Preparation method of polyester fabric moisture absorption and sweat releasing finishing agent containing naphthalene structure

A technology for moisture-absorbing and sweat-wicking polyester fabrics is applied in the field of preparation of moisture-absorbing and sweat-wicking finishing agents, which can solve the problems of difficulty in washing and removing stains, limitations, and long process time, so as to reduce carbon and sewage emissions, and save water and energy. , the effect of reducing the process time

Pending Publication Date: 2022-07-15
DYMATIC CHEM
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the absence of hydrophilic and hygroscopic groups in the molecular structure, the degree of swelling in water is small, and the dry and wet strengths and elongation at break are basically the same. It shows strong electrostatic and dirt-absorbing properties in the use of clothing or decorations. , Difficult to remove stains, poor hand feeling and other shortcomings, which are greatly restricted in use
[0003] At present, the finishing of polyester usually separates hydrophilic finishing and hand finishing, so it usually has the following disadvantages: long process time, low production efficiency; large amount of water and energy consumption, large carbon emissions; large amount of sewage, sewage difficult to handle

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of polyester fabric moisture absorption and sweat releasing finishing agent containing naphthalene structure
  • Preparation method of polyester fabric moisture absorption and sweat releasing finishing agent containing naphthalene structure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Synthesis of the moisture-absorbing and perspiring agent containing naphthalene structure: First, 70 g of polyethylene glycol was dehydrated, and the temperature was controlled at 100-105 °C for vacuum dehydration for 1 hour. After the dehydration is completed, 15g of dimethyl 1,8-naphthalenedicarboxylate, 15g of ethylene glycol, and 0.03g of zinc acetate are successively added to the reaction vessel equipped with a thermometer and a nitrogen tube, and the temperature is slowly raised under nitrogen protection for 25 to 30 minutes. When the temperature rose to 170°C, the temperature was controlled at 170-180°C for 4 hours.

[0017] After the transesterification is completed, continue to heat up to 190°C, control the temperature at 190-200°C and react for 30min, start vacuuming, and continue to heat up to 230°C, control the temperature at 220-230°C, and wait until the vacuum degree in the reaction vessel reaches -0.099MPa or more Timely heat preservation for 3 hours, and...

Embodiment 2

[0019] Synthesis of the moisture-absorbing and perspiring agent containing naphthalene structure: First, 65 g of polyethylene glycol was dehydrated, and the temperature was controlled at 100-105 °C for vacuum dehydration for 1 hour. After the dehydration was completed, 20g of dimethyl 1,8-naphthalene dicarboxylate, 15g of ethylene glycol, 0.03g of magnesium acetate were successively added to the reaction vessel equipped with a thermometer and a nitrogen tube, and the temperature was slowly raised under nitrogen protection for 25-30 minutes. When the temperature rose to 170°C, the temperature was controlled at 170-180°C for 4 hours.

[0020] After the transesterification is completed, continue to heat up to 190°C, control the temperature at 190-200°C and react for 30min, start vacuuming, and continue to heat up to 230°C, control the temperature at 220-230°C, and wait until the vacuum degree in the reaction vessel reaches -0.099MPa or more Timely heat preservation for 3 hours, a...

Embodiment 3

[0022] Synthesis of a moisture-absorbing and perspiring agent containing a naphthalene structure: firstly, 60 g of polyethylene glycol was subjected to dehydration treatment, and the temperature was controlled at 100-105 °C for vacuum dehydration for 1 hour. After the dehydration is completed, 25g of dimethyl 1,8-naphthalenedicarboxylate, 15g of ethylene glycol, 0.03g of calcium acetate are added successively to the reaction vessel equipped with a thermometer and a nitrogen tube, and the temperature is slowly raised under nitrogen protection for 25-30 minutes. When the temperature rose to 170°C, the temperature was controlled at 170-180°C for 4 hours.

[0023] After the transesterification is completed, continue to heat up to 190 °C, control the temperature at 190 to 200 °C for 30 minutes, start vacuuming, and continue to heat up to 230 °C, control the temperature at 220 to 230 °C, and wait until the vacuum degree in the reaction vessel reaches -0.099MPa or more Timely heat pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of a polyester fabric moisture-absorbing and sweat-releasing finishing agent containing a naphthalene structure, which comprises the following steps: by taking dimethyl 1, 8-naphthalate, ethylene glycol, polyethylene glycol and a catalyst as raw materials, carrying out transesterification, and then carrying out polycondensation to synthesize a polyester-polyether copolymerization type moisture-absorbing and sweat-releasing finishing agent suitable for polyester fabrics. The method is high in synthesis efficiency, the finished fabric is good in hydrophilicity and hand feeling, the moisture absorption and sweat releasing agent and silicone oil can be subjected to one-bath finishing, the hydrophilic performance is excellent after one-bath finishing, and the after-finishing efficiency of the fabric is greatly improved.

Description

technical field [0001] The invention relates to the technical field of moisture-absorbing and sweat-wicking finishing agents for polyester fabrics, in particular to a method for preparing a moisture-absorbing and sweat-wicking finishing agent that is applied to polyester fabrics and can maintain hydrophilic and washable properties when bathed with silicone oil. Background technique [0002] In addition to satisfying the basic functions of clothing fabrics, from the perspective of wearing comfort for the human body, if the sweat can be transferred and discharged in time, the clothes will not stick to the skin surface, making people feel hot and airtight, and enhancing the wearing comfort. especially important. Synthetic fibers have excellent properties unmatched by natural fibers, especially polyester, which accounts for more than 60% of synthetic chemical fibers. It has high breaking strength, high elastic modulus, good heat resistance, wear resistance, resistance and corro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G63/672C08G63/83D06M15/507D06M15/53D06M101/32
CPCC08G63/672C08G63/83D06M15/507D06M15/53D06M2101/32
Inventor 蒙业云梁永标黄尚东
Owner DYMATIC CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com