Fireproof coating composition and application thereof

A technology of fire-resistant coatings and compositions, applied in the direction of fire-resistant coatings, rubber derivative coatings, polyurea/polyurethane coatings, etc., to achieve excellent performance and effects

Inactive Publication Date: 2004-11-10
SHANGHAI BEIAN IND
View PDF0 Cites 33 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] So far, there has been no literature report on the use of fire-resistant coatings to coat cables so that they can maintain safe energization for a certain period of time in a fire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0067] Accurately weigh each component according to the ratio shown in Table 1 below.

[0068] raw material

Proportion (g)

Polybutene

27

polyphosphate amine

15

melamine

6

pentaerythritol

6

Cellulose Fiber

1

Mica

2

No. 200 solvent gasoline

43

[0069] Put the weighed components into the sand mill, but only 1 / 3 of the cellulose fibers. Close the lid, tighten the screws, and stir for 30 minutes to fully dissolve the components in the solvent, then start the machine for sanding. Add 1 / 3 of the cellulose fibers after 2 hours of sanding, and add the final 1 / 3 of the cellulose fibers after 4 hours of sanding. After sanding for 24 hours, take regular samples to check the average particle size. When the average particle size is 90 microns, stop sanding and discharge.

[0070] The prepared coating is coated on the cable with a coating thickness of 0.4mm to make ...

Embodiment 2

[0079] Accurately weigh each component according to the ratio shown in Table 4 below.

[0080] raw material

Proportion (g)

Chlorinated Rubber

20

polyphosphate amine

19

melamine

10

pentaerythritol

10

Viscose fiber

2

Mica

4

No. 200 solvent gasoline

35

[0081] Put the weighed components into the sand mill, but only 1 / 3 of the cellulose fibers. Close the lid, tighten the screws, and stir for 30 minutes to fully dissolve the components in the solvent, then start the machine for sanding. Add 1 / 3 of the cellulose fibers after 2 hours of sanding, and add the final 1 / 3 of the cellulose fibers after 4 hours of sanding. After sanding for 24 hours, take regular samples to check the average particle size. When the average particle size is 80 microns, stop sanding and discharge.

[0082] The prepared coating is coated on the cable with a coating thickness of 0.5mm...

Embodiment 3

[0086] Accurately weigh each component according to the ratio shown in Table 6 below.

[0087] raw material

Proportion (g)

Urea formaldehyde resin

8

Chlorinated paraffin

2.0

Chlorinated Rubber

2

polyvinyl chloride

3.6

polyphosphate amine

14.9

melamine

6.7

pentaerythritol

14.9

Cellulose Fiber

1

Mica

6

No. 200 solvent gasoline

37.9

Titanium dioxide

3.0

[0088] Put the weighed components into the sand mill, but only 1 / 4 of the cellulose fibers. Close the lid, tighten the screws, and stir for 30 minutes to fully dissolve the components in the solvent, then start the machine for sanding. Add 1 / 4 of the cellulose fibers after sanding for 2 hours, add 1 / 4 of the cellulose fibers after 4 hours of sanding, and add the final 1 / 4 of the cellulose fibers after 6 hours of sanding. After sanding for 24 hour...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a fire-resisting paint and its use, wherein the fireproofing coating composition comprises composite film forming resin 15-30 wt. portions, expansion combustion inhibitor 27-40 wt. portions, flame-proof insulating material 2-15 wt. portions, fabric filling material 1-5 wt. portions, coating material solvent 30-45 wt. portions, wherein the particle mean size of the solid state components is 1-90 micrometer. The fireproofing paint can be applied to cable coating which can substantially extend the fire-resistant period for the cable.

Description

technical field [0001] The invention relates to a fireproof coating and its application. The fireproof coating can be used as the outer coating of cables and wires, so that the cables can keep electricity safely for a certain period of time in a fire. Background technique [0002] Wires and cables are prone to fire and have great fire hazards. Therefore, cable fire protection is an important research topic in the field of fire protection. At present, fire-resistant cables, flame-retardant cables, and cable fire-resistant coatings have been developed at home and abroad. Among them, brushing the cable fireproof coating on the surface of the cable can effectively reduce the occurrence of fire and prevent the spread and spread of the flame. It is a simple and economical means. In GA181-1998), the detection of flame retardancy and fire resistance is only one item of carbonization height, so there are few domestic reports on the fire resistance of cables coated with cable fire re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/18C09D115/02C09D127/04C09D161/24C09D175/04
Inventor 杨佳庆陈莉戴昱商德民龚卿瑜
Owner SHANGHAI BEIAN IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka