sieving after grinding, and controlling the granularity to be 50-200 meshes; (3) mixing a glass raw material with the mesh number of 50-200 and a binder according to the mass ratio of 1: 1-5: 1, wherein the binder is any one of boric acid, methyl cellulose, polyethylene and the like; (4) feeding the raw materials mixed in the step (3) into a tablet press for tabletting, controlling the pressure of the tablet press to be 200-300KN, keeping the pressure for 20-60s, and starting to press a sample; and (5) detecting the pressed sample by using an X-ray fluorescence spectrophotometer. The method has the advantages that the binder is added before tabletting, so that the tabletted sample is smooth in surface and free of cracks, and the sample injection requirement of X-ray fluorescence spectrophotometer detection equipment can be met; powder forming is more efficient, and the sample detection efficiency is improved; and powder forming is more stable, and use safety of equipment is guaranteed.

Description

technical field [0001] The invention belongs to the technical field of instrument analysis, and relates to the field of X-ray fluorescence spectrometer analysis, in particular to a glass raw material tabletting method suitable for X-ray fluorescence spectrometer analysis. Background technique [0002] In the production of glass industry, raw material quality, composition analysis, intermediate control, etc. all need to use analytical methods. In traditional chemical analysis methods, the analysis process is mostly long, and the analysis needs to be completed through multiple processes such as sampling, sample preparation, sample fusion, and sample measurement. The workload of the analyst is very large, and the analysis cycle of a single element takes 1-2 For the urgent production situation, this method is not suitable; when the concentration of an element in the raw material is large, the measurement of the element is not suitable for plasma emission spectrometry (ICP), and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G01N23/2202G01N23/223
CPCG01N23/2202G01N23/223
Inventor 吴雪良周俊朱涛武杰陈士威封磊
Owner 中建材(蚌埠)光电材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap