Method for preparing CaO-P2O5-MgO glass reinforced porous beta-tricalcium phosphate bioceramics
A cao-p2o5-na2o-mgo, glass-reinforced technology, applied in the direction of ceramic products, applications, home appliances, etc., can solve the problems that are not enough to meet clinical applications
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0020] Example 1: CaO-P 2 O 5 -Na 2 O-MgO Bioglass
[0021] Take NH 4 H 2 PO 4 , Ca(OH) 2 , Na 2 CO 3 , (MgCO 3 ) 4 Mg(OH) 2 ·5H 2 O is the raw material, press P in the raw material 2 O 5 :CaO:Na 2 The mass percentage of O:MgO is 62:14.7:18:5.30, and the total mass is 100 grams. Weigh accurately 47.12 grams of NH 4 H 2 PO 4 , 19.45g Ca(OH) 2 , 30.19 grams of Na2 CO 3 And 63.69 grams (MgCO 3 ) 4 Mg(OH) 2 ·5H 2 O. Grind the said raw materials evenly, pour them into a beaker, slowly add deionized water, and keep stirring until no bubbles emerge. The mixture is dried in an oven at a constant temperature of 80°C, and then calcined and melted. The system is: in the temperature range of 300 to 400°C and 700 to 800°C, the heating rate is 1.5°C / min, and the temperature is 400°C to 700°C and 700°C. In the temperature range of ℃~910℃, the heating rate is 3.5℃ / min, and the temperature is raised to 910℃ for 1 hour. The molten glass is naturally cooled, ground and sieved according to the furnac...
Example Embodiment
[0022] Example 2: CaO-P 2 O 5 -Na 2 O-MgO Bioglass
[0023] Take (NH 4 ) 2 HPO 4 , CaCO 3 , Na 2 CO 3 , MgCO 3 As raw material, press P in raw material 2 O 5 :CaO:Na 2 The mass percentage of O: MgO is 41.4: 9.80: 12: 3.50, the total mass is 50 grams, 26.98 grams (NH 4 ) 2 HPO 4 , 13.06g CaCO 3 , 15.40 grams of Na 2 CO 3 And 5.46 grams of MgCO 3 . Grind the said raw materials evenly, pour them into a beaker, slowly add deionized water, and keep stirring until no bubbles emerge. The mixture is dried in an oven at a constant temperature of 80°C, and then calcined and melted. The system is: in the temperature range of 300 to 400°C and 700 to 800°C, the heating rate is 1.5°C / min, and the temperature is 400°C to 700°C and 700°C. In the temperature range from ℃ to 980℃, the heating rate is 3.5℃ / min, and the temperature is raised to 980℃ for 2 hours. The molten glass is naturally cooled with the furnace, ground and sieved. The ground glass powder is heat-treated at 720°C for half an hour,...
Example Embodiment
[0024] Example 3: Glass reinforced tricalcium phosphate porous ceramics
[0025] Raw material: medical grade calcium carbonate (CaCO 3 ) And calcium hydrogen phosphate dihydrate (CaHPO 4 ·2H 2 O) as the raw material, accurately weigh out 171.1 grams of CaHPO according to the Ca / P molar ratio of 1.5 4 ·2H 2 O and 50.0 g CaCO 3 , Pour the weighed material into the ball mill tank, add deionized water and zirconia grinding balls. According to the ratio of material: grinding ball: water according to the mass ratio of 1:3:2.2, the mixture is high-speed ball milled in an oven for 16 hours at a constant temperature of 85°C and dried, and then calcined at 830°C to obtain an average particle size of 380nm β-Calcium Phosphate Powder.
[0026] Process: The β-tricalcium phosphate and the bioglass prepared in Example 1 are weighed at a mass percentage of 80:20, weighing 50 grams of mixed powder, measuring 33 ml of deionized water, and adding molarity to the deionized water 4ml of ammonium polya...
PUM
Property | Measurement | Unit |
---|---|---|
Average compressive strength | aaaaa | aaaaa |
Aperture | aaaaa | aaaaa |
Average compressive strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap