Multicomponent moisture holding agent in low cost and preparation method

A water-retaining agent and multi-component technology, which is applied in the field of multi-component low-cost water-retaining agent and its preparation, can solve the problems that are not conducive to large-scale continuous production, serious production environment pollution, and production cost reduction, and achieve large-scale production Production, good gel strength, long-term effect

Inactive Publication Date: 2005-10-26
师进
View PDF2 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent CN1359974 discloses a low-cost water-retaining agent prepared by adding kaolin and bentonite through the copolymerization of acrylamide and potassium acrylate. The production of water-retaining agent by this method is not conducive to large-scale continuous production
Chinese Patent Application No. 03120346.9 discloses a method for preparing an organic-inorganic comp...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Example 1. First add 38.5% acrylamide aqueous solution and 1% N,N'-methylenebisacrylamide aqueous solution to the mixer at a ratio of 1:0.01, and adjust with sodium hydroxide under stirring. Polymerize the system until the pH value = 5; then add attapulgite, bentonite, 1% sodium sulfite solution, and potassium metabisulfite solution in the polymerization system in a ratio of 1:0.1:0.1:0.01:0.01, and stir evenly after each addition Then add the next raw material; then move the polymerization system into the polymerization reactor, and polymerize at 45°C for 3 hours; finally, dry, pulverize and sieve the polymerized colloid to obtain a multi-component water-retaining agent.

Embodiment 2

[0011] Example 2. First add pure acrylic acid and 1% aqueous solution of N,N'-methylenebisacrylamide in the mixer at a ratio of 1:0.05, and adjust the polymerization system to PH value = 5.5; then add attapulgite, bentonite, 1% sodium sulfite solution, and potassium metabisulfite solution in the polymerization system in a ratio of 1:0.5:0.5:0.02:0.02, and add the following A kind of raw material; then move the polymerization system into the polymerization reactor, and polymerize at 50°C for 3.5 hours; finally, dry, pulverize and sieve the polymerized colloid to obtain a multi-component water-retaining agent.

Embodiment 3

[0012] Example 3. First add 38.5% acrylamide aqueous solution and pure acrylic acid (the ratio of acrylamide aqueous solution to pure acrylic acid is 1:1) and 1% N, N' in the mixer in a ratio of 1:0.1 - methylenebisacrylamide aqueous solution, adjust the polymerization system to PH value = 6 with sodium hydroxide under stirring; then add attapulgite, bentonite, 1% sodium sulfite solution, potassium metabisulfite solution, add the next raw material after stirring evenly each time; then move the polymerization system into the polymerization reactor, and polymerize at 60°C for 4 hours; finally bake the polymerized colloid Drying, crushing, and sieving are multi-component water retaining agents.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention provids a preparation method of multicomponent low-cost water-retaining agent. Said water-retaining agent is prepared by adopting two organic monomers of acrylamide and acrylic acid as main agent, adding attapulgite and bentonite as reinforcing agent, using ammonium persulate or potassum persulfate as oxidant, using sodium sulfite and potassium metabisulfite as reducing agent and using N,N'-methylene-diacrylamide as cross-linking agent through a certain preparation process.

Description

technical field [0001] The invention relates to a water-retaining agent and a preparation method thereof, in particular to a multi-component low-cost water-retaining agent and a preparation method thereof. Background technique [0002] Water-retaining agents have been widely used in many fields, but their application has been greatly limited due to their high cost. How to reduce the cost of water retaining agent is an important and urgent issue facing water retaining agent. Chinese patent CN1359974 discloses a low-cost water-retaining agent prepared by adding kaolin and bentonite through the copolymerization of acrylamide and potassium acrylate. The production of water-retaining agent by this method is not conducive to large-scale continuous production. Chinese Patent Application No. 03120346.9 discloses a method for preparing an organic-inorganic composite water-retaining agent using 100 parts of acrylic acid and 20-60 parts of acidified attapulgite, because the method acc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F220/56
Inventor 师进黄高宝
Owner 师进
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap