Method for manufacturing fabric with moisture absorption and sweat discharge performance

A moisture-absorbing and perspiration-absorbing fabric technology, which is applied in textiles, papermaking, and fiber processing, can solve the problems of fabrics not being resistant to washing, high production costs, and slow production speed, and achieve good washing resistance, low cost, and fast production speed Effect

Inactive Publication Date: 2005-01-19
IND TECH RES INST
View PDF4 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the defects of high production cost, slow production speed, easy to generate a large amount of waste water in the production process, and the fabric produced is not resistant to washing in the prior art when the fabric is subjected to moisture absorption and perspiration processing, thereby providing a manufacturing method. Method with moisture-wicking fabrics to make fabrics that are both absorbent and quick-drying

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for manufacturing fabric with moisture absorption and sweat discharge performance
  • Method for manufacturing fabric with moisture absorption and sweat discharge performance
  • Method for manufacturing fabric with moisture absorption and sweat discharge performance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A 100% polypropylene knitted fabric with a density of 160 grams per square meter is passed through a corona discharge machine with a total power of 8000 watts at a speed of 0.5 meters per minute to activate the fiber surface. The activated knitted fabric undergoes surface modification for moisture absorption and perspiration by immersion-pressure absorption-baking. The composition of the pressure-absorbent aqueous solution used is: chitosan (molecular weight 340,000g / mol) 1.25%, acrylic acid 5%, polyvinyl alcohol (molecular weight 22,000g / mol) 8.5%, all based on the weight of the overall solution 100% counted. After the chitosan and polyvinyl alcohol in the composition of the pressure-absorbing liquid are completely dissolved, the pressure-absorbing liquid is heated to 50°C, and 0.3% cerium ammonium nitrate (based on the weight of the whole solution as 100%) is added, and the above is soaked The surface of the activated fiber fabric has a baking temperature of 95°C and a re...

Embodiment 2

[0046] The cloth type and pretreatment conditions are the same as in Example 1. The surface modification is carried out by immersion-pressure suction-baking. The composition of the pressure-absorbing water solution is: chitosan (molecular weight 340,000g / mol) 1.25%, acrylic acid 5%, polyvinyl alcohol (molecular weight 22,000g / mol) 8.5%, all based on 100% of the total solution weight. After the chitosan and polyvinyl alcohol in the composition of the pressure-absorbing liquid are completely dissolved, the pressure-absorbing liquid is heated to 50°C, and 0.5% of cerium ammonium nitrate (based on the total weight of the solution as 100%) is added, and the above is soaked The surface of the activated fiber fabric has a baking temperature of 95°C and a reaction time of 120 seconds. The obtained product is the moisture-absorbing and sweat-wicking fabric of the present invention, and the water evaporation rate is shown in Table 1.

Embodiment 3

[0048] The cloth type and pretreatment conditions are the same as in Example 1. The surface modification is carried out by immersion-pressure suction-baking. The composition of the pressure-absorbing water solution is: chitosan (molecular weight 340,000g / mol) 1.25%, acrylic acid 5%, polyvinyl alcohol (molecular weight 22,000g / mol) 8.5%, all based on 100% of the total solution weight. After the chitosan and polyvinyl alcohol in the composition of the pressure-absorbing liquid are completely dissolved, the pressure-absorbing liquid is heated to 50°C, and 0.5% of cerium ammonium nitrate (based on the total weight of the solution as 100%) is added, and the above is soaked Surface activated fiber fabric. The baking temperature is 95°C, and the reaction time is 120 seconds. The obtained product is the moisture-absorbing and sweat-wicking fabric of the present invention, and the water evaporation rate is shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
molecular weightaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for making fabric having moisture absorbing and sweating property, which includes: pre-activating on the surface of the hydrophobic fabric; then taking grafting reactions with polyalcohol, natural polysaccharide and copolymer formed by unsaturated carboxylic acid with double bond and a covalent bond is formed.

Description

Technical field [0001] The invention relates to a method for manufacturing a fabric with moisture absorption and sweat wicking properties, specifically, a graft reaction is carried out on the surface of a fiber fabric to impart moisture wicking properties to the fabric. Background technique [0002] In the fabric field, "moisture wicking" refers to making non-hydrophilic fabrics have both water absorption and quick-drying properties. Generally speaking, it is difficult for natural fibers or man-made synthetic fibers to have these two properties at the same time. For example, polypropylene fibers in man-made synthetic fibers have the functions of light weight, quick drying, soft touch, heat preservation, antibacterial properties, and high abrasion resistance, and have the potential as high-end clothing materials. However, polypropylene fiber is not hydrophilic, so the sweat permeability is not good, especially in high temperature and high humidity areas or summer is not suitable a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M14/12
Inventor 庄仲扬郑淑蕙
Owner IND TECH RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap