Method for making composite membrane for separation of polymer fluid

A manufacturing method, a fluid separation technology, applied in the direction of semi-permeable membrane separation, chemical instruments and methods, membrane technology, etc., can solve problems such as difficult guarantees, and achieve completely unblocked pore channels, high permeation flux, and high intrinsic permeability Effect

Inactive Publication Date: 2003-10-29
SICHUAN UNIV
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage of this method is that it is difficult to ensure that the polydimethylsiloxane (PDMS) casting solution does not penetrate into the pores of the microporous support layer.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for making composite membrane for separation of polymer fluid
  • Method for making composite membrane for separation of polymer fluid
  • Method for making composite membrane for separation of polymer fluid

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A circular support layer microporous membrane with a diameter of 200 mm was produced by solvent evaporation method. The polymer material used was polysulfone (PS), the micropore size was 0.6 micron, the porosity was 60%, and the microporous film thickness was 150 micron. Use the solvent glycerin to filter through this microporous membrane to make the pores saturated with glycerin, and carefully remove the glycerin on the surface of the membrane. Polyvinyl alcohol (PVA) and corresponding cross-linking agents, additives and compounding agents are dissolved in solvent water to prepare a film-forming solution for the active skin layer of polyvinyl alcohol. The concentration of polyvinyl alcohol is 5% (W / W). Coat the polyvinyl alcohol membrane-making solution on the polysulfone support membrane whose pores are saturated with glycerin, and then place it at a temperature of 60°C to solidify the polyvinyl alcohol to form an active skin layer, and then place the membrane at a tem...

Embodiment 2

[0022] Adopt the solvent volatilization method to make a circular support layer microporous membrane with a diameter of 200 mm. The material used is polyacrylonitrile (PAN). is 150 microns. Use solvent glycerin to filter through this microporous membrane to make the pores saturated with glycerin, and carefully remove the glycerin on the surface of the membrane. Polyvinyl alcohol (PVA) and corresponding cross-linking agents, additives and compounding agents are dissolved in solvent water, the concentration of polyvinyl alcohol is 2% (W / W), and the film-forming solution of the active skin layer of polyvinyl alcohol is prepared. Coat the film-making solution on the microporous polyvinyl nitrile support membrane saturated with glycerol, place it at a temperature of 60°C to solidify the polyvinyl alcohol to form an active skin layer, and then place the film at a temperature of 100°C and 10kPa Treat under vacuum for 2 hours to obtain a dry composite film. The SEM photograph of the...

Embodiment 3

[0024] The polysulfone (PS) microporous hollow fiber membrane is made by the L-S phase inversion method, the outer diameter of the fiber tube is 500 microns, the inner diameter is 250 microns, and the pore diameter is 0.1 microns. Immerse the fiber tube in solvent water to saturate the pores with water. Polydimethylsiloxane (PDMS) and corresponding crosslinking agents, catalysts and additives were dissolved in solvent benzene, and the concentration of polydimethylsiloxane (PDMS) was 10% (W / W). Seal both ends of the fiber tube, then immerse it in polydimethylsiloxane film-making solution for 1-2 mm, take it out to let the benzene volatilize naturally, and then place it at a temperature of 100 ° C and treat it under a vacuum of 10 kPa for 3 hours to form a dry hollow fiber composite membrane. The SEM photograph of the composite film shows that the thickness of the polydimethylsiloxane (PDMS) composite layer is 2 microns. When used for air separation, O 2 / N 2 The separation ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A composite polymer membrane for separating fluid is prepared through preparing a minipore polymer membrane, immersing it in a solvent, removing the solvent from its surface, dissolving another polymer, cross-linking agent, additive and complexant in another solvent, compounding the solution with said minipore membrane. Its advantages are high separation selectivity and high penetrability.

Description

1. Technical field [0001] The invention relates to a manufacturing method of a polymer composite membrane, in particular to a manufacturing method of a polymer composite membrane with a dense non-porous separation active skin layer for reverse osmosis and pervaporation of fluid separation. 2. Background technology [0002] Most of the dense non-porous multilayer composite membranes used in reverse osmosis and pervaporation for fluid separation are made of high molecular polymers. In order to obtain high membrane permeation flux and ensure the separation selectivity of the membrane, it must be made into a very thin and defect-free membrane. There are two general approaches to fabricate membranes with thin or ultrathin separation active skins. One is the so-called L-S immersion gel method for manufacturing asymmetric membranes, which have an ultra-thin dense top layer and a porous support bottom layer for separation. An asymmetric membrane has an asymmetric geometry across t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01D69/12
Inventor 肖泽仪黄卫星伍勇梁明征钟月华叶立徐怀东
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap