Process of preparing infusorial earth modified cement and light high strength concrete

A cement preparation and diatomite technology, which is applied in the field of diatomite modified cement and lightweight high-strength concrete preparation technology, can solve problems such as difficulty in meeting load-bearing requirements, low strength, and easy corrosion of steel bars, and achieve good heat insulation effect, Intense, Versatile Effects

Inactive Publication Date: 2005-01-05
罗炜
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Another method is porous concrete, which is made of air-entraining agent and foaming agent. Its strength is very low, and it is difficult to meet the load-bearing requirements, and the steel bars in porous concrete are easy to rust, especially in high humidity or dry conditions. It is more serious in the environment of alternating humidity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0012] The cement production equipment consists of a raw material warehouse, an electronic belt scale, a feeder, a rough mixer, a fine mixer, and a cement storage warehouse. The diatom concentrate is surface-modified diatomite after surface hydrophobic treatment. ) 42.5 Admixture ingredients made of 80% ordinary Portland cement, 19% surface modified diatomite, 1% calcium chloride early strength agent and water reducing agent. The belt scale is fed into the coarse mixer, and then fed into the fine mixer to obtain diatomite modified cement, and the obtained cement is mixed with 32% water to obtain a volume density of 850kg / cm 3 , CL30 (28-day strength of 30MPa) lightweight high-strength concrete, with a thermal conductivity of 0.062W / m.k.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a diatomite modified cement and light high-strength concrete preparing method, including components in weight percent: ordinary Portland cement 47-89.5%, surface modified diatomite 10-50%, and additive 0.5-3%, feeding the prepared materials in a rough mixing machine and a fine mixing machine, so as to obtain the diatomite modified cement, then mixing and stirring the diatomite modified cement with sand, stone and water to obtain the light high-strength concrete. This concrete has lightness, high strength, good heat-insulating and -preserving effect, ability to resist UV radiation, wide use, ability to act as light wall material, light cement prefabricated part, bearing material, etc, able to be widely applied to high-rise architectures, storey architectures, industries in need of preserving heat, insulating heat and insulating sound and civil architectures.

Description

Technical field [0001] The invention relates to a preparation process of diatomite modified cement and lightweight high-strength concrete. Background technique [0002] There are two ways to prepare lightweight concrete. One method is to use light aggregates. There are two types of light aggregates. Gangue; the other type is artificial light aggregate, which is obtained from clay, shale, perlite, etc. after high temperature swelling or sintering into a porous structure, such as fly ash ceramsite, coal gangue ceramsite, clay ceramsite, page Rock ceramsite and expanded perlite, expanded slag beads, cinder, etc. The strength of lightweight concrete made of light aggregate depends on the strength of the aggregate. Since the strength of light aggregate is low, the strength of the resulting concrete is not high, and the water absorption of light aggregate is large, so it is difficult to mix concrete. When high strength is required When lightweight concrete, the bulk density is h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B7/02C04B28/04
Inventor 罗炜李建锡
Owner 罗炜
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products