Artificial eye human body

A prosthetic eye and human body technology, applied in the field of prosthetic eyes, can solve the problems of tissue compatibility, softness and air permeability, etc., and achieve the effect of fast vascularization

Inactive Publication Date: 2006-11-08
SHANGHAI SUOKANG MEDICAL IMPLANTS
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Prosthetic eyes made of these materials are not ideal in terms of tissue compatibility, softness, and air permeability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Embodiment 1, fully mix the PTFE resin and sodium chloride containing 55% sodium chloride, the particle diameter of sodium chloride is 0.02mm~0.03mm; 2 ~120kg / cm 2 The pressure molded, sintered at 327 ℃ ~ 350 ℃ for 4 hours; mixed materials. After cooling, it is processed into a prosthetic eye with a sphere diameter of about 1.5 cm by cutting with a knife, and then steamed to remove sodium chloride. The obtained prosthetic eye has the aforementioned excellent properties.

Embodiment 2

[0015] Embodiment 2, fully mix the PTFE resin and sodium chloride containing 60% sodium chloride, the particle diameter of sodium chloride is 0.02mm~0.03mm; 2 ~200kg / cm 2 The pressure molded, sintered at 370 ℃ ~ 385 ℃ for 2 hours; mixed materials. After cooling, it is processed into a prosthetic eye with a sphere diameter of 2.5 cm by knife cutting, and then boiled to remove sodium chloride. The obtained prosthetic eye has the same excellent performance as above.

Embodiment 3

[0016] Example 3, fully mix the PTFE resin containing 65% sodium chloride and sodium chloride, the particle size of sodium chloride is 0.02mm-0.03mm; sinter at 350°C-360°C for 1 hour to obtain the mixed material. After cooling, it is processed into a prosthetic eye with a sphere diameter of about 2.2 cm by cutting with a knife, and then steamed to remove sodium chloride. The obtained prosthetic eye has the aforementioned excellent properties.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The present invention belongs to the field of medical device technology, and is especially one kind of artificial eye implanted directly into human body. The artificial eye is made with porous PTFE and has diameter of 1.2-2.5cm. It is made through the process of: mixing PTFE resin with sodium chloride in certain ratio, molding, sintering to obtain mixed material, forming into required shape, and boiling to eliminate sodium chloride to obtain the artificial eye. The artificial eye of the present invention is light, flexible, hydrophilic, air permeable, humidity permeable, tissue compatible, comfortable and good in wearing effect.

Description

technical field [0001] The invention belongs to the technical field of medical devices, in particular to an artificial eye that can be directly implanted into a human body. Background technique [0002] PTFE is a polymer of tetrafluoroethylene. English abbreviation is PTFE. The structural formula is It has excellent chemical stability, good biocompatibility, wide operating temperature, no aging, and permanent durability. [0003] In 1988, Elson proposed the ideal standard for soft tissue filling materials: grafts are compatible with recipient tissues and can coexist with connective tissue; minimal foreign body reactions and allergic reactions; no pain during treatment; long-lasting clinical correction effects; non-synthetic grafts products; the treatment process takes less time; the price of grafts is moderate and people can accept them. [0004] Expanded polytetrafluoroethylene (expanded polytetrafluoroethylene, e-PTFE) is a kind of strong and porous new material, whic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61F2/14A61F9/007A61L27/14
Inventor 叶明陶建熔
Owner SHANGHAI SUOKANG MEDICAL IMPLANTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap