Catalyst for hydrogenating Fischer-Tropsch synthetic wax and its prepn

A technology for Fischer-Tropsch synthesis of waxes and catalysts, which is applied in the preparation of organic compounds, chemical instruments and methods, catalysts for physical/chemical processes, etc. It can solve the problems of low hydrogenation saturation catalytic activity and achieve the effect of high hydrogenation saturation activity.

Inactive Publication Date: 2004-09-01
SYNFUELS CHINA TECH CO LTD
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above catalysts have good hydrogenation and dearomatization properties for petroleum waxes, but their catalytic activity for hydrogenation saturation of waxy hydrocarbons with high olefin content is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] γ-Al 2 o 3 The pellets were treated with steam for 4 hours under the conditions of 540°C and water-to-solution ratio of 2 (weight ratio) to obtain S 0 ;Weigh S 0 100g, add to TiCl 4 ethanol solution (66ml TiCl 4 +100ml ethanol) placed at room temperature for overnight hydrolysis, dried at 120°C, and baked in a muffle furnace at 500°C for 4 hours to obtain TiO 2 -Al 2 o 3 Carrier S 1 . Then, nickel nitrate (Ni(NO 3 ) 2 ·6H 2 O), ammonium metatungstate ((NH 4 ) 2 W 4 o 13 ·8H 2 O), dissolved in water according to the equal-volume impregnation method, prepared as an impregnation solution, and put TiO 2 -Al 2 o 3 Oxide carrier S 1 , impregnated for 2 hours, dried and roasted to obtain Ni-W-TiO 2 / Al 2 o 3 Catalyst N 1 . Its weight percentage is: NiO: WO 3 :TiO 2 : Al 2 o 3 =12.7:4.2:8.3:74.8.

Embodiment 2

[0026] A commodity γ-Al 2 o 3 The pellets were treated with steam for 4 hours under the conditions of 540°C and water-to-solution ratio of 2 (weight ratio) to obtain S 0 ;Weigh S 0 100g, add to Ti(OC 4 h 9 ) 4 Solution, weigh 100gS 0 Added to Ti(OC 4 h 9 ) 4 in ethanol solution (58mlTi(OC 4 h 9 ) 4 + 100ml ethanol) placed at room temperature for hydrolysis overnight, dried at 120°C, and placed in a muffle furnace at 500°C for 6 hours to obtain TiO 2 -Al 2 o 3 Oxide carrier S 2 . Then, nickel nitrate (Ni(NO 3 ) 2 ·6H 2 O), ammonium metatungstate ((NH 4 ) 2 W 4 o 13 ·8H 2 O), dissolved in water according to the equal-volume impregnation method, prepared as an impregnation solution, and put TiO 2 -Al 2 o 3 Oxide carrier S 2 , impregnated for 2 hours, dried and roasted to obtain Ni-W-TiO 2 / Al 2 o 3 Catalyst N 2 . Its weight percentage is: NiO: WO 3 :TiO 2 : Al 2 o 3 =14.0:3.5:7.0:75.5.

Embodiment 3

[0028] TiO 2 -Al 2 o 3The carrier is prepared by mixing industrial aluminum hydroxide dry rubber powder and titanium hydroxide dry rubber powder and extrusion molding. For example, weigh 100g of aluminum hydroxide dry rubber powder and 16.1g of metatitanic acid powder, add 9ml of 5% (weight ratio) dilute nitric acid, mix thoroughly, then add 3g of extrusion aid Tianqing powder, etc., and extrude into 3mm strips , dried at 120°C, placed in a muffle furnace and baked at 520°C for 3 hours to obtain TiO 2 -Al 2 o 3 Carrier S 3 . Then, nickel nitrate (Ni(NO 3 ) 2 ·6H 2 O), ammonium metatungstate ((NH 4 ) 2 W 4 o 13 ·8H 2 O), dissolved in water according to the equal-volume impregnation method, prepared as an impregnation solution, and put TiO 2 -Al 2 o 3 Oxide carrier S 3 , impregnated for 2 hours, dried and roasted to obtain Ni-W-TiO 2 / Al 2 o 3 Catalyst N 3 , and its weight percentage is: NiO:WO 3 :TiO 2 :Al 2 o 3 =11.5:5.0:14:69.5.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The catalyst consists of nickel oxide 5.0-20.0 wt%, tungsten oxide 0.1-15.0 wt%, titania 1.0-20.0 wt% and alumina 45.5-93.9 wt%. The preparation process includes the treatment of alumina, the introduction of titania, and impregnating active tungsten oxide and nickel oxide components. The present invention has the advantages of high hydrogenation activity for heavy hydrocarbon, and is especially suitable for hydrogenating saturation wax with high olefin content.

Description

[0001] Field: [0002] The invention relates to a hydrogenation catalyst, in particular to a hydrogenation catalyst used for hydrogenation and saturation of olefins in the crude wax by using carbon monoxide hydrogenation to synthesize crude product wax as a raw material. Background technique: [0003] Because the F-T crude product wax contains a large amount of olefins and a small amount of oxygen-containing compounds, it is easy to polymerize and be oxidized, so it cannot be directly processed for oil products and used in food and food packaging industries. For this reason, the F-T synthetic wax must be hydrogenated and saturated. At present, industrial wax hydrogenation catalysts are mainly for petroleum wax, and petroleum wax is different from F-T wax. It contains a large amount of condensed ring aromatic hydrocarbons and S, N, O heterocyclic compounds and other harmful substances, which need to be refined by catalytic hydrogenation. [0004] Paraffin hydrotreating catalys...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J21/06C07C67/60C07C69/26C10G45/08
Inventor 孙予罕任杰李永红李到姜建卫
Owner SYNFUELS CHINA TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com