Rare earth-doped srstrontium cerate nano crystal ceramic preparing method

A rare earth doping and nanocrystalline technology, applied in the field of inorganic ceramic material manufacturing, can solve the problems of high synthesis and sintering temperature, poor thermal stability of ceramics, poor composition uniformity, etc., and achieves low reaction temperature and sintering temperature and good thermal stability. , The effect of smooth surface with less defects

Inactive Publication Date: 2004-01-28
SHANGHAI UNIV
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The ceramic powder prepared by solid phase synthesis has large particles, poor composition uniformity, and high synthesis and sintering temperature
Although the co-precipitation method is simple, the grain growth of the powder produced is too fast, which is not suitable for control; at the same time, the thermal stability of the prepared ceramics is poor, and the grains are easy to grow during the sintering process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] Embodiment one: preparation SrCe 0.95 Yb 0.05 o 3 nanocrystalline ceramics

[0010] Will Yb 2 o 3 0.233g is dissolved in 20ml concentrated nitric acid, as A raw material, Sr(NO 3 ) 2 5.00g is made into a solution with 20ml of deionized water, and as the B raw material, Ce(NO 3 ) 3 ·6H 2 O 9.75g is made into a solution with 20ml of deionized water as the raw material of C. After stirring and mixing the raw materials of A, B, and C, add 2.0 times the ion weight (19.9g) of citric acid to make a solution of about 250ml. Under stirring or ultrasonic vibration, the solution was adjusted to pH = 7-8 with concentrated ammonia water, and heated in a water bath at 60°C until it turned into a transparent gel. The wet gel is infrared dried or vacuum dried at 120°C for 15 hours, and then becomes an opaque dry gel, and then calcined at 1000°C for 6 hours for synthesis reaction, and finally pure orthorhombic nano-ceramic powder can be obtained. The prepared ceramic powder w...

Embodiment 2

[0012] Embodiment two: preparation SrCe 0.90 Y 0.10 o 3 nanocrystalline ceramics

[0013] Will Y 2 o 3 0.535g is dissolved in 20ml concentrated nitric acid, as A raw material, Sr(NO 3 ) 2 5.00g is made into a solution with 20ml of deionized water, and as the B raw material, Ce(NO 3 ) 3 ·6H 2 O 9.26g was prepared into a solution with 20ml of deionized water as C raw material. After A, B, and C raw materials were stirred and mixed, citric acid with 2.0 times the ion weight (19.9 g) was added to form a solution of about 250 ml. Adjust the pH to 4-5 with ammonia water, and heat in a water bath at 70°C until it turns into a transparent gel. The wet gel was dried by infrared or vacuum at 130° C. for 10 hours, and then it became an opaque dry gel. Then calcined at 1000°C for 8 hours to carry out the synthesis reaction, and finally obtain nano-ceramic powder, press the prepared ceramic powder into a disc with a diameter of 20 mm and a thickness of 1 mm under isostatic pre...

Embodiment 3

[0015] Embodiment three: preparation SrCe 0.85 Yb 0.15 o 3 nanocrystalline ceramics

[0016] Will Yb 2 o 3 0.699g is dissolved in 20ml concentrated nitric acid, as A raw material, Sr(NO 3 ) 2 5.00g is made into a solution with 20ml of deionized water, and as the B raw material, Ce(NO 3 ) 3 ·6H 2 8.72g of O was made into a solution with 20ml of deionized water as C raw material. After A, B, and C raw materials were stirred and mixed, citric acid with 2.0 times the ion weight (19.9 g) was added to form a solution of about 250 ml. Adjust the pH to 7-8 with ammonia water, and heat in a water bath at 60°C until it turns into a transparent gel. Dry the wet gel in a microwave oven (power 800W) for 150 seconds to become an opaque dry gel, then calcined at 1000°C for 6 hours to carry out the synthesis reaction, and finally obtain nano-ceramic powder. SrCe was obtained by isostatic pressing at 20 MPa to form a disc with a diameter of 20 mm and a thickness of 1 mm, and then ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Conductivityaaaaaaaaaa
Login to View More

Abstract

The present invention for ceramics of rare earth doped with strontium cerate nano crystal mainly adopts sol-gel method, to prepare the solution with a certain concentration by using cerous nitrate, strontium nitrate or strontium acetate and rare earth oxide as raw material, the weight ratio of them is dependent on the composition of ceramics to be prepared, the composition of the ceramics is SrCe1-xRExO3, in which the range of x value is 0.02-0.20, the concentraitons of cerous nitrate, strontium nitrate or strontium acetate are 0.2-2 mol / L respectively, using citric acid as complex builder, the added quantity of citric acid is 1.5-2.5 times the said solution, under stirring or ultrasonic vibration, heating in wate bath with 50-80 deg.C, regulating pH value to obtain transparent gel, drying to obtain opaque dried gel.

Description

technical field [0001] The invention relates to a preparation method of rare earth-doped strontium cerate nanocrystalline ceramics, which belongs to the technical field of inorganic ceramic material manufacturing. Background technique [0002] doped perovskite SrCeO 3 , BaCeO 3 , CaZrO 3 , SrZrO 3 , BaZrO 3 Such composite oxide ceramics have good proton conductivity in medium-high temperature hydrogen and water vapor atmospheres. These proton conductors can be used as hydrogen sensors, medium-high temperature fuel cells, hydrogen pumps, electrolytic preparation, separation and purification of hydrogen, and organic synthesis. Catalytic hydrogenation and dehydrogenation and solid electrolytes of various electrochemical devices, etc., have very important application value and broad application prospects, especially in the application of hydrogen determination in the metallurgical industry, which has the advantages of fast, simple, and low cost. Medium and high temperature ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B35/50C04B35/624C04B35/64
Inventor 方建慧丁伟中施利毅鲁雄刚张宏力胡君蓉
Owner SHANGHAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com