Latex for coating drinking filter bag cotton paper and its preparing method

A filter bag and latex technology, which is applied in the coating of coated paper and its preparation, can solve the problems of unhygienic production and use, difficulty in removing latex, and affecting the taste of coffee, etc., and achieve high cost performance, less leachables, The effect of low cost

Inactive Publication Date: 2006-01-04
浙江森兰德包装科技有公司
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, manufacturers use styrene-acrylic latex to impregnate tissue paper. However, due to the large amount of high-boiling point monomers such as styrene and acrylate, the boiling point of styrene is as high as 146 ° C. It is difficult to remove residual monomers from latex. The amount is relatively high, and the smell is very bad during the coating process. After the coated tissue paper is made into a coffee bag, there are many dissolved substances in the water that affect the coffee taste, and it is extremely unhygienic during production and use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Name Quantity (g)

[0030] Kettle material:

[0031] Deionized water 80

[0032] Sodium Alkyl Sulfonate 2

[0033] Organic peroxide 0.011

[0034] Mixed monomer:

[0035] Vinylidene chloride (VDC) 85

[0036] Methacrylic acid (MAA) 9

[0037] Butyl acrylate (BA) 6

[0038] Initiator:

[0039] Initiator A: tert-butyl hydroperoxide 0.099

[0040] Deionized water 10

[0041] Initiator B: Carving white powder 0.08

[0042] Deionized water 10

[0043] The solid content of latex is 30%.

[0044] The specific operation process: first add 80 grams of deionized water and 2 grams of sodium alkyl sulfonate to the reaction kettle and blow nitrogen to fully replace the air inside, then increase the temperature, and add 0.011 grams of organic peroxide when the temperature rises to 40°C. When the temperature rises to 51°C, the mixed monomer and initiators A and B are contin...

Embodiment 2

[0046] Repeat Example 1. The difference between this example and Example 1 is that the components of the mixed monomer are: vinylidene chloride (VDC), the amount is 70 grams; (2) methacrylic acid (MAA), the amount is 20 grams; (3) Butyl acrylate (BA), the amount is 10 grams. The solid content of latex is 10%. When the temperature rises to 53°C, the mixed monomers and initiators A and B are continuously added to the reaction kettle through a metering pump, while keeping the temperature at 52-53°C. The prepared latex has good identity.

Embodiment 3

[0048] Repeat Example 1. The difference between this example and Example 1 is that the components of the mixed monomer are: vinylidene chloride (VDC), the amount is 80 grams; (2) acrylic acid (AA), the amount is 15 grams ; (3) Butyl acrylate (BA), the amount is 5 grams. The solid content of latex is 16%. When the temperature rises to 53°C, the mixed monomers and initiators A and B are continuously added to the reaction kettle through a metering pump, while keeping the temperature at 52-53°C. The prepared latex has good identity.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The latex for coating tissue paper of drink filtering bag is prepared through emulsion polymerization in the presence of emulsifier and initiator. The monomer mixture for the latex includes: vinylidene chloride in 60-85 wt%, acrylate in 5-30 wt%, and unsaturated fatty acid in 5-10 wt%. The latex makes the coated tissue paper possess high wet strength, high water penetrating capacity, no toxicity, no smell, few leached matter and high performance / cost ratio, and is especially suitable for coating tissue paper for coffee, tea and other drink extracting bag.

Description

Technical field [0001] The invention relates to a coating for coated paper and a preparation method thereof, in particular to a latex for coating beverage filter bag tissue paper and a preparation method thereof. technical background [0002] Coffee or tea filter bags were originally made of cloth. In recent years, they have been replaced with permeable tissue paper with sufficient wet strength. When the tissue paper is directly immersed in water, the wet strength is extremely low and the tear strength is extremely poor. After soaking, it loses its strength and is neither beautiful nor hygienic. So later, the method of coating a layer of latex on the tissue paper was used to enhance its strength, so that it can be soaked in water for a long time to maintain its strength, and at the same time, the tissue paper has good water permeability. At present, manufacturers use styrene-acrylic latex to dip and coat tissue paper, but due to the large amount of high-boiling monomers such as s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D21H21/16D21H19/16
Inventor 何祥麟黄建阮国富应忠芳季国华陈荣
Owner 浙江森兰德包装科技有公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com