A technology of polyvinyl butyral and foaming materials, which is applied in the field of polymer materials to achieve the effects of low cost, improved elasticity and wear resistance, and wide application

Active Publication Date: 2012-03-21
LUOHE IRON HORSE RUBBER PROD CO LTD
View PDF6 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For the preparation of polymer foam materials by using waste

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] The mass ratio of raw materials used in the polymer foam material of the present invention is:

[0048] Recycled waste polyvinyl butyral: 100 parts

[0049] Azodicarbonamide: 2 parts

[0050] Zinc stearate: 4 parts

[0051] Dioctyl phthalate: 10 parts

[0052] Borax: 0.3 parts

[0053] Manufacture polymer foam material of the present invention by following production process:

[0054] (1) Material mixing: Prepare the raw materials and ingredients according to the above ratio, and then add them to the high-speed mixer for high-speed mixing, the speed is 50r / min, and the time is 5min;

[0055] (2) Blending in the internal mixer: Add the high-speed mixed materials into the internal mixer for melt blending at a temperature of 130 0 C;

[0056] (3) Smelting into flakes: Put the material obtained by melting and blending in the extruder on the mill and masticate it into flakes at a temperature of 600 C;

[0057] (4) Molding and foaming molding: Weigh 25g of the material...

Embodiment 2

[0060] The mass ratio of raw materials used in the polymer foam material of the present invention is:

[0061] Recycled waste polyvinyl butyral: 100 parts

[0062] Azodicarbonamide: 4 parts

[0063] Zinc stearate: 2 parts

[0064] Nanoscale silica: 1 part

[0065] Acrylics: 7 parts

[0066] Dioctyl phthalate: 10 parts

[0067] Maleic anhydride: 0.3 parts

[0068] Polymer foams are produced by the following production processes:

[0069] (1) Material mixing: Prepare the raw materials and ingredients according to the above ratio, and then add them to the high-speed mixer for high-speed mixing, the speed is 50r / min, and the time is 5min;

[0070] (2) Extrusion blending: Put the high-speed mixed materials into the twin-screw extruder for melt blending, and the extrusion temperature is 140 0 C;

[0071] (3) Smelting into flakes: Put the material obtained by melting and blending in the extruder on the mill and masticate it into flakes at a temperature of 60 0 C;

[0072] (...

Embodiment 3

[0075] The mass ratio of raw materials used in the polymer foam material of the present invention is:

[0076] Recycled waste polyvinyl butyral: 100 parts

[0077] Azodicarbonamide: 4 parts

[0078] Zinc stearate: 2 parts

[0079] Zinc oxide: 1 part

[0080] Nanoscale titanium dioxide: 1 part

[0081] Acrylics: 7 parts

[0082] Dioctyl phthalate: 10 parts

[0083] Borax: 0.3 parts

[0084] Polymer foams are produced by the following production processes:

[0085] (1) Material mixing: Prepare the raw materials and ingredients according to the above ratio, and then add them to the high-speed mixer for high-speed mixing, the speed is 50r / min, and the time is 5min;

[0086] (2) Extrusion blending: Put the high-speed mixed materials into the twin-screw extruder for melt blending, and the extrusion temperature is 140 0 C;

[0087] (3) Smelting into flakes: Put the material obtained by melting and blending in the extruder on the mill and masticate it into flakes at a tempera...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polyvinyl butyral foamed material, which belongs to the field of high molecular materials. Recycled waste and used polyvinyl butyral is taken as a main raw material; rubber or an elastomer is taken as a main auxiliary material; a foaming agent, a foaming auxiliary agent, a plasticizing agent, a foamed hole nucleating agent, a foamed hole regulating agent, a crosslinking agent, a filler and the like are taken as the auxiliary materials; all the materials are mixed in a high-speed mixing machine at high speed, melted and blended in an extruding machine or an enclosed mixing machine, and formed through compression molding foaming in a flat-plate vulcanizing machine to obtain a polymer foamed material. The foamed material has excellent performance of an elastomer foamed material, has excellent cohesive property, is easy to process, and can be changed from wastes to valuables.

Description

technical field [0001] The invention relates to a polyvinyl butyral foaming material and belongs to the field of polymer materials. Background technique [0002] Due to the large number of bubbles inside the polymer foam material, it is not only light in weight and saves materials, but also has low thermal conductivity, good heat insulation performance, can absorb impact load, has excellent cushioning performance, sound insulation performance and high specific strength, etc. , agriculture, military, daily necessities and office supplies are widely used. [0003] Generally speaking, traditional polymer foaming materials can be roughly divided into plastic foaming materials and elastomer foaming materials according to the different raw materials used. Traditional plastic foaming materials have the advantages of simple formula, easy coloring and easy molding. It has the advantages of being processed into products with complex shapes, but its disadvantage is that its own elasti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L29/14C08L7/00C08L9/06C08L9/02C08L17/00C08L23/16C08L53/02C08K5/098C08K5/12C08K3/38C08K3/36C08K5/092C08K3/26C08J9/10C08J9/08
Inventor 曹艳霞张国栋王松杰唐淼王向红王凯丽曹贺鹏
Owner LUOHE IRON HORSE RUBBER PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager