Epoxy resin bromide with high glass transfusion temp. for glass fibre laminated board

A glass transition temperature, brominated epoxy resin technology, applied in the field of novel brominated epoxy resin, can solve the problems of poor processing operability of glass fiber laminates, achieve a wide lamination processing interval, excellent heat resistance, Effect of high resin melt viscosity

Inactive Publication Date: 2002-07-17
NANYA PLASTICS CORP
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a brominated epoxy resin with high glass transition temperature for glass fiber laminates, which has suitable reactivity, wide lamination processing range, good processing operability, high Tg and excellent heat resistance , electrical properties, flame resistance, and low water absorption, can solve the above problems caused by the use of multifunctional epoxy resins such as o-cresol cresol novolac epoxy resins, four-functional epoxy resins, and novolac epoxy resins. The problem of poor operability in processing fiber laminated boards

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Epoxy resin bromide with high glass transfusion temp. for glass fibre laminated board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] With 9.5 parts of phenol-benzaldehyde type polyfunctional epoxy resins (EEW=240, Nan Ya Plastic Industry Co., Ltd., product name NPPN-433), 53.7 parts of epoxy equivalents are the bisphenol A type epoxy resins of 186g / eq (Nan Ya Plastic Industry Co., Ltd., product name: NPEL-128E), 27.2 parts) tetrabromobisphenol A (TBBA), 4.8 parts epoxy equivalent weight (EEW) is the tetrabromobisphenol A type epoxy resin of 390g / eq (Nan Ya Plastics Industrial Co., Ltd., product name: NPEB-400), 4.8 parts of four-functional epoxy resin (EEW=220g / eq, (Nan Ya Plastic Industry Co., Ltd., product name: NPPN-431) these five kinds of chemical substances are at 170 ℃ After reacting for 120 minutes, the brominated epoxy resin "EP-1" was obtained, and the brominated epoxy resin "EP-1" was dissolved in 20% acetone to prepare an 80% solution. The resulting epoxy resin "EP-1" 1" has epoxy equivalent weight (EEW) = 390g / eq, weight average molecular weight = 2300, bromine content = 18.2%.

[0021]...

Embodiment 2

[0026] 40 parts of epoxy equivalent (EEW) is 186g / eq bisphenol A type epoxy resin (Nan Ya Plastic Industry Co., Ltd., product name: NPEL-128E) and 13 parts of phenol-benzaldehyde type multifunctional epoxy resin, 28 One part of tetrabromobisphenol A (TBBA), and two parts of four-functional epoxy resin (Nan Ya Plastic Industry Co., Ltd., product name: NPPN-431), the four chemical substances were reacted at 170 ° C for 120 minutes, cooled to 130 Then add 12 parts of epoxy equivalent (EEW) of bisphenol A type epoxy resin (Nan Ya Plastic Industry Co., Ltd., product name: NPEL-128E) and 5 parts of epoxy equivalent of 390g / eq tetrabromo Bisphenol A type epoxy resin (Nanya Plastic Industry Co., Ltd., product name: NPEB-400), after mixing evenly, brominated epoxy resin "EP-2" was prepared, and brominated epoxy resin "EP-2 " be dissolved in 20% acetone, be mixed with 80% solution, the epoxy resin " EP-2 " that obtains like this has epoxy equivalent EEW=394g / eq, weight average molecular...

Embodiment 3

[0029] 20.2 parts of epoxy equivalent (EEW) is 186g / eq bisphenol A type epoxy resin (Nan Ya Plastic Industry Co., Ltd., product name: NPEL-128E) and 49.5 parts of phenol-benzaldehyde type multifunctional epoxy resin, 21.2 Parts of tetrabromobisphenol A (TBBA), 3 chemical substances reacted at 170°C for 120 minutes, cooled to 130°C and then added 7 parts of tetrabromobisphenol A type epoxy with an epoxy equivalent weight (EEW) of 390g / eq Resin (Nan Ya Plastic Industry Co., Ltd., product name: NPEB-400) and 2 parts of four-functional epoxy resin (Nan Ya Plastic Industry Co., Ltd., product name: NPPN-431), after mixing evenly, brominated epoxy resin was obtained " EP-3 ", and brominated epoxy resin " EP-3 " is dissolved in 20% acetone, is mixed with 80% solution, and the epoxy resin " EP-3 " that obtains like this has epoxy equivalent weight (EEW)= 378, weight average molecular weight = 3366, bromine content = 15.8%. The resin solution was prepared from epoxy resin "EP-3", and t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
epoxy equivalentaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
epoxy equivalentaaaaaaaaaa
Login to View More

Abstract

The epoxy resin bromide is made up (A). phenol-benzaldehyde multifunctional epoxy resin 10-70 wt%, (B). bifunctinoal epoxy resin 0-55 wt%, (C). bromine-containing bifunctinoal epoxy resin 0-20 wt% and (D). tetrabromobisphenol A 15-40 wt% as main component through the process of synthesis. Said invented epoxy resin bromide can be used for making glass fibre laminated plate with high glass transfer temp. (Tg) and excellent heat resistance, and can be used to make high-performance electronic material.

Description

technical field [0001] The present invention relates to a novel brominated epoxy resin with suitable reactivity and a wide lamination processing range in the glass fiber laminated board manufacturing process, which has good processing operability and the obtained laminated substrate has a high glass transition temperature (Tg) and excellent heat resistance, suitable for high-performance electronic materials. Background technique [0002] With the development of printed circuit boards becoming lighter, thinner, smaller and more complex, the demand for high-performance materials is becoming more and more urgent. Usually the Tg value of a material is a very useful indicator, indicating the ability of the material to withstand dynamic stress such as vibration, high temperature, etc. at an operating temperature. If the material temperature is higher than Tg, it will often lead to poor interlayer bonding, and it will be bonded to copper foil. Then the strength is lost, resulting ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B17/12C08G59/14
Inventor 邹明仁
Owner NANYA PLASTICS CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com