Nanometer titanial/nanometer silver coating and preparing method thereof

A nano-titanium dioxide and nano-silver technology, applied in coatings and other directions, can solve the problems of poor stain resistance, environmental protection, poor weather resistance, etc., and achieve the effect of improving antibacterial properties, good antibacterial properties, and expanding the scope of use

Inactive Publication Date: 2005-02-23
RESEARCH INSTITUTE OF TSINGHUA UNIVERSITY IN SHENZHEN
View PDF0 Cites 38 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] An object of the present invention is to provide a coating capable of organically combining nano-titanium dioxide and nano-silver and its preparation method to solve the problems of existing coatings such as poor stain resistance, poor weather resistance, and non-environmental protection. New functions such as self-cleaning, antibacterial and air purification

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The preparation formula of this embodiment is:

[0038] Tap water: 220 kg; Dispersant: 8 kg;

[0039] Defoamer: 4 kg; Wetting and dispersing agent: 0.2 kg;

[0040] Thickener: 20 kg; Leveling agent: 10 kg;

[0041] Film-forming aid: 15 kg; Styrene-acrylic emulsion: 150 kg;

[0042] Titanium dioxide: 60 kg; Nano silver solution: 20 kg;

[0043] Nano-titanium dioxide dispersion: 20 kg; ultra-fine aluminum silicate: 20 kg;

[0044] Talcum powder: 80 kg; Lithopone: 120 kg;

[0045] Heavy calcium carbonate: 100 kg; Light and heavy calcium carbonate: 100 kg.

[0046] Its preparation method is:

[0047] (1) Mix the nano-titanium dioxide dispersion liquid and the nano-silver solution evenly.

[0048] (2) Mix uniformly mixed nano-titanium dioxide / nano-silver particle mixture, film-forming aids, leveling agents, dispersants, wetting and dispersing agents, defoamers, water, titanium dioxide, ultrafine aluminum silicate, talc powder , Lithopone, heavy calcium carbonate, and...

Embodiment 2

[0052] The preparation formula of this embodiment is:

[0053] Tap water: 100 kg; Dispersant: 6 kg;

[0054] Defoamer: 5 kg; Thickener: 5 kg;

[0055]Leveling agent: 3 kg; Coalescing agent: 5 kg;

[0056] Wetting and dispersing agent 0.3 kg Silicone acrylic emulsion: 300 kg

[0057] Ultrafine aluminum silicate: 10 kg; titanium dioxide: 300 kg;

[0058] Talc powder: 40 kg; Light calcium carbonate: 50 kg;

[0059] Wollastonite: 100 kg; Nano silver solution: 10 kg;

[0060] Nano-titanium dioxide dispersion: 10 kg.

[0061] Its preparation method is:

[0062] (1) Mix the nano-titanium dioxide dispersion liquid and the nano-silver solution evenly.

[0063] (2) Mix uniform nano-titanium dioxide / nano-silver mixed solution, wetting and dispersing agent, film-forming aid, leveling agent, dispersant, defoamer, water, talcum powder, titanium dioxide, ultrafine aluminum silicate, Wollastonite and light calcium carbonate were respectively weighed and added to the mixing tank, stirr...

Embodiment 3

[0067] The preparation formula of this embodiment is:

[0068] Tap water: 200 kg; Dispersant: 10 kg;

[0069] Defoamer: 5 kg; Thickener: 15 kg;

[0070] Leveling agent: 6 kg; Coalescing agent: 12 kg;

[0071] Wetting and dispersing agent 0.1 kg Vinegar-acrylic emulsion: 200 kg

[0072] Ultrafine aluminum silicate: 10 kg; titanium dioxide: 200 kg;

[0073] Talc powder: 50 kg; Light calcium carbonate: 70 kg;

[0074] Lithopone: 120 kg; Heavy calcium carbonate: 80 kg;

[0075] Nano silver solution: 10 kg; Nano titanium dioxide dispersion: 30 kg.

[0076] Its preparation method is:

[0077] (1) Mix the nano-titanium dioxide stock solution and the nano-silver solution evenly.

[0078] (2) Mix uniform nano-titanium dioxide / nano-silver mixture, film-forming aids, leveling agents, dispersants, wetting and dispersing agents, defoamers, water, titanium dioxide, ultrafine aluminum silicate, talcum powder, Lithopone, heavy calcium carbonate, and light calcium carbonate were weighe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

This invention is that a kind of nanometer oxidizes the titanium / the silver coating of nanometer two times And prepare the method. Featuring that has used receiving of this invention Meter oxidizes titanium and one kind of particles of nanometer silver two times, this coating is solved Existing coating bad to able to bear person who stain, able to bear poor person who wait, environmental protection, etc. The shortcoming, it is clean to have the excellent one at the same time, disinfect and disinfect, Purify new functions, such as air, etc.. The ones that have improved coating are resisted further Fungus performance, make it still have under or the dry situation There are good antibiotic results, has expanded the scope of application greatly.

Description

technical field [0001] The invention relates to the field of building materials, in particular to an environment-friendly nano-titanium dioxide / nano-silver coating with good antibacterial properties and a preparation method thereof. Background technique: [0002] Since nano-titanium dioxide has special photocatalytic properties, super-hydrophilicity, and UV shielding properties, applying it to coatings and keeping them in a nano-scale state in the coatings can not only improve the shortcomings of existing coatings such as poor weather resistance and easy staining, At the same time, it can also endow the coating with good antibacterial, self-cleaning and air-purifying properties. It can be widely used in high-end decoration of families, schools, hospitals, kindergartens, high-end hotels, and commercial buildings. In places with high humidity and serious pollution in the south, it is more suitable Competitive in the market. [0003] Nano-titanium dioxide coating can remove ba...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D131/04C09D133/00
Inventor 李荣先陈丽琼
Owner RESEARCH INSTITUTE OF TSINGHUA UNIVERSITY IN SHENZHEN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More